Resumo:
To understand mechanisms underlying laser-induced damage of BK7 and fused silica, we calculate the temperature field of the substrates with CO2 laser irradiating at a given laser power and beam radius. We find that the two glasses show different thermal behaviors. A model is developed for estimating the time t to heat the surface of the substrates up to a particular temperature T with cw CO2 laser irradiation. We calculate theoretically the duration t that the samples are irradiated, from the beginning to visual catastrophic damage, with the assumption of damage threshold determined by the critical temperature. The duration t that the samples are irradiated, from the beginning to visual catastrophic damage, is investigated experimentally as well. Here we take the melting point or softening point as the critical temperature, given the thermomechanical coupling properties, which is enough to cause damage for BK7. Damage features are characterized by the sound of visual cracks. Finally, we calculate stresses induced by laser heating. The analysis of stress indicates that the damage of BK7 is due to the stresses induced by laser heating. (c) 2005 Society of Photo-Optical Instrumentation Engineers.
Resumo:
To understand mechanisms underlying laser-induced damage of BK7 and fused silica, we calculate the temperature field of the substrates with CO2 laser irradiating at a given laser power and beam radius. We find that the two glasses show different thermal behaviors. A model is developed for estimating the time t to heat the surface of the substrates up to a particular temperature T with cw CO2 laser irradiation. We calculate theoretically the duration t that the samples are irradiated, from the beginning to visual catastrophic damage, with the assumption of damage threshold determined by the critical temperature. The duration t that the samples are irradiated, from the beginning to visual catastrophic damage, is investigated experimentally as well. Here we take the melting point or softening point as the critical temperature, given the thermomechanical coupling properties, which is enough to cause damage for BK7. Damage features are characterized by the sound of visual cracks. Finally, we calculate stresses induced by laser heating. The analysis of stress indicates that the damage of BK7 is due to the stresses induced by laser heating. (c) 2005 Society of Photo-Optical Instrumentation Engineers.
Resumo:
高功率大尺寸激光玻璃硬包边技术对于提高激光玻璃的饱和增益系数具有非常重要的价值。本文采用传统的玻璃熔制方法,研究了Li-Na混合碱效应对磷酸盐包边玻璃折射率、热膨胀系数α、玻璃转变温度Tg、膨胀软化温度Td以及溶解速率(DR)的影响规律。研究结果表明:当Li/(Li+Na)=0.5时,Tg、Td和DR取得极小值,表明混合碱效应既能降低包边玻璃的转变温度,又能提高包边玻璃的化学稳定性,这些性质对于包边玻璃的设计是非常可贵的。
Resumo:
包边技术是提高大尺寸激光玻璃饱和增益系数的关键技术。采用传统的方法熔制玻璃,研究了 P2O5含量对 P2O5-Al2O3-B2O3-CuCl-Na2O-ZnO磷酸盐包边玻璃的折射率、热膨胀系数、玻璃转变温度、膨胀软化温度以及化学稳定性的影响。结果表明:当 P2O5的摩尔分数为 60%左右,玻璃样品具有最高的折射率(1.522 0)、最低的玻璃转变温度(352.4 ℃)、较好的化学稳定性[0.52 mg/(cm^2·d)]和适宜的热膨胀系数(128.427×10^-7/℃),是用作钕磷酸盐激光玻璃硬包边的理
Resumo:
The structure of the titanate glass is destroyed during irradiation by the femtosecond laser pulses, and (TiO6)(8-) and (TiO4)(4-) anion units are exsolved from the network of the titanate glass. These anion units are rearranged to form some crystals such as anatase and Ba2TiO4 crystals. By Raman spectroscopy, it is found that these crystals have a strong dependence on the intensity of the femtosecond laser pulses. The relation between the generation of these crystals and space distribution of the femtosecond laser power intensity is qualitatively explained. (c) 2005 Elsevier B.V. All rights reserved.
Resumo:
We report on photoreduction of Ag+ in aluminoborate glasses induced by irradiation of a femtosecond laser. Novel fluorescence was observed in the femtosecond laser irradiated glass when excited by a 365 nm ultraviolet lamp. Optical absorption, emission, and electron spin resonance spectra of the glass samples demonstrated that after the laser irradiation, portions of silver ions near the focused part of the laser beam inside the glass were reduced to silver atoms, which resulted in the formation of the characteristic fluorescence. The observed phenomenon may have promising applications in the fabrication of functional optical devices.
Resumo:
对不同辐照条件下近红外飞秒激光在K9玻璃内部诱导产生的暗化现象和永久性折射率改变进行了实验研究。通过辐照前后的显微镜图片、吸收光谱、电子自旋共振谱(ESR)以及激光衍射实验,分析了K9玻璃中暗化现象产生的微观过程,发现暗化是由诱导产生的空穴型色心引起的。暗化程度和折射率改变随激光强度、扫描速度、扫描行间距变化而变化。光致色心的形成与非线性电离有关。对折射率永久性改变进行了简单说明,其机理仍在探索中。
Resumo:
总结了飞秒激光与晶体和玻璃相互作用产生的新现象,如光致折射率改变、光致晶体相变、光还原稀土离子及光致发光等。并分析了它们可能的应用。同时简要的介绍了各种现象产生的机理,展望了飞秒激光与其它物质相互作用可能的研究方向及可能出现的新现象。指出了进行这些研究时可能采用的新方法。
Resumo:
A novel multicomponent thick metallic glass coating has been synthesised by laser cladding. The maximum coating thickness was I mm. The clad cooling rate restrained the epitaxial growth of dendrites in the metallic glass coating. The metallic glass had high glass forming ability with a wide supercooled liquid region ranging from 59 to 70 K. The metallic glass coating also revealed high hardness and good corrosion resistance.
Resumo:
A thick amorphous alloy (a-alloy) coating was synthesized by laser cladding. The a-alloy had a multicomponent chemistry, i.e., Ni66Cr5MO4Zr6P15B4 (in atom%). The maximum thickness of the coating is 0.8 mm. The a-alloy coating had large glass-forming ability (GFA) with wide supercooled liquid region (SLR) ranging from 52 to 61 K through the coating. The reason for high GFA in the a-alloy coating was discussed. (C) 2002 Published by Elsevier Science B.V.
Resumo:
We investigate the mechanism of selective metallization on glass surfaces with the assistance of femtosecond laser irradiation followed by electroless plating. Irradiation of femtosecond laser makes it possible to selectively deposit copper microstructures in the irradiated area on glass surfaces coated with silver nitrate films. The energy-dispersive X-ray (EDX) analyses reveal that silver atoms are produced on the surface of grooves formed by laser ablation, which serve as catalysis seeds for subsequent electroless copper plating. (C) 2008 Elsevier B.V. All rights reserved.
Resumo:
We report micromodification of Eu element distribution in a silicate glass with femtosecond laser irradiation. Elemental analysis shows that the content of Eu decreased at the focal point and increased in a ring-shaped region around the focal point, which indicates migration of Eu ions has been induced by the femtosecond laser irradiation. Confocal fluorescence spectra demonstrate that the fluorescence intensity of Eu3+ ions increased by 20% in the laser-induced, Eu-enriched, ring-shaped region compared with that for nonirradiated glass. The mechanism for the laser induced change in fluorescence properties of Eu3+ has been investigated. (C) 2009 Optical Society of America
Resumo:
We investigated the effect of cerium oxide on the precipitation of Ag nanoparticles in silicate glass via a femtosecond laser irradiation and successive annealing. Absorption spectra show that Ce3+ ions may absorb part of the laser energy via multiphoton absorption and release free electrons, resulting in an increase of the concentration of Ag atoms and a decrease of the concentration of hole-trapped color centers, which influence precipitation of the Ag nanoparticles. In addition, we found that the formed Ag-0 may reduce Ce4+ ions to Ce3+ ions during the annealing process, which inhibits the growth of the Ag nanoparticles.
Resumo:
An erratum is presented to correct the propagation loss of the freestanding optical fibers fabricated in glass chip. (c) 2006 Optical Society of America.
Resumo:
Multiple refocusing of a tightly focused femtosecond laser due to the dynamic transformation between self-focusing and self-defocusing is employed to provide a novel method to produce quasi-periodic voids in glass. It is found that the diameter or the interval of the periodic voids increases with the increasing pulse energy of the laser. The detailed course for producing periodic voids is discussed by analysing the damaged track induced by the tightly focused femtosecond laser pulses. It is suggested that this periodic structure has potential applications in fabrication of three-dimensional optical devices.