PP/EVA共混体系敏化辐射交联的研究

研究了在多官能团单体-三烯丙基异氰酸酯(TAIC)存在下,聚丙烯(PP)/乙烯-醋酸乙烯酯(EVA)共混体系的辐射交联、并应用凝胶量、力学性能等数据对其进行表征。结果表明,TAIC对PP/EVA共混体系的辐射交联的敏化作用显著,EVA对体系凝胶生成有正的协同作用,改善了TAIC在共混体系中的分布。敏化交联还改善了PP/EVA共混体系的相容性,增强了相间粘附,提高了其力学性能。

PEO／EVA共混物的结构研究

ＰＥＯ以分散相形式存在于ＰＥＯ／ＥＶＡ共混物中，且具有部分相容性。Ｘ－射线衍射谱表明ＥＶＡ含有较强的ＰＥ衍射峰；ＰＥＯ／ＥＶＡ共混物既表现出ＰＥ的衍射峰也含有ＰＥＯ的晶面反射。随着ＰＥＯ的Ｍｎ的增加，ＰＥＯ／ＥＶＡ的Ｗｃ、ｘ增大且于时获得最大值：ＰＥ０／ＥＶＡ的Ｗｃ、ｘ值比纯ＰＥＯ的Ｗｃ、ｘ明显降低。

PET／EVA共混体系的流变行为和形态

用恒负荷式毛细管流变仪研究了ＰＥＴ／ＥＶＡ共混物的流变行为，讨论了ＥＶＡ对ＰＥＴ流变行为的影响；并用ＳＥＭ观察了挤出条横截面的形态。结果表明，在一定范围内，加入ＥＶＡ能够提高ＰＥＴ的表观粘度，改善其加工性能；电镜结果表明ＰＥＴ和ＥＶＡ明显分相；动态力学结果证明ＰＥＴ和ＥＶＡ不相容。

RADIATION GRAFT COPOLYMER OF ACRYLIC-ACID ONTO EVA

The structure of the radiation graft copolymer of acrylic acid onto EVA has been studied by infrared spectroscopy and XPS. It was found that along with the main peak C there is a photoelectron peak at 288.5 eV attributed to [GRAPHICS] group in XPS spectra and the content of its area in XPS increases with increasing of grafting degree of EVA. It was also found that hydrophilicity of EVA increases with the increase of grafting degree.

PET-EVA共混体系的结晶与熔融行为

用热分析法测定了PET-EVA共混物在不同条件下的结晶与熔融行为.结果表明,加入EVA使PET结晶温度降低,结晶温度区间变窄,结晶度有一定提高,在EVA含量10％附近出现极值.总体上讲,EVA对PET的熔融行为没有影响.

CPE/EVA共混物的辐射交联规律的研究

本文研究了CPE/EVA共混体系的辐射交联规律,证实了该共混体系对文献[4]的适应性,发现在CPE/EVA共混体系中,随辐射剂量的增加,CPE的结晶度和熔点逐渐消失。

HDPE/EVA共混体系的研究

采用DSC、WAXD和力学性能测试,研究了HDPE/EVA共混体系。结果表明,HDPE/EVA共混体系是不相容的,但在共混组成中含有少量(<10％)的EVA,力学性能下降很少,而加工性能得到改善,具有一定实用价值。

LDPE/EVA共混体系的结晶行为

本文通过DSC、WAXD、偏光显微镜、DMA等方法,对LDPE/EVA共混体系进行了研究。结果表明,EVA可使LDPE的熔融峰温提高15℃。并在LDPE结晶过程中起稀释剂作用。LDPE/EVA共混体系为非晶相相容。

LLDPE/EVA和LLDPE/EPDM共混体系的辐射凝胶生成动力学研究

研究了辐照线性低密度聚乙烯/乙烯-醋酸乙烯酯共聚物(LLDPE/EVA)共混体系和线性低密度聚乙烯/三元乙丙橡胶(LLDPE/EPDM)共混体系的溶胶分数(S)与辐照剂量(R)间的关系,发现适用于某些纯聚合物辐射交联规律的Charlesby-Pinner关系式和陈-刘-唐关系式不适用于共混体系。建立了LLDPE/EVA和LLDPE/EPDM共混体系的S与R间的关系:R(S+S~(1/2))=1/q_0u_1+α_0R~(βb)/q_0及β_b=∑PW_iβ_1,用此式计算出的结果与实验结果较吻合。

辐射交联LDPE/EVA导电性复合材料物理性能的研究

本文对添加导电填料的辐射交联LDPE/EVA共混多相体系的某些物理性能进行了研究。考察了导电填料含量和聚合物组份对共混体系的电学和力学性能的影响。同时进行了辐射交联LDPE/EVA导电性多相体系的力学性能温度谱,热分析和X射线衍射分析的研究。