Development And Characterization Of Composite Ni-Cr-C-Caf2 Laser Cladding On Gamma-Tial Intermetallic Alloy

A process of laser cladding Ni-CF-C-CaF2 mixed powders to form a multifunctional composite coatingd on gamma-TiAl substrate was carried out. The microstructure of the coating was examined using XRD, SEM and EDS. The coating has a unique microstructure consisting of primary dendrite or short-stick TiC and block Al4C3 carbides reinforcement as well as fine isolated spherical CaF2 solid lubrication particles uniformly dispersed in the NiCrAlTi (gamma) matrix. The average microhardness of the composite coatings is approximately HV 650 and it is 2-factor greater than that of the TiAl substrate. (C) 2008 Elsevier B.V. All rights reserved.

Ni-Cr系光谱选择性吸收薄膜制备与表征

太阳能选择性吸收薄膜是中高温太阳能集热器的最关键部分，目前世界很多国家都在积极研究工艺简单、成本低廉、性能优良稳定的中高温光谱选择性吸收薄膜。本论文根据金属陶瓷型太阳能光谱选择性吸收表面和磁控溅射技术的原理，在国内外研究发展的基础上，针对目前国内平板型太阳能集热器的现有状况，结合太阳能热水器建筑一体化的发展趋势，开展了磁控溅射制备光谱选择性吸收薄膜的研究。本工作以直流反应磁控溅射方法作为制备手段，选择Ni-Cr合金作为靶材，以N2, 02两种气体为反应气体，反应溅射制备折射率变化的NiCr-NiCrO,N

The photo-induced decarbonylation of Cp ' M(NO)(CO)(2) (M = Cr, Mo, W) with diorgano dichalcogenides (R2E2; E = S, Se; R = Me, Ph)

The photo-induced decarbonylation of Cp'Cr(NO)(CO)(2) (1a) in MeCN solution in the presence of R2E2 (E = S, Se; R = Me, Ph) leads to the formation of chalcogenolato-bridged binuclear complexes Cp-2'Cr-2(NO)(2)(mu -ER)(2) [E = S; R = Me (2a), Ph (3a); E = Se, R = Me (4a), Ph (5a)] while reactions between Cp'M(NO)(CO)(2) [M = Mo (1b), W (1c)] and Ph2E2 (E = S, Se) result in mononuclear complexes Cp'M(NO)(EPh)(2) [M = Mo; E = S (9b), Se (10b); M = W, E = S (11c), Se (12c)]. The corresponding reactions of (1b) with Me2E2 (E = S, Se) yielded both mono and binuclear complexes: Cp'Mo(NO)(SeMe)(2) (8b), Cp-2'Mo-2(NO)(2)(mu -EMe)(2) [E = S (6b), Se (7b)]. The new complexes have been characterized by i.r., H-1-, C-13-n.m.r. spectra and by electron-impact mass spectrometry.

Characterization and thermodynamic study of ultra-fine particle of Ni-B amorphous alloy

Ultra-fine particle of Ni-B amorphous alloy was prepared by chemical reduction of Ni2+ with NaBH4 and characterized with TEM and XRD. The heat capacity and thermal stability were measured with a high-precision automatic adiabatic calorimeter and DTA. The upper limit of applied temperature of the substance was found to be 684 K for use as catalyst. (C) 1999 Elsevier Science B.V. All rights reserved.

Microstructure and high-temperature wear and oxidation resistance of laser clad gamma/W2C/TiC composite coatings on gamma-TiAl intermetallic alloy

There are very strong interests in improving the high-temperature wear resistance of the y-TiAl intermetallic alloy, especially when applied as tribological moving components. In this paper, microstructure, high-temperature dry sliding wear at 600 degrees C and isothermal oxidation at 1000 degrees C on ambient air of laser clad gamma/W2C/TiC composite coatings with different constitution of Ni-Cr-W-C precursor mixed powders on TiAl alloy substrates have been investigated. The results show that microstructure of the laser fabricated composite coatings possess non-equilibrium microstructure consisting of the matrix of nickel-base solid solution gamma-NiCrAl and reinforcements of TiC, W2C and M23C6 carbides. Higher wear resistance than the original TiAl alloy is achieved in the composite coatings under high-temperature wear test conditions. However, the oxidation resistance of the laser clad gamma/W2C/TiC composite coatings is deceased. The corresponding mechanisms resulting in the above behaviors of the laser clad composite coatings are discussed. (c) 2006 Elsevier B.V. All rights reserved.

Shear Localization In Dynamic Deformation: Microstructural Evolution

Investigations made by the authors and collaborators into the microstructural aspects of adiabatic shear localization are critically reviewed. The materials analyzed are low-carbon steels, 304 stainless steel, monocrystalline Fe-Ni-Cr, Ti and its alloys, Al-Li alloys, Zircaloy, copper, and Al/SiCp composites. The principal findings are the following: (a) there is a strain-rate-dependent critical strain for the development of shear bands; (b) deformed bands and white-etching bands correspond to different stages of deformation; (c) different slip activities occur in different stages of band development; (d) grain refinement and amorphization occur in shear bands; (e) loss of stress-carrying capability is more closely associated with microdefects rather than with localization of strain; (f) both crystalline rotation and slip play important roles; and (g) band development and band structures are material dependent. Additionally, avenues for new research directions are suggested.

Ti-V-Cr固溶体储氢合金的结构及电化学性能研究

本论文首先研究了Ni、Zr分别对Ti-V－Cr固溶体储氢合金中Cr和Ti部分取代的影响，得到了性能良好的Ti0．17Zr0．08V0．35Cr0．10Ni030基质合金。在此基础上进一步研究了入甄、B、Fe、Co、Al元素的添加或取代对基质合金的结构及电化学性能的影响。采用XRD、ICP、SEM一EDX、XPS、EIS、线性极化和阳极极化等表征手段对Ti一V－Cr固溶体储氢合金的结构及电化学性能进行分析和表征，主要结果如下：①Ti一V－Cr合金自身在碱性电解液中几乎无电化学活性。当用Ni部分取代Cr后，合金中出现具有电化学活性的第二相，其电化学性能得到有效地改善和提高。②Ti0.25-xZr_xV0.35Cr0.1Ni0.3（x＝0．05-0．15）合金主要是由bcc相和c14Laves相组成。随Zr含量从0．05增加到0．08，合金电极的放电容量和倍率放电能力增加；当x继续从0．08增加到0．15时，其变化较小。合金电极的电荷转移电阻随x增加而降低，当x在0．08到0．15之间变化时，电荷转移电阻变化也比较小。表明电荷转移电阻的大小与合金的电化学性能密切相关。③经过50次充、放电循环后，Tio．17zr"sV时scrol0Ni03。合金电极在303K和313K的放电容量能保持在90％以上；在70℃时的放电容量仍能达到275mA扮g。根据不同温度时的交换电流密度，计算了Ti。，17Zr008V时SCr川0Ni030合金电极表面电化学反应的表观活化能，其值约为50kJ／mol。④通过Nln、B、Fe、C。、AI对Tio．17zroosvo35Crol0Nio3。合金基质的添加与取代的研究，得到了具有高容量的储氢合金。其中Tio．17Zr008Vo35Cro．10Ni020Mnol。合金室温最高放电容量达到390n1A扮g；在253一343K的温度范围内，Tiol7Zr08V035Cr0JONioz5Mnoos合金具有高的放电容量，其容量在167一298mA树g之间变化，但是这些合金的稳定性有待进一步的提高。⑤合金充、放电过程中，晶格的扭曲和膨胀、Zr和V的溶解使得合金结构发生变化；合金的严重粉化及表面致密氧化膜的形成，是导致Ti一V－Cr合金电化学性能的衰减的主要原因。

镍-金属氢化物电池新型负极材料研究

贮氢合金是镍一金属氢化物电池的核心材料，其综合性能的改善是提高镍一金属氢化物电池性能的关键。本研究以探索镍一金属氢化物电池新型负极材料为目的，以非ABS型贮氢合金为研究对象，采用X射线衍射、Rietveld分析、恒电流充／放电、P-C-T曲线及线性微极化等方法，从基础和潜在应用等方面详细研究了非ABS型合金的结构与电化学性能。对La-Ni体系中非ABS型二元合金的结构和电化学性能的研究表明，LaNi_(228)具有最优异的高倍率充电性能；La_2Ni_7合金电极的高倍率放电性能最佳；La_7Ni_3在低温条件下表现出较好的放电性能。然而，所有得到的La-Ni合金电极容量远低于其理论容量。因此，必须通过进一步研究，如元素取代、热处理、表面处理等来提高其电化学容量。对RENi_3（RE＝La，Ce，Pr，Nd，Sm，Gd，Th，Dy，Ho，Er，Y）研究表明：YNi_3合金因其具有最大的晶胞体积，最小的密度，而表现出最好的高倍率充／放电性能及低温放电性能，但其高温放电性能需要进一步提高，以满足实际应用的要求。用Al、Mn、Ti、Fe、Sn、Si、Cr、M。、Cu和Co十种元素取代Ni进行了大量的配方筛选工作。得到了大量的实验数据，并发现LaNi_(3.7)Al_(0.3)合金电极电化学放电容量最高，达290.8mAh／g；LaNi_(3.7)Mo_(0.3)合金电极的高倍率放电性能最好，在以4200mA/g的电流密度下进行放电时，其放电容量仍达到145.8mA/g；而I镍一金属氢化物电池新型负极材料研究镍一金属氢化物电池新型负极材料的研究Al的取代会使合金电极性能对温度不敏感。以我们的实验为基础，进一步进行合金配方的微调，具有可能开发出具有实用价值的贮氢合金的潜力。在Ar保护下用真空电弧炉熔炼合成了四种Lal一xMg：（NICoAI）3．6体系贮氢合金，制成姐卜Ni电池负极，通过恒电流充／放电方法研究了其电化学性能。结果表明：Lal一xMg：（NiCoAI）3．6体系金属氢化物电极较容易活化，室温下具有优异的高倍率放电性能，在以4200mA／g电流放电时，La卜汉gx（NICoAI）36合金电极的放电容量是ABS型合金电极的3倍，达152hah／g，显示出良好的动力学特性。R，入1兮Ni（R：raree田劝，Ca，Y）型合金因能吸引／释放1．8一1．87％质量的HZ而被认为是种很有希望的贮氢合金。但其吸／放氢平台过高，循环寿命短。如何提高Rh厦g剑19循环稳定性是这类合金能否成功商业化的关键。研究发现，Co能够显著提高ABS型合金电极的循环寿命，但其价格太贵。人们发现Al在提高电极寿命方面与C。有类似的作用，但Al元素的添加因其在碱性电解质的作用下在电极表面易生成致密的氧化膜而不利于氢的扩散，进而对高倍率放电性能不利。入物在提高电极表面活性，改善其高倍率放电性方面作用明显。本工作在前面的基础上用Al和MO联合取代Ni，以期待同时改善La一Mg一Ni一Co合金的循环稳定性和高倍率放电性能。详细研究了La07Mg03Ni切一（A105Mo05）x（x：o，0．2，0．4，0．6，0．8）系列贮氢合金的晶体结构和电化学性能。X射线衍射及Rietveld分析发现：所有La07Mg03Ni4D一x（A105Mo05）x合金均为包含PuNi3结构的六方LaZMgNig相、CaCus结构的LaNis主相及L匆Ni7，LaN儿和LaNi杂相的多相结构。合金中La（La，Mg）剑19相及LaNis相的晶格参数及晶胞体积均随合金中Al和Mo含量的增加而增大。用电化学方法测得的RC一T曲线显示：Al和'fo部分取代Ni降低了氢的平台压力。随合金中Al和Mo含量的增加，电极的电化学容量从329．7（x＝0）、徽橇毓孺鑫盆一11瀚加至365．物A吨（＝0．6）后又降低到351．3毗吨（x＝0．8）。当以1200m刀g的电流密度进行放电时，其I｛RD从62．0％沁0）增加到82．1％沁0．8）。线性微极化结果显示：Al和Mo的添加增大了合金表面的交换电流密度，因而也改善了合金电极的高倍率放电性能。另外，Al和M。取代合金中的Ni增大了氢在电极合金中的扩散系数（D），改善了La07Mgo3Ni4。一x（Alo5M。。5）x（X＝o，0．2，0．4，0．6，0．8）合金电极的低温放电性能（LTD）。