Controlled synthesis of nanoporous Au microsheet via surfactant emulsion template

A facile and wet-chemical approach was employed to control synthesis of self-organizing, hyperbranched nanoporous Au microsheet with high quality in bulk quantity. This method produced nanoporous Au microsheets with a thickness of 7-15 nm. The microsheets were composed of irregularly interconnected planar Au nanoplates with interstices, i.e. nanopores of 10-50 nm. And the nanoporous Au microsheets were enveloped in 10-30 nm thick polyaniline (PANI) sheaths. The morphology of the nanostructured Au composites could also be easily tuned by changing the concentration of aniline and chlorauric acid. The dendritic and epitaxial growth of nanoporous Au microsheet was believed as the diffusion-limited process confined in the lamellar emulsion phase through self-assembly of aniline and dodecylsulfate. The solution reaction proceeded at a mild condition (room temperature and aqueous solutions), and less toxic reagents were employed instead of extreme toxic and corrosive chemicals.

Renormalization group approach on nanostructured systems

The electronic spectra of one-dimensional nanostructured systems are calculated within the pure hopping model on the tight-binding Hamiltonian. By means of the renormalization group Green's function method, the dependence of the density of states on the distributions of nanoscaled grains and the changes of values of hopping integrals in nanostructured systems are studied. It is found that the frequency shifts are dependent rather on the changes of the hopping integrals at nanoscaled grains than the distribution of nanoscaled grains.

Structural and optical properties of nanostructured TiO2 thin films fabricated by glancing angle deposition

TiO2 films deposited by electron beam evaporation with glancing angle deposition (GLAD) technique were reported. The influence of flux angle on the surface morphology and the microstructure was investigated by scanning electron microscopy. The GLAD TiO2 films are anisotropy with highly orientated nanostructure of the slanted columns. With the increase of flux angle, refractive index and packing density decrease. This is caused by the shadowing effect dominating film growth. The anisotropic structure of TiO2 films results in optical birefringence, which reaches its maximum at the flux angle alpha = 65 degrees. The maximum birefringence of GLAD TiO2 films is higher than that of common bulk materials. It is suggested that glancing angle deposition may offer an effective method to obtain tailorable refractive index and birefringence in a large continuous range. (c) 2006 Elsevier B.V. All rights reserved.

Preparation and characterization of nanostructured ZrO2 thin films by glancing angle deposition

ZrO2 films were prepared by electron beam evaporation with glancing angle deposition (GLAD) technique. The as-deposition and annealed ZrO2 films are all amorphous, different from that deposited at normal incidence. Due to the shadowing effect, a highly orientated structure composed of slanted columns formed, and the obtained films became the mixture of slanted columns and voids. The relationship among the effective refractive index, packing density and flux incident angle was investigated. The refractive index and packing density of ZrO2 films decrease with the increase of the incident angle. The in-plane birefringence of GLAD ZrO2 films was calculated. At the packing density of 0.576, the maximum birefringence is 0.037. (c) 2006 Elsevier B.V. All rights reserved.

Preparation of self-supporting hierarchical nanostructured anatase/rutile composite TiO2 film

Via the combination of an electrospinning method with a hydrothermal reaction, a large-scale cedar-like hierarchical nanostructured TiO2 film with an anatase/rutile composite phase was fabricated.

Replacement of methane from quartz sand-bearing hydrate with carbon dioxide-in-water emulsion

The replacement of CH4 from its hydrate in quartz sand with 90:10, 70:30, and 50:50 (W-CO2:W-H2O) carbon dioxide-in-water (C/W) emulsions and liquid CO2 has been performed in a cell with size of empty set 36 x 200 mm. The above emulsions were formed in a new emulsifier, in which the temperature and pressure were 285.2 K and 30 MPa, respectively, and the emulsions were stable for 7-12 h. The results of replacing showed that 13.1-27.1%, 14.1-25.5%, and 14.6-24.3% of CH4 had been displaced from its hydrate with the above emulsions after 24-96 It of replacement, corresponding to about 1.5 times the CH4 replaced with high-pressure liquid CO2. The results also showed that the replacement rate of CH4 with the above emulsions and liquid CO2 decreased from 0.543, 0.587, 0.608, and 0.348 1/h to 0.083, 0.077, 0.069, and 0.063 1/h with the replacement time increased from 24 to 96 h. It has been indicated by this study that the use of CO2 emulsions is advantageous compared to the use of liquid CO2 in replacing CH4 from its hydrate.

Formation of a novel type of reverse microemulsion system and its application in synthesis of the nanostructured La0.95Ba0.05MnAl11O19 catalyst

In the study, a novel microemulsion system, consisting of water, iso-propanol and n-butanol, was developed to synthesize the nanostructured La0.95Ba0.05MnAl11O19 catalyst with high surface area and catalytic activity for methane combustion.

The synthesis of nanostructured W2C on ultrahigh surface area carbon materials via carbothermal hydrogen reduction

Nanostructured tungsten carbides were synthesized, for the first time, with a size distribution of 5-12 nm on ultrahigh surface area carbon material, by carbothermal hydrogen reduction (CHR) at 850degreesC and metal Ni promoted CHR at 650 degreesC.

Nanostructured bulk novel hard material with "rounded" grains obtained by nanocrystalline "rounded" (W0.5Al0.5)C powders

A novel nano-scaled bulk hard material (W0.5Al0.5)C-Co with "rounded" grains was prepared by nanocrystalline "rounded" (W0.5Al0.5)C powders with "rounded" particle shape in this study. The nano-scaled "rounded" particles do not contain sharp edges, which form local tensile stress concentrations on loading of the composite, thus leading to improved toughness and reduced sensitivity to crack. Nanocrystalline (W0.5Al0.5)C powders with "rounded" particle shape were used as starting materials. X-ray diffraction, scanning electron microscopy, and transmission electron microscopy were used to characterize the samples.

Nanostructured novel cemented hard alloy obtained by mechanical alloying and hot-pressing sintering and its applications

A novel cemented carbides (W0.8Al0.2)C-0.7-Co with different cobalt contents were prepared by mechanical alloying and hot-pressing technique. Hot-pressing technique as a common technique was performed to fabricate the bulk bodies of the hard alloys. The novel cemented carbides have superior mechanical properties compared with WC-Co. The density, operate cost of the novel material were much lower than WC-Co system. The novel materials were easy to process nanoscale sintering and get the rounded particles in the bulk materials.

Nanostructured CaWO4, CaWO4 : Eu3+ and CaWO4 : Tb3+ particles: Sonochemical synthesis and luminescent properties

Nanostructured CaWO4, CaWO4:Eu3+, and CaWO4:Tb3+ phosphor particles were synthesized via a facile sonochemical route. X-ray diffraction, Fourier transform infrared spectroscopy, field emission scanning electron microscopy, transmission electron microscopy, photoluminescence, low voltage cathodoluminescence spectra, and photoluminescence lifetimes were used to characterize the as-obtained samples. The X-ray diffraction results indicate that the samples are well crystallized with the scheelite structure of CaWO4.