Hard magnetic properties of Sm3Fe26.7VxN4 and Sm3Fe26.7VxCy

Sm3Fe26.7V2.3N4 nitrides and Sm3Fe26.7V2.3Cy carbides have been synthesized by gas-solid phase reaction. Their hard magnetic properties have been investigated by means of additional ball-milling at room temperature. The saturation magnetization of Sm3Fe26.7V2.3N4 almost decreases linearly with increasing ball-milling time t, but that of Sm3Fe26.7V2.3Cy has no obvious change when the ball-milling time increases from t = 1 to 28 h. As a preliminary result, the maximum remanence B-r of 0.94 and 0.88 T, the coercivity mu(0i)H(C) of 0.75 and 0.25 T, and the maximum energy product (BH) of 108.5 and 39.1 kJ/m(3) for their resin-bonded permanent magnets are achieved, respectively, by ball-milling at 293 K. (C) 1999 Published by Elsevier Science B.V. All rights reserved.

Crystallographic and electrochemical characteristics of TiZrNiCu quasicrystal ball-milled with La0.9Zr0.1Ni4.5Al0.5 alloy

Icosahedral quasicrystalline Ti45Zr35Ni17Cu3 alloy was ball-milled with 30 mass% La0.9Zr0.1Ni4.5Al0.5 alloy (LaNi5 phase), the effect of the milling time on crystallographic and electrochemical characteristics of the alloy powder was investigated. The amount of amorphous phase increased with increasing milling time from 60 to 360 min, and the LaNi5 phase cannot be observed when milling time was 240 min or more. The maximum discharge capacity and high-rate dischargeability of milled alloy electrodes were obviously higher than those of the alloy electrode before milling. The cycling capacity retention rate after 40 cycles increased from 52.8% (t = 60 min) to 62.9% (t = 360 min).

Crystallographic and electrochemical properties of ball-milled quasicrystalline Ti45Zr35Ni17Cu3 alloy with 20 mass% Ni

Icosahedral quasicrystalline Ti45Zr35Ni17Cu3 alloy powder was ball-milled with 20 mass% Ni, and the effect of the ball-milling time (t) on crystallographic and electrochemical characteristics were investigated. The amounts of icosahedral quasicrystalline and Ni phases decreased when ball-milling time increased from 30 to 180 min. The powder consisted of amorphous and (Ni and Ti) phases after 360 min of ball-milling. The maximum discharge capacity of the powder electrodes first increased from 89 (t = 0 min) to 192 mAh g(-1) (t = 180 min), and then decreased to 138 mAh g(-1) (t = 360 min). The high-rate dischargeability and the discharge capacity after 15 cycles increased with increasing ball-milling time.

Formation of epsilon-FeXN/BN magnetic nanocomposite and its thermodynamic and kinetic analyses

A nanocomposite of nanometer-sized magnetic granular epsilon-FeXN embedded in a nonmagnetic amorphous boron nitride matrix was prepared by ball milling mixture of alpha-Fe and hexagonal boron nitride in argon atmosphere. The grain size of the epsilon-FeXN alloy was about 10-20 nm. The nitrogen concentration in the epsilon-FeXN alloy increases with extending milling time. Both thermodynamic calculation and the present experiment show that iron and nitrogen atoms have higher alloying driving force than iron and boron atoms. Analyses of thermodynamics and kinetics about formation of the epsilon-FeXN alloy suggested that the formation of the epsilon-FeXN alloy is related to amorphization of the hexagonal boron nitride and refinement of the alpha-Fe. II was found from the present experiment that a critical grain size of the alpha-Fe reacting with nitrogen in the amorphous boron nitride is about 8 nm.