Al2O3 : Cr3+ nanotubes synthesized via homogenization precipitation followed by heat treatment

Cr3+-doped NH4Al(OH)(2)CO3 nanotubes, templated by surfactant assemblies, were successfully synthesized via the homogenization precipitation method, and various crystallographic phase Al2O3:Cr3+ nanotubes were also obtained by postannealing at different temperatures. The characteristic R-1, R-2 doublet line transitions of ruby can be observed in the high crystalline alpha-Al2O3 nanotubes calcined at temperatures higher than 1200 degrees C. The results also indicate that the formation mechanism of the tubular nanostructures should result from the self-rolling action of layered compound NH4Al(OH)(2)CO3 under the assistance of the surfactant soft-template. The convenient synthetic procedure, excellent reproducibility, clean reactions, high yield, and fine quality of products in this work make the present route attractive and significant. Aluminum oxide nanotubes with high specific surface area could be used as fabricating nanosized optical devices doped with different elements and stable catalyst supports of metal clusters.

Vibronic transitions and site substitution of Eu2+ and codoped ions in KMgF3 : Eu-X (X=Ce, Cr, Gd, Cu) system

The high-resolution emission spectra of KMgF3 : Eu and KMgF3 : Eu-X(X = Ce, Cr, Gd, Cu) single crystals were measured at 300 and 77 K. The vibronic side bands of Eu2+ were characterized and an assignment of the normal mode frequencies to particular vibrations has been made. The correlation between the vibronic frequencies of Eu2+ and the site substitution of other co-dopcd ions was first found. The relationship between vibronic intensity of Eu2+ and other doped ions concentration showed that Cr3+, Gd3+ ions competed K+ sites with Eu2+ ions. Ce3+ and Eu3+ occurred the electron transference. The introduction of Cu+ made for Eu2+ substuting for K+ sites.

Two bifurcation transitions of the floating half zone convection in a fat liquid bridge of larger Pr

The transient process of the thermocapillary convection was obtained for the large Pu floating half zone by using the method of three-dimensional and unsteady numerical simulation. The convection transits directly from steady and axisymmetric state to oscillatory flow for slender liquid bridge, and transits first from steady and axisymmetric convection to the steady and non-axisymmetric convection, then, secondly to the oscillatory convection for the fatter liquid bridge. This result implies that the volume of liquid bridge is not only a sensitive critical parameter for the onset of oscillation, but also relates to the new mechanism for the onset of instability in the floating half zone convection even in case of large Prandtl number fluid.

Transitions Between Different Contact Models

The transitions between the different contact models which include the Hertz, Bradley, Johnson-Kendall-Roberts (JKR), Derjaguin-Muller-Toporov (DMT) and Maugis-Dugdale (MD) models are revealed by analyzing their contact pressure profiles and surface interactions. Inside the contact area, surface interaction/adhesion induces tensile contact pressure around the contact edge. Outside the contact area, whether or not to consider the surface interaction has a significant influence on the contact system equilibrium. The difference in contact pressure due to the surface interaction inside the contact area and the equilibrium influenced by the surface interaction outside the contact area are physically responsible for the different results of the different models. A systematic study on the transitions between different models is shown by analyzing the contact pressure profiles and the surface interactions both inside and outside the contact area. The definitions of contact radius and the flatness of contact surfaces are also discussed. (C) Koninklijke Brill NV, Leiden, 2008.

Effect Of Load Triaxiality On Polymorphic Transitions In Zinc Oxide

Molecular dynamics (MD) simulations and first-principles calculations are carried out to analyze the stability of both newly discovered and previously known phases of ZnO under loading of various triaxialities. The analysis focuses on a graphite-like phase (FIX) and a body-centered-tetragonal phase (BCT-4) that were observed recently in [0 1 (1) over bar 0]- and [0 0 0 1]-oriented nanowires respectively under uniaxial tensile loading as well as the natural state of wurtzite (WZ) and the rocksalt (RS) phase which exists under hydrostatic pressure loading. Equilibrium critical stresses for the transformations are obtained. The WZ -> HX transformation is found to be energetically favorable above a critical tensile stress of 10 GPa in [0 1 (1) over tilde 0] nanowires. The BCT-4 phase can be stabilized at tensile stresses above 7 GPa in [0 0 0 1] nanowires. The RS phase is stable at hydrostatic pressures above 8.2 GPa. The identification and characterization of these phase transformations reveal a more extensive polymorphism of ZnO than previously known. A crystalline structure-load triaxiality map is developed to summarize the new understanding. (c) 2007 Elsevier Ltd. All rights reserved.

Three-photon-excited upconversion luminescence of YVO4 single crystal by infrared femtosecond laser irradiation

We report on the upconversion luminescence of a pure YVO4 single crystal excited by an infrared femtosecond laser. The luminescent spectra show that the upconversion luminescence comes from the transitions from the lowest excited states T-3(1), T-3(2) to the ground state (1)A(1) of the VO43-. The dependence of the fluorescence intensity on the pump power density of laser indicates that the conversion of infrared irradiation to visible emission is dominated by three-photon excitation process. We suggest that the simultaneous absorption of three infrared photons promotes the VO43- to excited states, which quickly cascade down to lowest excited states, and radiatively relax to ground states, resulting in the broad characteristic fluorescence of VO43-. (c) 2005 Optical Society of America.

Coherent population accumulations of multiphoton transitions induced by an ultrashort pulse train in polar molecules

Coherent population accumulations of multiphoton transitions induced by an ultrashort pulse train in a two-level polar molecule are investigated theoretically by solving the density-matrix equations without invoking any of the standard approximations. It is shown due to the effects of permanent dipole moments, that the population accumulation of multiphoton transitions can be obtained in the polar molecule. Moreover, the population accumulations depend crucially on the relative phase between two sequential pulses, and the period in which the maximum population accumulation occurs is 2 pi/N in N-photon transitions.

Optical transitions and upconversion luminescence of Er3+/Yb3+-codoped halide modified tellurite glasses

Er3+-doped halide modified tellurite glasses were synthesized by conventional melting and quenching method. The Judd-Ofelt analysis was performed on the absorption spectra and the transition probabilities, excited state lifetimes, and the branching ratios were calculated and discussed. The intense infrared and visible fluorescence spectra under 980 nm excitation were obtained. Strong upconversion signal was observed at pumping power as low as 30 mW in the glasses with halide ions. The upconversion mechanisms and power dependent intensities were discussed, which showed two-photon process are involved for the green and red emissions. The decay times of the emitting states and the corresponding quantum efficiency were determined and explained. (C) 2004 American Institute of Physics.

Optical transitions of Er3+ and Yb3+ ions in novel oxyfluoride bismuth-germanium glass: Observation of up-conversion

Er3+/Yb3+-codoped novel oxyfluoride bismuth-germanium glass was prepared and its up-conversion fluorescence property under 975 nm excitation has been studied. Intense green and weak red emissions centered at 525, 546, and 657 nm, corresponding to the transitions 2H(11/2) -> I-4(15/2), S-4(3/2) -> I-4(15/2), and F-4(9/2) -> I-4(15/2), respectively, were observed at room temperature. The possible up-conversion mechanism was also evaluated. The optimal Yb3+-Er3+ concentration ratio is found based on the direct lifetime measurements of excited levels for Er3+ ion. The structure of this novel oxyfluoride bismuth-germanium glass has been investigated by peak-deconvolution of FT-Raman spectrum, and the structural information was obtained from the peak wavenumbers. This novel oxyfluoride bismuth-germanium glass with relatively lower maximum phonon energy (similar to 731 cm(-1)) can be used as potential host material for up-conversion lasers. (c) 2005 Elsevier B.V. All rights reserved.

Enhanced near-infrared emission from Ni2+ in Cr3+ Ni2+ codoped transparent glass ceramics

Transparent Li2O-Ga2O3-SiO2 glass ceramics containing Cr3+/Ni2+ codoped LiGa5O8 nanocrystals were synthesized. The steady state emission spectra indicated that the near-infrared emission intensity of Ni2+ at 1300 nm in Cr3+/Ni2+ codoped glass ceramics was enhanced up to about 7.3 times compared with that in Ni2+ single-doped glass ceramics with 532 nm excitation. This enhancement in emission intensity was due to efficient energy transfer from Cr3+ to Ni2+, which was confirmed by time-resolved emission spectra. The energy transfer efficiency was estimated to be 85% and the energy transfer mechanism was discussed. (C) 2008 American Institute of Physics.

Upconversion luminescence from E-2 state of Cr3+ in Al2O3 crystal by infrared femtosecond laser irradiation

Visible upconversion luminescence was observed in Cr3+: Al2O3 crystal under focused femtosecond laser irradiation. The luminescence spectra show that the upconversion luminescence originates from the E-2-(4)A(2) transition of Cr3+. The dependence of the fluorescence intensity of Cr3+ on the pump power reveals that a two-photon absorption process dominates in the conversion of infrared radiation to the visible emission. It is suggested that the simultaneous absorption of two infrared photons produces the population of upper excited states, which leads to the characteristic visible emission from E-2 state of Cr3+.

Quantum phase transitions in the S=1/2 distorted diamond chain

By means of the second derivative of the ground-state and first-excited energy, the quantum phase transitions (QPTs) for the distorted diamond chain (DDC) with ferromagnetic and antiferromagnetic frustrated interactions and the trimerized case are investigated, respectively. Our results show the plentiful quantum phases owing to the spin interaction competitions in the model. Meanwhile, by using the transfer-matrix renormalization-group technique, we study the two-site thermal entanglement of the DDC model in the thermodynamic limit for a further understanding of the QPTs.