A small arc-heated plasma testing facility for thermal protection materials

Experimental research on a 150 kW arc-heated plasma testing facility was conducted. Stable plasma jets with different gas compositions, temperatures and velocities were obtained at chamber pressure between 400 Pa – 100 kPa. Stagnation ablation experiments were conducted on samples of typical super alloys used for thermal protection systems. The microstructure and hardness of alloys before and after ablation were compared.

Crack tip behavior and crack-propagation in ductile materials

Dilatational plastic equations, which can include the effects of ductile damage, are derived based on the equivalency in expressions for dissipated plastic work. Void damage developed internally at the large-strain stage is represented by an effective continuum being strain-softened and plastically dilated. Accumulation of this local damage leads to progressive failure in materials. With regard to this microstructural background, the constitutive parameters included for characterizing material behaviour have the sense of internal variables. They are not able to be determined explicitly by macroscopic testing but rather through computer simulation of experimental curves and data. Application of this constitutive model to mode-I cracking examples demonstrates that a huge strain concentration accompanied by a substantial drop of stress does occur near the crack tip. Eventually, crack propagation is simulated by using finite elements in computations. Two numerical examples show good accordance with experimental data. The whole procedure of study serves as a justification of the constitutive formulation proposed in the text.

Static and fatigue failure behavior of carbon-fiber reinforced epoxy composite-materials with edge notch

A study of carbon fiber reinforced epoxy composite material with 0° ply or ±45°ply(unnotched or with edge notch) was carried out under static tensile and tension-tensioncyclic loading testing. Static and fatigue behaviour and damage failure modes in unnotched/notched specimens plied in different manners were analysed and compared with each other.A variety of techniques (acoustic emission, two types of strain extensometer, high speed pho-tography, optical microscopy, scanning electron microscope, etc.) were used to examine thedamage of the laminates. Experimental results show that when these carbon/epoxy laminateswith edge notch normal to the direction of the load are axially loaded in static or fatiguetension, the crack does not propagate along the length of notch but is in the interface (fiberdirection). The notch has no substantial effect on the stresses at the unnotched portion. Thedamage failure mechanism is discussed.

Real-time non-destructive testing of dynamic holograms in doubly-doped LiNbO3 crystals using phase-conjugate technique

Nankai University

A new cellular model for in vitro biocompatibility evaluation of microcapsule materials

Fibrosis caused by the host response to long-term transplanted microcapsules and the limitation of traditional L929 cell model for biocompatibility testing inspire the development of an assay of biocompatibility based on macrophage behavior. In this paper, the human monocytic cell line THP-1 was utilized for biocompatibility evaluation of microcapsule materials. The cell viability and secretion of nitric oxide (NO) and cytokines served as index of biocompatibility were assayed. It was found that the evaluated microcapsule materials had no effect on the stimulation of NO and cytokines secretion, which meant that these materials were biocompatible. Furthermore, it suggests the THP-1 cell a convenient in vitro experimental model that might be useful for long-term predictions of material biocompatibility.