Photoluminescence characteristics of GaAsSbN/GaAs epilayers lattice-matched to GaAs substrates

The photoluminescence (PL) characteristics of GaAsSbN/GaAs epilayers grown by molecular beam epitaxy (MBE) are carefully investigated. The results show that antimony (Sb) incorporation into GaNAs material has less influence on the N-induced localization states. For the same N concentration, GaAsSbN material can reach an emission wavelength near 1.3 mum more easily than GaInNAs material. The rapid thermal annealing (RTA) experiment shows that the annealing induced rearrangement of atoms and related blueshift in GaAsSbN epilayers are smaller than those in GaNAs and GaInNAs epilayers. The GaAsSbN material can keep a longer emission wavelength near 1.3 mum-emission even after the annealing treatment. Raman spectroscopy analysis gives further insight into the structure stability of GaAsSbN material after annealing. (C) 2004 Elsevier Ltd. All rights reserved.

聚醋酸乙烯酯/聚丙烯酸甲酯互穿聚合物网络的研究

Interpenetrating Polymer Network-IPN是六十年代初开始发展起来的一种新的化学共混方法。对它在基础和应用开发等方面的研究都有着重要的意义。目前，在IPN的研究领域内，还存在着许多没有表征清楚和难以表征的问题。如IPN中互穿缠结的存在及其形态，IPN的微相结构，IPN的结构与性能之间的关系等问题。这固然与IPN体系本身的复杂性和其理论和基础研究不成熟等因素有关，但也是部分地由于没有选择一个较好的IPN体系，能够较系统地对这些问题加以研究。聚醋酸乙烯酯与丙烯酸甲酯的结构单元在化学结构上是同分异构体，因此是一对相容性较好的聚合物。本工作合成了一系列的聚醋酸乙烯酯-聚丙烯酸甲酯LPN，并对这一体系进行了以下几个方面的研究。一、IPN的合成条件对其动态力学性能的影响二、IPN中的网络I和网络II由于互穿缠结而起的强迫互容效应。三、IPN的溶胀行为反其网络间互穿缠结对溶胀行为的影响。四、IPN体系的橡胶态模量反互穿缠结效应对IPN橡胶态模量的影响。用Binder-Frisch模型解释实验结果，并描述互穿缠结链的形态。五、IPN中网络间的互穿缠结效应对其微相结构的稳定作用。我们首次研究了非Millar-IPN的溶胀行为和其橡胶态模量行为。结果表明在IPN中确实存在着网络间的互穿缠结效应，并且证明，对于互穿缠结效应，网络I比网络II起着更为重要的作用。定性地证明Binder-Frisch模型反其互穿缠结熵公式，ΔSent ∝ φ_I~(-2/3)(1-φ_I)~(1/3) N_I~(-1)N_(II)~(-1/2)σ_I~(-2)σ_(II)~(-1)对于IPN体系是合理的。通过改变网络链的运动环境和改变其相容性等实验手段证明IPN中网络的互穿缠结效应对其形态结构有着远程的稳定作用。