Temperature and pressure dependences of the Mn2+ and donor-acceptor emissions in ZnS : Mn2+ nanoparticles

Temperature and pressure dependent measurements have been performed on 3.5 nm ZnS:Mn2+ nanoparticles. As temperature increases, the donor-acceptor (DA) emission of ZnS:Mn2+ nanoparticles at 440 nm shifts to longer wavelengths while the Mn2+ emission (T-4(1)-(6)A(1)) shifts to shorter wavelengths. Both the DA and Mn2+ emission intensities decrease with temperature with the intensity decrease of the DA emission being much more pronounced. The intensity decreases are fit well with the theory of thermal quenching. As pressure increases, the Mn2+ emission shifts to longer wavelengths while the DA emission wavelength remains almost constant. The pressure coefficient of the DA emission in ZnS:Mn2+ nanoparticles is approximately -3.2 meV/GPa, which is significantly smaller than that measured for bulk materials. The relatively weak pressure dependence of the DA emission is attributed to the increase of the binding energies and the localization of the defect wave functions in nanoparticles. The pressure coefficient of Mn2+ emission in ZnS:Mn2+ nanoparticles is roughly -34.3 meV/GPa, consistent with crystal field theory. The results indicate that the energy transfer from the ZnS host to Mn2+ ions is mainly from the recombination of carriers localized at Mn2+ ions. (C) 2002 American Institute of Physics.

Pressure dependence of Mn2+ fluorescence in ZnS : Mn2+ nanoparticles

The photoluminescence of Mn2+ in ZnS:Mn2+ nanoparticles with an average size of 4.5 nm has been measured under hydrostatic pressure from 0 to 6 GPa. The emission position is red-shifted at a rate of -33.3+/-0.6meV/GPa, which is in good agreement with the calculated value of -30.4meV/GPa using the crystal field theory. (C) 2000 Elsevier Science B.V. All rights reserved.

Energy structure and fluorescence of Eu2+ in ZnS : Eu nanoparticles

Eu2+-doped ZnS nanoparticles with an average size of around 3 nm were prepared, and an emission band around 530 nm was observed. By heating in air at 150 degrees C, this emission decreased, while the typical sharp line emission of Eu3+ increased. This suggests that the emission around 530 nm is from intraion transition of Eu2+: In bulk ZnS:Eu2+, no intraion transition of Eu2+ was observed because the excited states of Eu2+ are degenerate with the continuum of the ZnS conduction band. We show that the band gap in ZnS:Eu2+ nanoparticles opens up due to quantum confinement, such that the conduction band of ZnS is higher than the first excited state of Eu2+, thus enabling the intraion transition of Eu2+ to occur.