Effect of Nb Content on the Microstructure and Mechanical Properties of Zr-Cu-Ni-Al-Nb Glass Forming Alloys

(Zr65Al10Ni10Cu15)(100-x) Nb-x glass forming alloys with Nb contents ranging from 0 to 15 at.% were prepared by water-cooled copper mould cast. The alloys with different Nb contents exhibited different microstructures and mechanical properties. Unlike the monolithic Zr65Al10Ni10Cu15 bulk metallic glass, only a few primary bee beta-Ti phase dendrites were found to distribute in the glassy matrix of the alloys with x = 5. For alloys with x = 10, more beta-phase dendrites forms, together with quasicrystalline particles densely distributed in the matrix of the alloys. For alloys with x = 15, the microstructure of the alloy is dominated by a high density of fully developed P-phase dendrites and the volume fraction of quasicrystalline particles significantly decreases. Room temperature compression tests showed that the alloys with x = 5 failed at 1793 MPa and exhibited an obvious plastic strain of 3.05%, while the other samples all failed in a brittle manner. The ultimate fracture strengths are 1793, 1975 and 1572 MPa for the alloys with x = 0, 10 and 15 at.% Nb, respectively.

Metallographic Analysis of Cu-Zr-Al Bulk Amorphous Alloys with Yttrium Addition

Minor yttrium addition can improve the glass-forming ability of Cu-Zr-Al ternary alloys via suppression of the growth of eutectic clusters. Yttrium addition also makes the room temperature ductility of the alloys decrease, and both the compressive strength and elastic strain limits increase slightly.

The microstructures and mechanical properties of cast Mg-Zn-Al-RE alloys

The microstructures and mechanical properties of cast Mg-Zn-Al-RE alloys with 4 wt.% RE and variable Zn and At contents were investigated. The results show that the alloys mainly consist of alpha-Mg, Al2REZn2, Al4RE and tau-Mg-32(Al,Zn)(49) phases. and a little amount of the beta-Mg17Al12 phase will also be formed with certain Zn and At contents. When increasing the Zn or At content, the distribution of the Al2REZn2 and Al4RE phases will be changed from cluster to dispersed, and the content of tau-Mg-32(Al,Zn)(49) phase increased gradually. The distribution of the Al2REZn2 and Al4RE phases, and the content of beta- or tau-phase are critical to the mechanical properties of Mg-Zn-Al-RE alloys.

Atomistic investigation of the effects of temperature and surface roughness on diffusion bonding between Cu and Al

Molecular dynamics (MD) simulations are carried out to analyze the diffusion bonding at Cu/Al interfaces. The results indicate that the thickness of the interfacial layer is temperature-dependent, with higher temperatures yielding larger thicknesses. At temperatures below 750 K, the interface thickness is found to increase in a stepwise manner as a function of time. At temperatures above 750 K, the thickness increases rapidly and smoothly. When surface roughness is present, the bonding process consists of three stages. In the first stage, surfaces deform under stress, resulting in increased contact areas. The second stage involves significant plastic deformation at the interface as temperature increases, resulting in the disappearance of interstices and full contact of the surface pair. The last stage entails the diffusion of atoms under constant temperature. The bonded specimens show tensile strengths reaching 88% of the ideal Cu/Al contact strength. (c) 2007 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

富钇稀土-铝合金制取的研究Study on Preparation of Yttrium-Rich RE-Al Alloys

我国江西龙南稀土矿是目前世界上储量最大的富钇稀土矿、研制具有多种用途的钇（Y）-铝（Al）或富钇混合稀土（Ymm）-铝中间合金，对于开拓我国龙南稀土矿的应用领域扩大稀土合金出口具有重要意义。基于这一背景并针对目前氟化物体系制取Ymm-Al合金时存在着电解温度高，腐蚀现象严重，电效偏低等缺点，本文系统开展了在氯化物熔盐体系中电解制取Ymm-Al合金的研究工作。本工作由三部分组成：在第一部分工作中，开展了熔盐电解所需要基本原料-无水稀土氯化物制取的工艺研究。利用化学分析和结构分析手段，弄清了干法氯化过程中YmmCl_3水解的机理，提出了减弱水解的措施，即YmmCl_3先在850-900 ℃灼烧1.5 + 0.2hr，脱掉吸附水并将碱式碳酸盐转化为氧化物，增加稀土氧化物的比表面。通过条件试验得到最佳工艺条件为：采用NH_4 Cl:Ymm_2 O_3 = 14:1（摩尔比）的配料比，每次投入氯化装置的原料量为0.26 - 0.36 kg, 在400-450 ℃氯化反应激烈开始后迅速降温至400 ℃以下，待物料粘结现象消失后，再行升温氯化。出料及后期控制温在475 ± 25 ℃。经过3.8 ± 0.2hr氯化，可制得水不溶物小于1%并符合熔盐电解要求的YmmCl_3原料。此新工艺与原有干法工艺相比，流程短，装置简单，不需密闭抽真空，成本低，适于制取任何量的优质熔盐电解所需氯化稀土原料。在第二部分工作中，利用上述YmmCl_3原料，以液态铝为阴极，在氯化物体系中进行熔盐电解，通过试验得出在小型试验规模制取Ymm-Al合金的最隹工艺条件为：电解质组成（重量比）40%YmmCl_3-1%NaF-59%等摩尔的NaCl-KCl；电解温度为790 ± 5 ℃；阴极电流密为0.7 - 0.02A/cm~2；电解电量为333 ± 5库仑/克铝，制得钇铝合金中Ymm含量为10 ± 2%。添加1%的NaF可消除阴极表面生成枝状物，减少合金中夹渣和熔盐中沉渣。在电解工作中，将方差分析应用于试验数据处理，方差分析结果表明，各种试验因素对电效有明显影响，试验数据可靠，试验误差在允许范围以内。在第三部分工作中，利用线性扫描伏安法测定了在最隹电解工艺条件下Y~（3+）和Ymm在液态铝及钼电极上的析出电位。测定结果表明：Y~（3+）和Ymm~（3+）在液态铝阴极上的析出电位比在钼阴极上偏正0.2 ～ 0.8伏，氟离子的加入要比不加氟时析出电位不有同程度的负移，但考虑到氟离了具有消渣作用，加入少量氟比物添加剂对提高电效有利。

Cd、Pb、Cu、Zn和As在草甸棕壤中垂直迁移规律的研究

本文运用土柱淋溶试验，研究了不同条件下Cd、Pb、Cu、Zn和As等五种重金属元素在草甸棕壤中垂直迁移的规律。试验表明，一般情况下各重金属元素向下迁移的深度不超过10cm，绝大部分还是滞留在表层污染土中，因此在本试验条件下不会因淋溶迁移而导致地下水的污染。从不同重金属元素的迁移情况来看，Cd和Zn的迁移能力较强，Cu、Pb和As的迁移能力较弱。随着土壤pH值降低，Cd、Pb、Cu和Zn的迁移加强，As的迁移减弱。加大淋溶水量，能促进各种重金属离子随土壤水溶液的迁移。在供试浓度下，各重金属元素对水稻的生长没有危害，但对紫花苜蓿的生长却有影响，水稻籽实（或糙米）和紫花苜蓿茎叶中各重金属元素的含量都有增加，甚至超标。土壤施用石灰，能抑制各重金属元素在草甸棕壤中的迁移及被作物的吸收，是降低土壤重金属污染危害的一个有效措施。但是利用施加腐殖酸来防治土壤重金属污染往往会因造成土壤pH值下降、增加某些重金属的可溶性而遭失败。试验还表明，Cd、Pb、Cu和Zn的迁移在酸雨条件下会加剧，但As的迁移仅在弱酸性酸雨条件下增加，强酸性酸雨反而抑制As的迁移。