Electrospinning of multicomponent ultrathin fibrous nonwovens for semi-occlusive wound dressings

This work describes the design and assembly of multifunctional and cost-efficient composite fiber nonwovens as semi-occlusive wound dressings using a simple electrospinning process to incorporate a variety Of functional components into an Ultrathin fiber. These components include non-hydrophilic poly(L-lactide) (PLLA) as fibrous backbone, hydrophilic poly(vinyl pyrrolidone)iodine (PVP-I), TiO2 nanoparticles, zinc chloride as antimicrobial, odor-controlling, and antiphlogistic agents, respectively. The process of synthesis starts with a multicomponent solution Of PLLA, PVP, TiO2 nanoparticles plus zinc chloride, in which TiO2 nanoparticles are synthesized by in situ hydrolysis of TiO2 precursors in a PVP Solution for the sake of obtaining the particle-uniformly dispersive solution. Subsequent electrospinning generates the corresponding composite fibers. A further iodine vapor treatment to the composite fibers combines iodine with PVP to produce the PVP-I complexes. Experiments indicate that the assembled composite fibers (300-400 nm) possess the ointment-releasing characteristic and the phase-separate, core-sheath structures in which PVP-I residing in fiber Surface layer becomes the sheath, and PLLA distributing inside the fiber acts as the core.

Medicated wound dressings based on poly(vinyl alcohol)/poly(N-vinyl pyrrolidone)/chitosan hydrogels

Poly(vinyl alcohol) /poly(N-vinyl pyrrolidone) (PVP)/chitosan hydrogels were prepared by a low-temperature treatment and subsequent Co-60 -gamma-ray irradiation and then were medicated with ciprofloxacin lactate (an antibiotic) and chitosan oligomer (molecular weight = 3000 g/mol). The gel content, swelling ratio, tensile strength, and crystallinity of the hydrogels were determined. The effects of the chitosan molecular weight, the low-temperature treatment procedure, and the radiation dosage on the hydrogel properties were examined. The molecular weight of chitosan was lowered by the irradiation, but its basic polysaccharide structure was not destroyed. Repeating the low-temperature treatment and gamma-ray irradiation caused effective physical crosslinking and chemical crosslinking, respectively, and contributed to the mechanical strength of the final hydrogels. The incorporation of PVP and chitosan resulted in a significant improvement in the equilibrium swelling ratio. and elongation ratio of the prepared hydrogels. The ciprofloxacin lactate and chitosan oligomer were soaked into the hydrogels. Their in vitro release behaviors were examined, and they were found to follow diffusion-controlled kinetics.