PREPARATION AND MICROSTRUCTURAL CHARACTERIZATION OF SURFACE-MODIFIED NANOSIZED SNO2 PARTICLES

Nanosized stannic oxide particles modified with a layer of DBS were successfully prepared through the colloidal chemical method and their microstructures were characterized. FTIR and XPS were used for the determination of the main components. It can be proved that the nanosized SnO2 particles were capped by DBS. The sizes of particle were determined by TEM and XRD. By the investigation of XPS, we can conclude that there are a lot of oxygen vacancies in the surface of the nanoparticulates. Based on this conclusion, the ESR signal of the sample can be explained.

Microstructure and mechanical properties of a novel Zr-based bulk metallic glass composite

Zr48.5Cu46.5Al5 bulk metallic glass (BMG) composites with diameters of 3 and,4 mm were prepared through suction casting in an arc melting furnace by modulating the alloy composition around the monothetic BMG composition of the high glass forming ability. Microstructural characterization reveals that the composites contain micron-sized CuZr phase with martensite structure, as well as nano-sized Zr2Cu crystalline particles and Cu10Zr7 plate-like phase embedded in an amorphous matrix. Room temperature compression tests showed that the composites exhibited significant strain hardening and obvious plastic strain of 7.7% for 3 nun and 6.4% for 4 nun diameter samples, respectively.

Influence of laser-glazing on hot corrosion resistance of yttria-stabilized zirconia TBC in molten salt mixture of V2O5 and Na2SO4

Plasma-sprayed 8YSZ (zirconia stabilized with 8 wt% yttria)/NiCoCrAlYTa thermal barrier coatings (TBCs) were laser-glazed using a continuous-wave CO2 laser. Open pores within the coating surface were eliminated and an external densified layer was generated by laser-glazing. The hot corrosion resistances of the plasma-sprayed and laser-glazed coatings were investigated. The two specimens were exposed for the same period of 100 h at 900 degrees C to a salt mixture of vanadium pentoxide (V2O5) and sodium sulfate (Na2SO4). Serious crack and spallation occurred in the as-sprayed coating, while the as-glazed coating exhibited good hot corrosion behavior and consequently achieved a prolonged lifetime. The results showed that the as-sprayed 8YSZ coating achieved remarkably improved hot corrosion resistance by laser-glazing.

Structural characterization of mn implanted AlInN

AlInN/GaN thin films were implanted with Mn ions and subsequently annealed isochronically at 750 and 850 degrees C. X-ray diffraction and Rutherford backscattering spectroscopy (RBS) techniques were employed to study the microstructural properties of the implanted/annealed samples. The effect of annealing on implantation-induced strain in thin films has been studied in detail. The strain was found to increase with dose until it reached a saturation value and after that it started decreasing with a further increase in the dose. RBS measurements indicated the atomic diffusion of In, Al, Ga and Mn in implanted samples. The in- and out-diffusion of atoms has been observed after annealing at 750 degrees C and 850 degrees C, respectively. Strong decomposition of the samples took place when annealed at 850 degrees C.

Structural characterization of stable amorphous silicon films

A kind of hydrogenated diphasic, silicon films has been prepared by a new regime of plasma enhanced chemical vapor deposition (PECVD) in the region adjacent to the phase transition from amorphous to crystalline state. The photoelectronic and microstructural properties of the films have been investigated by the constant photocurrent method (CPM), Raman scattering and nuclear magnetic resonance (NMR). Our experimental results and corresponding analyses showed that the diphasic films, incorporated with a subtle boron compensation, could gain both the fine photosensitivity and high stability, provided the crystalline fraction (f) was controlled in the range of 0 < f < 0.3. When compared with the conventional hydrogenated amorphous silicon (a-Si:H), the diphasic films are more ordered and robust in the microstructure, and have a less clustered phase in the Si-H bond configurations. (C) 2002 Elsevier Science Ltd. All rights reserved.

Characterization of diphasic nc-Si/a-Si : H thin films and solar cells

Hydrogenated silicon films with diphasic structure have been prepared by using a new regime of plasma enhanced chemical vapor deposition (PECVD) in the region adjacent to the phase transition from amorphous to crystal. line state. The photoelectronic and microstructural properties of the films have been characterized by the constant photocurrent method (CPM), Raman scattering and nuclear magnetic resonance (NMR). In comparison with typical hydrogenated amorphous silicon (a-Si:H), these diphasic films with a crystalline fraction less than 0.3 show a similar optical absorption coefficient, lower deep-defect densities and higher stability upon light soaking. By using the diphasic nc-Si/a-Si films a p-i-n junction solar cell has been prepared With an initial efficiency of 8.51 % and a stabilized efficiency of 8.02 % on an area of 0.126 cm(2) (AM1.5, 100 mW/cm(2)).

Structural characterization and property of in-situ synthesized AZ91-Mg2Si composite

A new-type Mg2Si composite was prepared with Mg-9Al-1Zn (AZ91) alloy and vermiculite as raw materials by melt infiltration method. The results show that the microstructure of composite consists of a large amount Of Mg2Si precipitates and a little amount of MgO embedded in alpha-Mg matrix. The Vickers hardness of the composite is obviously higher than that of matrix of AZ91 alloy. Moreover, the composite exhibits excellent compressive property. The ultimate compressive strength of the material is 290 MPa, the yield strength is 175 MPa, and the elongation is about 5%, which are higher than those of AZ91 alloy.