Sol-gel combustion synthesis and luminescence Of Y4Al2O9 : Eu3+ nanocrystal

Y4Al2O9:EU3+ phosphor was synthesized through a sol-gel combustion method. The Y4Al2O9 phase can form through sintering at 800 degrees C. This temperature is much lower than that required via the solid state reaction method. The average grain size of the phosphor was about 30 run. Compared with the amorphous phosphor, the charge transfer band of crystalline phosphor shows a blue shift. The emission Of Y4Al2O9:Eu3+ indicates the existence of two luminescent centers, in agreement with the crystal structure of Y4Al2O9. Higher doping concentration could be realized in Y4Al2O9 nanocrystal host lattice. This indicates that the sol-gel combustion synthesis method can increase emission intensity and quenching concentration due to a good distribution of EU3+ activators in Y4Al2O9 host. (c) 2005 Elsevier B.V. All rights reserved.

Nanoporous In2O3 nanocrystal clusters: One-step synthesis, thermal stability and optical property

Nanoporous In2O3 nanocrystal clusters with high surface areas have been synthesized by a one-step solvent-thermal method at a relatively low temperature. On the basis of our experimental data and nanomaterial growth mechanism, a template-assistant dehydration accompanied by aggregation mechanism was proposed to explain their formation. Besides, the influence of the high-temperature treatment on their porous structure and optical properties were studied and compared by various technologies.

Direct synthesis and intense luminescence of Y2O3 : Eu nanophosphors by complexation combustion

In this paper, we report the synthesis of high-luminance Y2O3:Eu nanocrystal through a citrate-nitrate complexation combustion method at a low temperature of 200-280 degrees C. The as-combusted Y2O3:Eu phosphors are almost equiaxed crystallites with an average size of 30-40 run, and have an intense red luminescence. The present fuel-deficient method suggests that by control of the ratio of citric acid to nitrates, it is valuable for the fabrication of Y2O3 nanoparticles without heat treatment. This process should be applicable to a wide range of nanocrystal oxides.

Synthesis and characterization of magnetite dodecahedron nanostructure by hydrothermal method

Magnetite dodecahedral nanocrystals were fabricated using ethlenediamine tetraacetic acid (EDTA)-mediated hydrothermal route. Scanning electron microscopy images displayed that the products were almost dodecahedrons. The length of two different ribs were about 300 and 200 nm, respectively. X-ray diffraction patterns showed that the products were the cubic inverse spinel structure. Fourier transform infrared spectrum directly provided evidence of the EDTA bound to a specific surface of the precipitated magnetic nanocrystal.

Shape and Phase-Controlled Synthesis of KMgF3 Colloidal Nanocrystals via Microwave Irradiation

In this paper, we present a facile one-step route to controlled synthesis of colloidal KMgF3 nanocrystals via the thermolysis of metal trifluoroacetate precursors in combined solvents (OA/OM) using microwave irradiation. X-ray diffraction (XRD), transmission electron microscopy (TEM), thermogravimetric and differential thermal analysis (TG-DTA), Fourier transform infrared (FT-IR) spectra, and photoluminescence (PL) spectra were employed to characterize the samples. Only through the variation of the OA/OM ratio, can the phase and shape of nanocrystals be readily controlled, resulting in the formation of well-defined near-spherical nanoparticles, and nanoplates of cubic-phased KMgF3, as well as nanorods of tetragonal-phased MgF2, and a possible mechanism has been proposed to elucidate this effect. Furthermore, all these samples in this system can be well dispersed in nonpolar solvents such as cyclohexane to form stable and clear colloidal solutions, due to the successful coating of organic surfactants (OA/OM) on the nanocrystal surface.

Synthesis and characterization of SiO2/Gd2O3 : Eu core-shell luminescent materials

Europium-doped Gd2O3 with an average size of similar to15 nm was coated on the surface of preformed silica nanospheres by the wet chemical method. SEM and TEM photographs showed that SiO2/Gd2O3:Eu core-shell submicrospheres are obtained. XRD patterns indicated that the Gd2O3:Eu shell is crystalline after heat treatment. FTIR and XPS spectra showed that the Gd2O3:Eu shell is linked to the silica surface by forming a Si-O-Gd bond. Photoluminescence studies showed that the luminescent properties are still retained after coating on an inert silica core; additionally, we noted that the emitting peaks are broadened, which results from size effects and interface effects of nanocrystal.