结构弛豫对Zr_(64.13)Cu_(15.75)Ni_(10.12)Al_(10)块体非晶合金硬度和剪切带特征的影响

通过接近玻璃转变温度的等温退火获得不同弛豫状态的Zr64.13Cu15.75Ni10.12Al10块体非晶合金样品。利用维氏显微硬度计和洛氏硬度计研究结构弛豫对合金硬度和压痕周围剪切带特征的影响规律。结果表明:在590K等温退火处理使Zr64.13Cu15.75Ni10.12Al10块体非晶合金发生焓弛豫行为,其维氏显微硬度随退火时间的延长较快增加后趋于稳定,而大载荷洛氏硬度对结构弛豫不敏感。通过洛氏压痕周围剪切带特征的研究,定量比较了结构弛豫对剪切带间距、数量的影响规律。

锰含量对LiNi_(0.85-x)Co_(0.15)Mn_xO_2结构及形貌的影响

采用共沉淀法先合成出氢氧化物前驱体Ni0.85-xCo0.15Mnx(OH)2,其中X=0、0.1、0.2和0.4,前驱体与Li2CO3在空气气氛中固相烧结制得正极材料LiNi0.85-xCo0.15MnxO2。用XRD、SEM研究了锰含量对材料结构和形貌的影响。研究发现,LiNi0.85Co0.15O2的X射线衍射图中存在微量第二相,而锰掺杂有利于减小反应过程中锂离子损失和镍离子占据锂位,容易形成有序层状结构材料。随着Mn离子替代Ni离子量的增加,晶胞参数a减小,晶胞参数c、c/a及I003/I104值增大。SEM结果表明前驱体和最终产物形貌均随锰含量增加颗粒均匀性增强,粒子尺寸变小,粒径分布变窄。

力学未来15年国际学术讨论会论文集

Investigation on nonradiative decay of the (Er3+I13/2)-I-4 -> I-4(15/2) transition in different tellurite glass matrix

Three kinds of Er3+-doped tellurite glasses with different hydroxyl groups are prepared by the conventional melt-quenching method. Infrared spectra are measured to estimate the exact content of OH- groups in samples. The maximum phonon energy in glasses are obtained by measuring the Raman scattering spectra. The strength parameters Omega(t) (t = 2, 4, 6) for all the samples are calculated and compared. The nonradiative decay rate of the Er3+ I-4(13/2) -> I-4(15/2) transition are calculated for the glass samples with different phonon energy and OH- group contents. Finally, the effect of OH- groups on fluorescence decay rate of Er3+ is analysed, the constant KOH-Er Of TWN, TZPL and TZL glasses are calculated to be 9.2 x 10(-19) cm(4)s(-1), 5.9 x 10(-19) cm(4)s(-1), and 3.5 x 10(-19) cm(4)s(-1), respectively.

Effect of hydroxyl groups on nonradiative decay of Er3+: I-4(13/2)-> I-4(15/2) transition in zinc tellurite glasses

A series of zinc tellurite glasses of 75TeO(2)-20ZnO-(5-x)La2O3-xEr(2)O(3) (x=0.02, 0.05, and 0.1 mol%) with the different hydroxl groups were prepared by the conventional melt-quenching method. Infrared spectra were measured in order to estimate the exact content of OH- groups in samples. The observed increase of the fluorescence lifetime with the oxygen bubbling time has been related to the reduction in the OH- content concentration as evidenced by IR transmission spectra. Various nonradiative decay rates from I-4(13/2) of Er3+ with. the change of OH content were determined from the fluorescence lifetime and radiative decay rates were calculated on the basis of Judd-Ofelt theory. (c) 2005 Elsevier B.V. All rights reserved.

Comparison of spectroscopic parameters of 15 at% Yb : YAlO3 and 15 at% Yb : Y3Al5O12

Yb: YAlO3 (YAP) (15 at %) and Yb: Y3Al5O12 (YAG)(15 at %) have been grown using the Czochralski method. Their absorption and fluorescence spectra were measured at room temperature and important spectroscopic parameters were calculated. Through the comparison of spectroscopic parameters of Yb:YAP and Yb: YAG, all results indicate that 15 at % Yb:YAP crystal is a potential candidate used for compact, efficient thin chip lasers when the laser output wavelength is 1012 or 103 8 nm. (C) 2004 Elsevier B.V. All rights reserved.

Anti-HIV Actions of 7- and 10-Substituted Camptothecins (vol 15, pg 138, 2010)

The authors thank the anonymous reviewer for helpful comments on the early version of the manuscript. This work was financially supported by the earmarked fund for Modern Agro-industry Technology Research System, the Science Fund for Young Scholars in Sichuan Province (Grant No: ZQ 026-017), and the National 863 Project of China (No. 2008AA101001).