Graphitic nanofilaments as novel support of Ru-Ba catalysts for ammonia synthesis

A novel graphitic-nanofilament-(GNF-) supported Ru-Ba catalyst is prepared and used in ammonia synthesis reaction. The Ru-Ba/GNFs catalyst shows remarkably high activity and stability for ammonia synthesis, which can be attributed to high purity and graphitization of GNFs with unique structure. TEM micrographs of the Ru-Ba/GNFs catalysts show that Ru metal particles uniformly disperse on the outer wall of GNFs, and the particles become bigger than that before ammonia synthesis reaction after 50 h of operation at 500degreesC and 7.0 MPa, probably due to the Ru crystals covered by promoter and support materials and/or sintering of Ru crystals. (C) 2002 Elsevier Science (USA).

Ammonia synthesis on graphitic-nanofilament supported Ru catalysts

Graphitic-nanofilaments (GNFs) supported ruthenium catalysts were prepared and characterized by NZ physisorption, X-ray diffraction (XRD), transmission electron microscope (TEM) and temperature programmed reduction-mass spectroscopy (TPR-MS) and used for ammonia synthesis in a fixed bed microreactor. The TEMs of the Ru/GNFs and Ru-Ba/GNFs catalysts indicate that the Ru particles are in the range of 2-4 nm, which is the optimum size of Ru particles for the maximum number of B5 type sites. The activity of Ru-Ba/GNFs catalysts is higher than that of Ru-Ba/AC by about 25%. The methanation reaction on the Ru/GNFs catalyst is remarkably inhibited compared with a Ru/AC catalyst. High graphitization of GNFs is likely to be the reason for the high resistance to the methanation reaction. The power rate law for ammonia synthesis on Ru-Ba/GNFs catalysts can be expressed by r = Kp(NH3)(-0.4) P-N2(0.8) P-H2(-0.7), indicating that H-2 is an inhibitor for N-2 activation on the catalyst. Catalysts with the promoters Ba, K and Cs show large differences in activity for ammonia synthesis. The catalyst promoted with Ba (Ba/Ru = 0.2 molar ratio) was found to be the most active, whereas that with a K promoter was the least active. (C) 2003 Elsevier B.V. All rights reserved.

Perfectly Hydrophobic Silicone Nanofiber Coatings: Preparation from Methyltrialkoxysilanes and Use as Water-Collecting Substrate

Perfectly hydrophobic (PHO) coatings consisting of silicone nanofibers have been obtained via a solution process using methyltrialkoxysilanes as precursors. On the basis of thermal gravimetry and differential thermal analysis (TG-DTA) and Fourier transform infrared spectroscopy (FTIR) results, the formula of the nanofibers was tentatively given and a possible growth mechanism of the nanofibers was proposed. Because of the low affinity between the coatings and the small water droplet, when using these coatings as substrate for collecting water vapor, the harvesting efficiency could be enhanced as compared with those from bare glass substrate for more than 50% under 25 degrees C and 60-90% relative humidity. By removing the surface methyl group by heat treatment or ultraviolet (UV) irradiation, the as-prepared perfectly hydrophobic surface can be converted into a superhydrophilic surface.

Photochemical formation of silver and gold nanostructures at the air-water interface and their electrocatalytic properties

In this paper, we report a simple method of fabricating silver and gold nanostructures at the air - water interface, which can be spontaneously assembled through the reduction of AgNO3 and HAuCl4 with ultraviolet (UV) irradiation in the presence of polyacrylic acid (PAA), respectively. It was found that the building blocks in the silver nanostructure are mainly interwoven silver nanofilaments, while those of the gold nanostructure are mainly different sizes of gold nanoparticles and some truncated gold nanoplates, and even coalescence into networks. At the air - water interface, these silver and gold nanostructures can be easily transferred onto the surface of indium tin oxide (ITO) slides and used for electrochemical measurements. After a replacement reaction with H2PdCl4, the silver nanostructure is transformed into a Ag - Pd bimetallic nanostructure, with good electrocatalytic activity for O-2 reduction. The gold nanostructure can also show high electrocatalytic activity to the oxidation of nitric oxide (NO) with a detection limit of about 10 mu M NaNO2 at S/N = 3.