Effects of techniques of implanting nitrogen into buried oxide on the characteristics of partially depleted SOIPMOSFET

Effects of techniques of implanting nitrogen into buried oxide on the characteristics of the partially depleted silicon-on-insulator (SOI) p-channel metal-oxide-semiconductor field-effect transistors (PMOSFETs) have been studied with three different nitrogen implantation doses, 8 x 10(15), 2 x 10(16), and 1 x 10(17) cm(-2). The experimental results show that this technology can affect the threshold voltage, channel hole mobility and output characteristics of the partially depleted SOI PMOSFETs fabricated with the given material and process. For each type of the partially depleted SOI PMOSFET with nitrided buried oxide, the absolute value of the average threshold voltage increases due to the nitrogen implantation. At the same time, the average channel hole mobility decreases because of the nitrogen implantation. In particular, with the high nitrogen implantation doses, the output characteristic curves of the tested transistors present a distinct kink effect, which normally exists in the characteristic output curves of only partially depleted SOI NMOSFETs.

Effects of the technology of implanting nitrogen into buried oxide layer on the characteristics of partially depleted SOI nMOSFET

The effects, caused by the process of the implantation of nitrogen in the buried oxide layer of SIMOX wafer, on the characteristics of partially depleted silicon-on-insulator nMOSFET have been studied. The experimental results show that the channel electron mobilities of the devices fabricated on the SIMON (separation by implanted oxygen and nitrogen) wafers are lower than those of the devices made on the SIMOX (separation by implanted oxygen) wafers. The devices corresponding to the lowest implantation dose have the lowest mobility within the range of the implantation dose given in this paper. The value of the channel electron mobility rises slightly and tends to a limit when the implantation dose becomes greater. This is explained in terms of the rough Si/SiO2 interface due to the process of implantation of nitrogen. The increasing negative shifts of the threshold voltages for the devices fabricated on the SIMON wafers are also observed with the increase of implanting dose of nitrogen. However, for the devices fabricated on the SIMON wafers with the lowest dose of implanted nitrogen in this paper, their threshold voltages are slightly larger on the average than those prepared on the SIMOX wafers. The shifts are considered to be due to the increment of the fixed oxide charge in SiO2 layer and the change of the density of the interface-trapped charge with the value and distribution included. In particular, the devices fabricated on the SIMON wafers show a weakened kink effect, compared to the ones made on the SIMOX wafers.