Microwave-assisted hydrothermal synthesis of hydroxy-sodalite zeolite membrane

A high quality pure hydroxy-sodalite zeolite membrane was successfully synthesized on an alpha-Al2O3 support by a novel microwave-assisted hydrothermal synthesis (MARS) method. Influence of synthesis conditions, such as synthesis time, synthesis procedure, etc., on the formation of hydroxy-sodalite zeolite membrane by MAHS method was studied by X-ray diffraction (XRD), scanning electron microscopy (SEM) and gas permeation measurements. The synthesis of hydroxy-sodalite zeolite membrane by MAHS method only needed 45 min and synthesis was more than 8 times faster than by the conventional hydrothermal synthesis (CHS) method. A pure hydroxy-sodalite zeolite membrane was easily synthesized by MAHS method, while a zeolite membrane, which consisted of NaX zeolite, NaA zeolite and hydroxy-sodalite zeolite, was usually synthesized by CHS method. The effect of preparation procedures had a dramatic impact on the formation of hydroxy-sodalite zeolite membrane and a single-stage synthesis procedure produced a pure hydroxy-sodalite zeolite membrane. The pure hydroxy-sodalite zeolite membrane synthesized by MARS method was found to be well inter-grown and the thickness of the membrane was 6-7 mum. Gas permeation results showed that the hydrogen/n-butane permselectivity of the hydroxy-sodalite zeolite membrane was larger than 1000. (C) 2004 Elsevier Inc. All rights reserved.

Growing process of CdS nanoclusters in zeolite Y studied by positron annihilation

Zeolite Y has been used as the host to generate CdS nanoclusters. The location of CdS nanoclusters inside zeolite hosts was confirmed by the blue-shifted reflection absorption spectra with respect to that of bulk CdS materials. But which kind of cage inside zeolite Y, sodalite cage or supercage, was preferred for the CdS clusters remained unclear. In this paper, we conducted positron annihilation spectroscopy (PAS) measurements for the first time on a series of CdS/Y zeolite samples and concluded that CdS clusters were not located in supercages but in smaller sodalite cages. The stability of CdS clusters inside the sodalite units was due to the coordination of Cd atoms with the framework oxygen atoms of the double six-ring windows. Moreover, PAS revealed some important information of surface states existing on the interfacial layers between CdS clusters and zeolite Y. (C) 2001 Elsevier Science B,V, All rights reserved.

On configuration of exchanged La3+ on ZSM-5: A theoretical approach to the improvement in hydrothermal stability of La-modified ZSM-5 zeolite

Density functional calculations have been employed to investigate the locating and binding of lanthanum cation, i.e., La(OH)(2)(+), on HZSM-5 zeolite. Through geometry optimization, it was determined that lanthanum ions are favorably accommodated in the two 6-T rings of the straight channels (Clusters 1 and 2, see Sec. III A for details). Cluster 1 was found to exist in prior to Cluster 2 due to the preference of Al substitution in the T11 site (Cluster 1) rather than in the T8 site (Cluster 2). Geometry-optimization of Cluster 1 containing another two lanthanide ions Nd3+ and Yb3+ was also carried out and it was found that a monotonic decrease in Ln-O bond length will take place as the atomic number increases, conforming well to the rule of lanthanide contraction. Some of the optimized parameters are comparable to the corresponding experimental values in Y zeolite, which confirms that the optimized configurations are acceptable. The average frequencies of hydroxyls attached to La3+ or Yb3+ in Cluster 1 fall at 3609.16 and 3579.76 cm(-1), respectively, with the gap of these two frequencies close to that in the sodalite cage of Y zeolite. Compared to H-form zeolite, the charges on both Al and O atoms in Ln-ZSM-5 zeolite show an obvious increase, which will undoubtedly lead to a stronger mutual interaction and hence enhance the stability of the [AlO4](-) anion. Moreover, the Ln(OH)(2)(+) seem to have thickened the zeolite framework, which can effectively retard the process of dealumination. Through the evaluation of the possibility for dimer formation, it turned out that when the exchange degree arrived to approximately 0.28, lanthanum monomers began to aggregate into dimers, and were completely converted into dimers when the exchange degree approached 0.60. (C) 2003 American Institute of Physics.

Photostimulated luminescence of AgI clusters in zeolite-Y

AgI clusters in zeolite-Y (AgI/Y) were prepared by Ag+ exchange followed by reaction with NaI in solution. The formation of the clusters was determined by transmission electron microscopy and Auger electron spectroscopy. The clusters were uniform and even in size, 1.0-2.0 nm. The fluorescence spectrum of the clusters consists of two emission bands, which are attributed to AgI and Ag clusters, respectively. Photostimulated luminescence (PSL) is observed by stimulation at 675 or at 840 nm. The PSL spectrum of AgI/Y is consistent with the emission spectrum of Ag clusters and thus the PSL is considered to be caused by the charge transfer or carrier migration from the zeolite framework or from the AgI clusters to the Ag clusters. The appearance of PSL indicates that these materials may find application as a medium for erasable optical memory. (C) 1998 American Institute of Physics. [S0021-8979(98)02407-4].

Formation, structure and fluorescence of CdS clusters in a mesoporous zeolite

CdS clusters are formed in the pores of a mesoporous zeolite in which the size of the clusters may be adjusted. The size of the clusters increases as the CdS loading is increased. X-ray diffraction investigation shows that the lattice constants of the clusters contract upon increasing size. This contraction is attributed to an increase of the static pressure exercised by the zeolite framework as the clusters grow bigger. Both the excitonic and trapped emission bands are detected and become more intensive upon decreasing size. Three absorption bands appear in the photoluminescence excitation (PLE) spectra and they shift to the blue as cluster size decreases. Based on the effective-mass approximation, the three bands are assigned to the 1S-1S, 1S-1P and 1S-1D transitions, respectively. The size-dependence of the PLE spectra can also be explained. (C) 1997 Elsevier Science Ltd.

Influence of A-type Zeolite on Methane Hydrate Formation

The porous medium has an important effect on hydrate formation. In this paper, the formation process and the gas storage capacity of the methane hydrate were investigated with A-type zeolite and Sodium Dodecyl Sulfate (SDS) existing in the system. The results show that A-type zeolite can influence methane hydrate formation. At the temperature of 273.5 K and pressure of 8.3 MPa, the distilled water with A-type zeolite can form methane hydrate with gaseous methane in 12 hours. The formation process of the system with A-type zeolite was quite steady and the amount of A-type zeolite can influence the gas storage capacity significantly. The adding of A-type zeolite with 0.067 g.(g water)(-1) into 2 x 10(-3) g.g(-1) SDS-water solution can increase the gas storage capacity, and the maximum increase rate was 31%. Simultaneously the promotion effect on hydrate formation of 3A-type zeolite is much more obvious than that of 5A-type zeolite when the water adding amounts are 0.033 g.g(-1) and 0.067 g.g(-1) at the experimental conditions.

The fabrication of TiO2-supported zeolite with core/shell heterostructure for ethanol dehydration to ethylene

The TiO2-supported zeolite with core/shell heterostructure was fabricated by coating aluminosilicate zeolite (ASZ) on the TiO2 inoculating seed via in situ hydrothermal synthesis. The catalysts were characterized by transmission electron microscope (TEM), X-ray diffraction (XRD), nitrogen physisorption (BET), and Fourier transform infrared spectroscopy (FT-IR). The surface acidity of the catalysts was measured by pyridine-TPD method. The catalytic performance of the catalysts for ethanol dehydration to ethylene was also investigated. The results show that the TiO2-supported zeolite composite catalyst with core/shell heterostructure exhibits prominent conversion efficiency for ethanol dehydration to ethylene.

Catalytic Dehydration of Ethanol to Ethylene on TiO2/4A Zeolite Composite Catalysts

TiO2/4A zeolite composite catalysts were prepared by coating TiO2 on 4A zeolite via liquid phase deposition. The TiO 2/4A zeolite composite catalysts wtih higher surface weak acidity and lower mediate strong acidity exhibit much better catalytic performance on ethanol dehydration to ethylene compared with 4A zeolite. It is suggested that the TiO2 promoter could improve the effective Lewis acidity of composite catalyst which consequently enhanced the catalytic performance.

Influence of 5A-Type Zeolite Powder on Tetrahydrofuran Hydrate Formation and Dissociation Process

Visual observations of tetrahydrofuran (THF) hydrate formation and dissociation processes with 5A-type zeolite powder were made at normal atmospheric conditions and below zero temperature by microscope. Results indicate that 5A-type zeolite powder can promote THF hydrate growth. At the same time, in the presence of 5A-type zeolite, agglomerated crystals and vein-like crystals of THF hydrate were also formed. SA-type zeolite powder increases the crystallization temperature and decreases the dissociation temperature. The particle size distribution of 5A-type zeolite powder influences THF hydrate formation and its dissociation characteristics significantly.

Photoluminescence of ZnS clusters in zeolite-Y

Two obvious emissions are observed from the ZnS clusters encapsulated in zeolite-Y. The emission around 355 nm is sharp and weak, locating at the onset of the absorption edge. The band around 535 nm is broad, strong and Stokes-shifted. Both the two emissions shift to blue and their intensities firstly increase then decrease as the loading of ZnS in zeolite-Y or clusters size decreases. Through investigation, the former is attributed to the excitonic fluorescence, and the latter to the trapped luminescence from surface states. The cluster size-dependence of the luminescence may be explained qualitatively by considering both the carrier recombination and the nonradiative recombination rates. Four peaks appearing in the excitation spectra are assigned to the transitions of 1S-1S, 1S-1P, 1S-1D and surface state, respectively. The excitation spectra of the clusters do not coincide with their absorption spectra. The states splitted by quantum-size confinement are detected in the excitation spectra, but could not be differentiated in the optical absorption spectra due to inhomogeneous broadening. The size-dependence of the excitation spectra is similar to that of the absorption spectra. Both the excitation spectra of excitonic and of trapped emissions are similar, but change in relative intensity and shift in position are observed.

Photostimulated luminescence of silver clusters in zeolite-Y

Upon UV-irradiation at 254 nm, the photoluminescence of silver atoms in zeolite-Y decreases, meanwhile an absorption band shows up around 840 nm. By photostimulation at 840 nm, fluorescence of silver atoms is detected, which is called photostimulated luminescence, and the photoluminescence of silver atoms is increased slightly. These phenomena are attributed to the charge-transfer interaction between the zeolite framework and the entrapped silver atoms. (C) 1997 Published by Elsevier Science B.V.

Absorption spectra of Se-8-ring clusters in zeolite 5A

Samples with different weight ratio of Se to zeolite 5A (Se concentration) have been prepared by loading Se into the pores of zeolite 5A, and the measuerments of the absorption and Raman spectra have been carried out for the prepared samples. The measured absorption edges of the samples are close to the value for monoclinic Se containing Se-8-ring, suggesting the formation of Se-8-ring clusters(1) in the pores. The continuous and broadening features of the absorption spectra are interpreted by the strong electron-nucleus coupling in the Se-8-ring cluster. The absorption edges are red shifted with the increase of the Se concentration. It is tentatively attributed to two reasons. One is the existence of the double Se-8-ring cluster in the high Se concentration samples, and the other is that for the strong electron-nucleus coupling cluster, the absorption edge of the clusters system will be red shifted with the increase of the cluster concentration in the clusters system. A single broad band at about 262 cm(-1) is observed in the Raman spectra, which further supports the formation of Se-8-ring clusters. (C) 1997 Published by Elsevier Science S.A.

Thermoluminescence of CdS clusters in zeolite-Y

Thermoluminescence (TL) of CdS clusters encapsulated in zeolite-Y is reported for the first time. The TL of the clusters is much stronger than that of the bulk CdS and increases as the CdS loading decreases. This inverse dependence of TL intensity upon CdS loading is caused mainly by the size-effect of the clusters. All samples exhibit almost the same glow peak position and shape, indicating that traps or surface states are not sensitive to the cluster sizes.

New observation on the luminescence of CdS clusters in zeolite-Y

The excitation spectrum of CdS dusters in zeolite-Y is consistent with their absorption spectrum, both showing two absorption bands that are assigned to the Is-is and Is-lp transitions, respectively. A new emission at 400 nn is considered to be the recombination of the bounded excitons. The emission firstly increases then decreases with increasing cluster size or loading. The emission by excitation into the Is-is band is stronger and sharper than that by excitation into the Is-lp band. This phenomenon is attributed to the size inhomogeneity and the strong electron-phonon interaction of the dusters. Copyright (C) 1996 Elsevier Science Ltd

Absorption and Raman spectra of Se-8-ring clusters in zeolite 5A

Samples with different weight ratio of Se to zeolite 5A (Se composition) have been prepared by loading Se into the cages of zeolite 5A and the measurements of the absorption and Raman spectra have been carried out for the prepared samples. The measured absorption edges of the samples close and blue shifted to the value for monoclinic Se containing Se-8-ring, suggesting the formation of Se-8-ring clusters dagger in the cages. The continuous and broadening features of the absorption spectra are interpreted by the strong electron-phonon coupling in Se-8-ring clusters. The sample with high Se composition has a red shift of the absorption band edge relative to the samples with less Se composition. It is tentatively attributed to the reason that with different Se composition, single Se-8-ring clusters and double Se-8-ring clusters are formed in the cages of zeolite 5A. A single broad band at about 262 cm(-1) is observed in the Raman spectra, that gives the further support of the formation of Se-8-ring clusters. Copyright (C) 1996 Elsevier Science Ltd