Raman scattering characterization of Mn composition and strain in Ga1-xMnxSb/GaSb epitaxial layers

Raman scattering (RS) experiments have been performed for simultaneous determination of Mn composition and strain in Ga1-xMnxSb thin films grown on GaSb substrate by liquid phase epitaxy technique. The Raman spectra obtained from various Ga1-xMnxSb samples show only GaSb-like phonon modes whose frequency positions are found to have Mn compositional dependence. With the combination of epilayer strain model, RS and energy dispersive x-ray (EDX) experiments, the compositional dependence of GaSb-like LO phonon frequency is proposed both in strained and unstrained conditions. The proposed relationships are used to evaluate Mn composition and strain from the Ga1-xMnxSb samples. The results obtained from the RS data are found to be in good agreement with those determined independently by the EDX analysis. Furthermore, the frequency positions of MnSb-like phonon modes are suggested by reduced-mass model. (C) 2008 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim

Raman scattering study on Ga1-xMnxAs prepared by Mn ions implantation, deposition and post-annealing

Raman scattering measurements have been performed in Ga1-xMnxAs crystals prepared by Mn ions implantation, deposition, and post-annealing. The Raman spectrum measured from the implanted surface of the sample shows some weak phonon modes in addition to GaAs-like phonon modes, where the GaAs-like LO and TO phonons are found to be shifted by approximately 4 and 2 cm(-1), respectively, in the lower frequency direction compared to those observed from the unimplanted surface of the sample. The weak vibrational modes observed are assigned to hausmannite Mn3O4 like. The coupled LO-phonon plasmon mode (CLOPM), and defects and As related vibrational modes caused by Mn ions implantation, deposition, and post-annealing are also observed. The compositional dependence of GaAs-like LO phonon frequency is developed for strained and unstrained conditions and then using the observed LOGaAs peak, the Mn composition is evaluated to be 0.034. Furthermore, by analyzing the intensity of CLOPM and unscreened LOGaAs phonon mode, the hole density is evaluated to be 1.84 x 10(18) cm(-3). (C) 2009 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim