Subsurface damage of Nd-doped phosphate glasses in optical fabrication

We present a destructive method for detecting and measuring subsurface damage of Nd-doped phosphate glasses. An instrument based on the dimple method - a destructive method - was developed. Subsurface damage depth produced in each fabrication procedure was obtained. We extend the surface roughness-subsurface damage relation to Nd-doped phosphate glasses. The constant ratio of subsurface damage and surface roughness was obtained as well. We also analyse the relation of abrasive size and subsurface damage experimentally. From a measurement of the surface roughness or abrasive size, one can obtain an accurate estimate of the damage layer thickness that must be eliminated by polishing or subsequent grinding operations. (C) 2007 Elsevier GmbH. All rights reserved.

Effect of Fe impurity on the optical loss of Nd-doped phosphate laser glass

The optical loss coefficient at 1053-nm wavelength, influenced by Fe ions in N31-type Nd-doped phosphate laser glass, was determined precisely and analyzed in detail. It is found that the optical loss coefficient per unit of Fe concentration (cm^(-1)/ppmw) increases with Fe concentration in the range of 0---300 ppmw, but it approaches a constant as the Fe concentration is larger than 300 ppmw. Such a concentration effect is due to a shift in the redox equilibrium between Fe3+ and Fe2+ ions in the glass. The effect of oxygen pressure, temperature, and variable valence states of other metal ions in glass samples on the optical loss is also discussed.

Fluorescence properties and laser demonstrations of Nd-doped high silica glasses prepared by sintering nanoporous glass

Porous glass with high-SiO2 content was impregnated with Nd ions, and subsequently sintered at 1100 degrees C into a compact non-porous glass in air or reducing atmosphere. Sintering in a reducing atmosphere produced an intense violet-blue fluorescence at 394 nm. However, the sintering atmospheres almost did not affect the fluorescence properties in the infrared range. A good performance Nd3+-doped silica microchip laser operating at 1064 nm was demonstrated. The Nd-doped sintering glasses with high-SiO2 content are potential host materials for high power solid-state lasers and new transparent fluorescence materials. (c) 2007 Elsevier B.V. All rights reserved.

Magnetic coupling properties of rare-earth metals (Gd, Nd) doped ZnO: First-principles calculations

The electronic structure and magnetic coupling properties of rare-earth metals (Gd, Nd) doped ZnO have been investigated using first-principles methods. We show that the magnetic coupling between Gd or Nd ions in the nearest neighbor sites is ferromagnetic. The stability of the ferromagnetic coupling between Gd ions can be enhanced by appropriate electron doping into ZnO Gd system and the room-temperature ferromagnetism can be achieved. However, for ZnO Nd system, the ferromagnetism between Nd ions can be enhanced by appropriate holes doping into the sample. The room-temperature ferromagnetism can also be achieved in the n-conducting ZnO Nd sample. Our calculated results are in good agreement with the conclusions of the recent experiments. The effect of native defects (V-Zn, V-O) on the ferromagnetism is also discussed. (C) 2009 American Institute of Physics. [DOI 10.1063/1.3176490]

掺钕材料激光终态能级寿命测量

介绍了目前测量掺钕材料激光终态能级寿命的三种方法，通过对三种测量方法比较，采用间接法测量激光终态能级寿命相对简单易行。

固着磨料加工工艺对磷酸盐钕玻璃亚表面缺陷的影响

散粒磨料研磨与固着磨料研磨是光学研磨加工过程中的两种主要手段,但两者材料去除的机制不同。目前针对高功率固体激光装置中的主要工作物质——磷酸盐激光钕玻璃的亚表面缺陷(SSD)研究相对较少,因此在实验的基础上,通过系统地研究固着磨料对磷酸盐激光钕玻璃的研磨工艺过程,分析了多种因素,如磨料粒径、载荷大小、机床转速,以及结合剂材料与冷却液等对钕玻璃亚表面缺陷形成的影响,并与散粒磨料研磨工艺所产生的亚表面缺陷进行了比较,对关键工艺参数进行定量,为高质量钕玻璃制造工艺的选型以及进一步优化亚表面缺陷提供了重要的参考数据。

Nd-glass belt lasers with improved beam quality

Nd-doped phosphate glass belt lasers pumped by laser diodes are demonstrated. The Nd-glass belt with a large cross-section and a small Fresnel number is air-cooled to provide around 18-W continuous wave (CW) output power with a beam quality factor of My2

钕离子掺杂和钕铝共掺高硅氧玻璃的光谱性质研究

Nd-doped and Nd-Al-codoped high silica glasses were obtained by sintering porous glass impregnated with Nd3+ and Al3+ ions. The absorption, fluorescence spectra and fluorescence lifetime of Nd-doped and Nd-Al-codoped high silica glasses were measured. The intensity parameters Omega(1), ( t = 2, 4, 6), fluorescence lifetime, radiative quantum efficiency and stimulated emission cross section were calculated by Judd-Ofelt theory. The effect of aluminum codoping on the fluorescence and structural properties of Nd-doped silica glass has been discussed. By comparing the spectroscopic properties with other Nd-doped oxide glasses and commercial silicate glasses, this Nd-doped high silica glass is likely to be a promising laser material for use in high power and high repetition rate lasers.

Low heat and high efficiency Nd:GdVO4 laser pumped by 913 nm

A Nd:GdVO4 crystal is pumped directly into its emitting level at 913 nm for the first time to the best of our knowledge. 3.35 W output laser emitting at 1063 nm is achieved in a 1.1 at.% Nd-doped Nd:GdVO4. The crystal absorbs pumping light of 4.30 W at 913 nm and produces a very low quantity of heat with the opto-optic conversion efficiency of 77.2%. The average slope efficiency is 81.2% from 0.21 W, at the threshold, to 4.30 W of absorbed pump power. Because of the very weakly thermal effect, the near-diffraction-limit beam is easily obtained with beam quality factor of M-2 approximate to 1.1.

磷酸盐钕玻璃表面/亚表面损伤特性实验研究

系统地研究了光学研磨过程中,磨料粒径、载荷大小以及机床转速对钕玻璃表面及亚表面损伤的影响。结果表明,机床转速和载荷基本不改变材料表面粗糙度,而较大载荷或较低机床转速产生较大的亚表面缺陷,表面粗糙度和亚表面缺陷缺陷深度基本与最大磨料粒径呈正比,载荷增倍使亚表面缺陷与表面粗糙度的常数比值增加0.05。研究结果为钕玻璃加工工艺改进提供了参考依据。