用电子束加热沉积法（EBD）制备了厚度420um的ZnIn2ZTe4薄膜。研究了最佳成膜工艺条件和性能，用电子能谱（XPS）分析了ZuIn2Te4薄膜的组成、结构和状态；典型ZnIn2Te4膜最佳参数为：电阻率ρ为3．2×10－1Ω·cm，Hall迁移率是79cm2V－1s－1，载流子浓度是1．58×1017cm－3，禁带宽度（Eg）是2．33eV；探讨了ZuIn2Te4膜导电机理，制作了ZuIn2Te4－Si太阳能电池。

Influence of oxygen post-treatment on laser-induced damage of antireflection coatings prepared by electron-beam evaporation and ion beam assisted deposition

Antireflection coatings at the center wavelength of 1053 nm were prepared on BK7 glasses by electron-beam evaporation deposition (EBD) and ion beam assisted deposition (IBAD). Parts of the two kinds of samples were post-treated with oxygen plasma at the environment temperature after deposition. Absorption at 1064 nm was characterized based on surface thermal lensing (STL) technique. The laser-induced damage threshold (LIDT) was measured by a 1064-nm Nd:YAG laser with a pulse width of 38 ps. Leica-DMRXE Microscope was applied to gain damage morphologies of samples. The results revealed that oxygen post-treatment could lower the absorption and increase the damage thresholds for both kinds of as-grown samples. However, the improving effects are not the same. (c) 2008 Elsevier B.V. All rights reserved.