The FeCl3-doped poly(3-alkyithiophenes) in solid state

The FeCl3-doped three poly(3-alkylthiophenes) (P3ATs) in solid state, i.e. poly( 3-octylthiophenl) (P3OT), poly(3-dodecylthiophene) (P3ODT) and poly( 3-octadecylthiophene) (P3ODT), were investigated in this paper. In X-ray diffraction results, there are obvious variations of the interlayer and interlayer spacings in the layered structures of P3ATs. In addition, it is found that some orientations of the side-chain groups occur after the doping process. The infrared spectra have also shown the microstructural changes arising from the readjustments of the polymer chains due to the intervention of the dopant. The presence of dopant leads to the formation of bipolarons and polarons at the same time. The conductivity measurements reveal that the conductivity decreases with the increase of the length of sidechain group. We have also observed the relaxation behaviors in the conductivities of the doped polymers. (C) 2001 Elsevier Science B.V. All rights reserved.

The effects of different alkyl substitution on the structures and properties of poly(3-alkylthiophenes)

In order to investigate the influence of different alkyl side chain substitution on the structures and properties of P3ATs, X-ray diffraction, differential scanning calorimetry (DSC), thermal gravity analysis (TGA), Fourier transform infrared spectra (FTIR) and ultraviolet-visible spectra (W-VIS) were applied to characterizing the samples of ploy(3-octylthiophene) (P3OT), poly(3-dodecylthiophene) (P3DDT) and poly(3-octadecylthiophene) (P3ODT). It is found that the different length of alkyl group substitution leads to great difference in molecular chain packings, according to the room temperature X-ray diffraction results. The temperature dependence of X-ray diffraction experiments were also performed to study the melting processes of P3ATs. With the increase in the number of carbon atoms in alkyl side chains, the melting point decreases, and the thermal stability decreases too. The results of both FTIR and W-VIS spectra indicate that the conjugation length of P3DDT is the longest. among the three P3ATs. (C) 2001 Elsevier Science B.V. All rights reserved.

Non-isothermal crystallization kinetics of the poly(3-alkylthiophenes)

According to the data obtained from Differential Scanning Calorimetry (DSC),the method of Jeziorny, BOPOXOBCKHH and a new approach proposed by our laboratry are applied to study the nonisothermal crystallization behavior of poly( 3-dodecylthiophene) (P3DDT) and poly(3-octadecylthiophene) (P3ODT),and Kissinger method is used to get the value of the crystallization activation energy. The effect of the different alkyl substitution on crystallization is also investigated. In comparison to the methods of Jeziorny and BOPOXOBCKHH in which it can be found that the deviation from the line occurs in the later stage of crystallization, the new approach appears applicable due to the better linear relation. The values of the crystallization activation energy of P3DDT and P3ODT are estimated as 184.78kJ/mol and 246.93kJ/mol, respectivley, which implies that it is easiser to crystallize P3DDT than P3ODT.

Characterization and properties of the neutral and doped blends of poly(3-dodecylthiophene) with low-density polyethylene

In this paper, the structures and properties of the neutral and doped blends of poly(3-dodecylthiophene) (P3DDT) with low-density polyethylene (LDPE) were investigated. Wide-angle X-ray diffraction (WAXD), differential scanning calorimetry (DSC), Fourier transform infrared spectra (FTIR), and scanning electron microscopy (SEM) were used to characterize the structures and morphologies of the blends, and conductivity was also measured. It was found that separate crystallizations occur between P3DDT and LDPE. When the amount of P3DDT is small in the blend, it has the effect of a nucleation reagent and has some influence on the crystal structure. After doping, the interaction force between the molecular chains increases, and leads to a more compact packing and a more uniform dispersion in morphology. Through blending, the thermal stability of pure component could be greatly improved, especially when the P3DDT content is 5 wt %. The conductivity measurements indicate that the conductivity increases with the increase of the P3DDT composition and doping time.

MAGNETIC-RESONANCE EXPERIMENTS ON UNDOPED AND DOPED POLY(PARA-PHENYLENE)

We investigated the electron paramagnetic resonance (EPR) spectra of undoped, FeCl3- and iodine-doped poly(para-phenylene) (PPP) prepared by the method of Kovacic. EPR measurements are used to characterize electronic states relevant for carrier transport in doped PPP. We found a novel dependence of room temperature linewidth (DELTAH(pp)) and spin density (N(spin)) on the dopant concentrations for iodine-doped PPP, namely, DELTAH(pp) first decreased and increased, and then decreased and increased again with increasing iodine concentration in the iodine-doped PPP. The corresponding value of N(spin) first increased and decreased, and then increased and decreased again with increasing iodine concentration in PPP. However, the changes in DELTAH(pp) and N(spin) with FeCl3 concentration in FeCl3-doped PPP differ from those of iodine-doped PPP. We explain the different EPR properties in FeCl3-doped and iodine-doped PPP.

Morphology and crystalline transition of poly (3-butylthiophene) associated with its polymorphic modifications

Poly (3-butylthiophene) (P3BT) is a much less studied conjugated polymer despite its high crystallizability and thus excellent electrical property. In this work, morphology of P3BT at different crystalline polymorphs and solvent/thermal induced phase transition between form I and U modifications have been intensively investigated by using optical microscopy, electron microscopy, differential scanning calorimetry, and X-ray diffraction. It is shown that a direct deposition from carbon disulfide (CS2) at fast evaporation results in P3BT crystals in form I modification, giving typical whiskerlike morphology. In contrast, low evaporation rate from CS, leads to formation of form II crystals with spherulitic morphology, which is so far scarcely observed in polythiophene.

Effects of fullerene solubility on the crystallization of poly(3-hexylthiophene) and performance of photovoltaic devices

The substantial crystallization suppression of poly(3-hexylthiophene) (P3HT) in the untreated P3HT:C60 composite film prepared from o-dichlorobenzene (ODCB) solution has been revealed. Besides, the effective conjugation length of P3HT in this composite has been nearly maintained to that in the solution. The different crystallization behaviors of P3HT in its composites with C60 and [6,6]-phenyl C-61 butyric acid methyl ester (PCBM) are mainly attributed to the relative solubility of C60 and PCBM with respect to P3HT in ODCB. The solution to overcome this disadvantage of chain conformation and crystallinity of P3HT in the composite with C60 is thus proposed and finalized by resorting to the addition of low volatile solvent with much higher solubility of C60 than P3HT into the main solvent used, so as P3HT can crystallize before C60 forms crystallites in the solution. The feasibility of this approach has been proven by the improved efficiency of devices based on composites of P3HT and the low cost C60 without resorting to post-treatments.

Morphology of head-to-tail poly(3-hexylthiophene) single crystals from solution crystallization

Single crystals of head-to-tail poly(3-hexylthiophene)s have been grown through the method of isothermal solution crystallization. Electron diffraction in combination with powder X-ray diffraction revealed the crystal structure, a = 1.52 nm, b = 3.36 nm, c = 1.56 nm and alpha = beta = gamma = 90 degrees.

Extended-chain lamellar packing of poly(3-butylthiophene) in single crystals

We developed an approach, i.e. solvent-assist crystallization (SAC), for growing high quality single crystals of head-to-tail regio-regular poly(3-butylthiophene) (P3BT). By means of atomic force microscopy, electron diffraction and X-ray diffraction, we found that P3BT macromolecules formed lamella single crystals through gradient crystallization, and in the single crystals, molecules packed normal to the lamella with extended-chain conformation with alkyl side chains in the growth front during crystallization.

Morphology of electrodeposited poly(3,4-ethylenedioxythiophene)/poly(4-styrene sulfonate) films

Poly(4-styrene sulfonate)-doped poly(3,4-ethylenedioxythiophene) (PEDOT/PSS) films with ring-, arrow-, and bubble-like microstructures have been electrochemically generated simply by a one-step cyclic voltammetry in an aqueous media. Influences of applied potentials and surfactant/dopant-PSS on morphology of the resulting film were investigated, and a gas bubble template mechanism has been proposed. The result confirmed a well-doping of PSS in the PEDOT film. Electrochemical property and conductivity of the micro-structured PEDOT/PSS film were investigated further. Similar preparation with potential applications in fabrication of microdevices and micro-sensors can be extended to other micro-structured conducting polymers.

External field induced crystallization of poly(3-dodecylthiophene)

In order to investigate the effect of external field on the crystallization behavior of poly(3-dodecylthiopliene) (P3DDT), the samples were recrystallized with different electrostatic field intensity, different pressure and different solidification direction in temperature gradient field. Measurements of differential scanning calorimetry and X-ray diffraction were operated to characterize these samples for analysis. The results suggest that after recrystallization, whether the external field is added or not, a more compact packing of molecular chains in P3DDT could be obtained without the change of the crystal structure model. Moreover, the addition of electrostatic field has greater effects on the crystallization of rigid main chains than on that of flexible side chains, Merely great pressure field can effect the rearrangements of molecular chains greatly. As for the temperature gradient field induced crystallization, different oriented solidification direction will lead to different effects on the compact degree and perfect degree of molecular chains packing,

Poly(3-dodecylthiophenes) polymerized with different amounts of catalyst

The effect of the amount of the catalyst FeCl3, used during the direct oxidation polymerization, on the structure and properties of the obtained poly(3-dodecylthiophene) (P3DDT) was investigated in this paper. Such measurements as gel permeation chromatography (GPC), nuclear magnetic resonance (NMR) spectroscopy, thermal analysis, X-ray diffraction, infrared spectroscopy (FTIR) and ultraviolet-visible (W-vis) spectroscopy were applied. It is found that a suitable addition of FeCl3 can contribute to generate a P3DDT with greater percentage of head-to-tail head-to-tail (HT-HT) linkages, which are generally favored. The reduction of the other linkage defects helps to lengthen conjugation length, thus leading to more orderly chain packing. (C) 2000 Elsevier Science S.A. All rights reserved.

Carrier transport assisted by dopants in doped poly(N-vinylcarbozole) light-emitting diodes

We have investigated the transient electroluminescence (EL) onset of the double-layer light-emitting devices made from poly(N-vinylcarbozole) (PVK) doped with 4-(dicyanomethylene)-2-t-butyl-6(1,1,7,7-tetramethyljulolidyl-9-enyl)-4H-pyran (DCJTB) and tris(8-hydroxy-quinoline) aluminium (Alq(3)). For the double-layered device in which PVK was doped with 0.1 wt% DCJTB, the EL onset of PVK lags that of DCJTB and Alq(3), while the EL onset of DCJTB and Alq(3) is simultaneous. However, the EL emission of the double-layered device of PVK/Alq(3) originates only from Alq(3). The results show that DCJTB dopants can not only help to tunnel electrons from Alq(3) zone to PVK but can also assist electrons transfer in PVK under high electric field by hopping between DCJTB molecules or from DCJTB to PVK sites at a low doping concentration of 0.1 wt%. When the DCJTB doping concentration is 4.0 wt%, the EL onset of Alq(3) lags that of DCJTB. The difference in the EL onsets of DCJTB, Alq(3) and PVK is attributed to the slow build-up of the internal space charge in the vicinity of the interface between PVK and Alq(3). The electron potential difference of the interface between Alq(3) and PVK doped by DCJTB can be adjusted by changing the DCJTB doping concentration in double-layer devices.

Near-infrared polymer light-emitting diodes based on infrared dye doped poly(N-vinylcarbazole) film

Infrared light-emitting diodes possess potential applications in optical communication and safety detection. in this paper, we fabricated near-infrared light-emitting diodes possess potential applications in optical communication and safety detection. in this paper, we fabricated near-infrared polymer light-emitting diode employing a commercial near-infrared (NIR) organic dye as an emissive dopant dispersed within poly(N-vinylcarbazole) (PVK) by spin-casting method. The used device structure was indium tin oxide/3,4-polyethylene-dioxythiophene-polystyrene sulfonate/PVK: NIR dye/Al.