菱铁矿热转变过程中岩石磁学性质基本特征

利用吉林大栗子铁矿纯菱铁矿样品，系统测量了菱铁矿在空气环境的的磁化特征，揭示出其饱和曙剩磁（ＳＩＲＭ）、剩磁矫顽力（ＨＣＲ）和居里温度（ＴＣ）随加热温度升高而秘珠系列变化，菱放氧化中准稳定态性矿物磁赤铁矿是中间产物之一，并且具有较高的热稳定性，Ｘ射线衍射和穆斯堡尔效应等分析结果证实了岩石磁学研究所揭示的菱铁矿氧化中磁性矿物转变过程，菱铁矿氧化过程中结晶结构的转变可能会影响其氧化产物的磁性特性。

Magnetic properties and magnetic domain structure of bulk glass forming Nd60Al10Fe20Co10 alloy

The transition from hard to soft magnetic behaviour with increasing quenching rate is shown for Nd60WAl10Fe20Co10 melt-spun ribbons with different thickness. Microstructure and magnetic domain structure of ribbons were studied by magnetic force microscopy (MFM). Particle sizes < 5 nm decreasing gradually with increasing quenching rate were deduced from topographic images which differ from large-scale magnetic domains with a periodicity of about 350 nm in all ribbons irrespective the coercivity. This indicates that the magnetic properties of the alloy are governed by interaction of small magnetic particles. It is concluded that the presence of short-range-ordered structures with a local ordering similar to the Al metastable Nd-Fe binary phase is responsible for the hard magnetic properties in samples subjected to relatively low quenching rate.

Domain structure of hard magnetic NdAlFeCo bulk metallic glass

Magnetic domain structure of hard magnetic Nd60Al10Fe20Co10 bulk metallic glass (BMG) has been studied by using magnetic force microscopy. In the magnetic force images it is shown that the exchange interaction type magnetic domains with a period of about 360 nm do exist in the BMG, which is believed to be associated with the appearance of hard-magnetic properties in this system. As the scale of the magnetic domain is much larger than the size of the short-range ordered atomic clusters existing in the BMG, it is believed that the large areas of magnetic contrast are actually a collection of a group of clusters aligned in parallel by strong exchange coupling interaction. After fully crystallization, the BMG exhibits paramagnetism. No obvious magnetic contrast is observed in the magnetic force images of fully crystallized samples, except for a small quantity of ferromagnetic crystalline phase with low coercivity and an average size of 900 nm.

The magnetic and structure properties of room-temperature ferromagnetic semiconductor (Ga,Mn)N

Diluted magnetic semiconductor (Ga,Mn)N were prepared by the implantation of Mn ions into GaN/Al2O3 substrate. Clear X-ray diffraction peak from (Ga,Mn)N is observed. It indicates that the solid solution (Ga,Mn)N phase was formed with the same lattice structure as GaN and different lattice constant. Magnetic hysteresis-loops of the (Ga,Mn)N were obtained at room temperature (293 K) with the coercivity of about 2496.97 A m(-1). (C) 2003 Elsevier B.V. All rights reserved.

Magnetic properties of sintered sm2fe17ny magnets

Sintered magnets of Sm2Fe17Ny nitrides, with a density of 6.0-7.4 g/cm3, have been prepared by using an explosion technique. Both crystalline structure and the magnetic properties of Sm2Fe17Ny nitrides were retained in the process. The sintered magnet had a remanence B(r)=0.83 T, an intrinsic coercivity mu(0i)H(c)=0.57 T and an energy product (BH)max=88 kJ/m3. The temperature dependence of coercivity and remanence were also measured. The temperature coefficients alpha of remanence and beta of coercivity are -0.076%/degrees-C and -0.51%/degrees-C, respectively.

Structure and magnetic properties of CoNiP nanowire arrays embedded in AAO template

Ternary CoNiP nanowire (NW) arrays have been synthesized by electrochemical deposition inside the nanochannels of anodic aluminum oxide (AAO) template. The CoNiP NWs deposited at room temperature present soft magnetic properties, with both parallel and perpendicular coercivities less than 500 Oe. In contrast, as the electrolyte temperature (T-elc) increases from 323 to 343 K, the NWs exhibit hard magnetic properties with coercivities in the range of 1000-2500 Oe. This dramatic increase in coercivities can be attributed to the domain wall pinning that is related to the formation of Ni and Co nanocrystallites and the increase of P content. The parallel coercivity (i.e. the applied field perpendicular to the membrane surface) maximum as high as 2500 Oe with squareness ratio up to 0.8 is achieved at the electrolyte temperature of 328 K. It has been demonstrated that the parallel coercivity of CoNiP NWs can be tuned in a wide range of 200-2500 Oe by controlling the electrolyte temperature, providing an easy way to control magnetic properties and thereby for their integration with magnetic-micro-electromechanical systems (MEMS). (C) 2008 Elsevier B.V. All rights reserved.

Magnetic properties of ZnO-doped cobalt ferrite

The cobalt ferrites with chemical composition Co1+xZnxFe2-2xO4 (r=0.0, 0.1, 0.2, 0.4) were obtained with conventional solid reaction. The ZnO-doped samples have lower lattice constant than CoFe2O4 by adjusting Co ions to the octahedral sites. The results show that doping ZnO could extremely improve the magnetic properties. In comparison with pure CoFe2O4, the little ZnO-doped sample has higher permeability and much lower coercivity at the condition of a little decrease of magnetization saturation. Sample with x=0.1 shows evident magnetostrictive effect at the magnetic field of 30-60 mT while pure cobalt ferrite sample does not, though the saturation magnetostriction decreases. These indicate that ZnO-doping improves the magnetostrictive sensitivity of the cobalt ferrites and have potential applications in magnetoelectric devices and magnetic detector.

Formation of ferromagnetic clusters in GaAs matrix and GaAs/AlGaAs superlattice through Mn ion implantation at two different temperatures

Different submicron ferromagnets are fabricated into GaAs and GaAs/AlGaAs superlattice through ion implantation at two different temperatures followed by thermal annealing. The structural and magnetic properties of the granular film are studied by an atomic force microscope, X-ray diffraction and alternating gradient magnetometer. By analyzing the saturation magnetization M-s, remanence M-r, coercivity H-c and remanence ratio S-q, it is confirmed that both MnGa and MnAs clusters are formed in the 350degreesC-implanted samples whereas only MnAs clusters are formed in the room-temperature implanted samples. (C) 2004 Elsevier B.V. All rights reserved.

The magnetic and structure properties of room-temperature ferromagnetic semiconductor (Ga,Mn)N

Diluted magnetic semiconductor (Ga,Mn)N were prepared by the implantation of Mn ions into GaN/Al2O3 substrate. Clear X-ray diffraction peak from (Ga,Mn)N is observed. It indicates that the solid solution (Ga,Mn)N phase was formed with the same lattice structure as GaN and different lattice constant. Magnetic hysteresis-loops of the (Ga,Mn)N were obtained at room temperature (293 K) with the coercivity of about 2496.97 A m(-1). (C) 2003 Elsevier B.V. All rights reserved.

Effects of annealing on properties of spin-valve pinned with FeMn alloy

The magnetic properties of spin-valve pinned by FeMn layer were investigated after it was annealed at different temperatures. Its property was dependent on the vacuum annealing temperature. The pinning field could be increased through annealing at a temporature lower than 200degreesC;the pinning field would reduce and other properties be deteriorated as the annealing temperature was higher than 200degreesC; the pinning effect lost and giantmagnetic resistance disappeared at 300degreesC. Based on the results of AES analysis it was concluded that the diffusion in spin-valve multilayer was along grain boundary.

Determination of oxidation states in magnetic multilayers

X-ray photoelectron spectroscopy has been used to characterize the oxidation states in Ta/NiOx/Ni-81/Fe-19/Ta magnetic multilayers prepared by rf reaction and dc magnetron sputtering. The exchange coupling field and the coercivity of NiOx/Ni81Fe19 are studied as a function of the ratio of Ar to O-2 during the deposition process. The chemical states of Ni atoms in the interface region of NiOx/NiFe have also been investigated by x-ray photoelectron spectroscopy and the peak decomposition technique. The results show that the ratio of Ar to O-2 has a great effect on the chemical states of nickel in NiOx films. Thus the exchange coupling field and the coercivity of Ta/NiOx/Ni81Fe19/Ta are seriously affected. Also, the experiment shows that x-ray photoelectron spectroscopy is a powerful tool in characterizing magnetic multilayers.

Hard magnetic properties of Sm3Fe26.7VxN4 and Sm3Fe26.7VxCy

Sm3Fe26.7V2.3N4 nitrides and Sm3Fe26.7V2.3Cy carbides have been synthesized by gas-solid phase reaction. Their hard magnetic properties have been investigated by means of additional ball-milling at room temperature. The saturation magnetization of Sm3Fe26.7V2.3N4 almost decreases linearly with increasing ball-milling time t, but that of Sm3Fe26.7V2.3Cy has no obvious change when the ball-milling time increases from t = 1 to 28 h. As a preliminary result, the maximum remanence B-r of 0.94 and 0.88 T, the coercivity mu(0i)H(C) of 0.75 and 0.25 T, and the maximum energy product (BH) of 108.5 and 39.1 kJ/m(3) for their resin-bonded permanent magnets are achieved, respectively, by ball-milling at 293 K. (C) 1999 Published by Elsevier Science B.V. All rights reserved.

Thermomagnetic behavior and first order magnetization processes of Sm3Fe29-xTx and Sm3Fe29-xTxN4 (T = V and Cr)

A systematic investigation of structure and intrinsic magnetic properties of the compounds Sm3Fe29-xTx (T = V and Cr) and their nitrides has been performed. Nitrogenation resulted in remarkable improvements in the saturation magnetization and anisotropy fields at 4.2 K and room temperature. First order magnetization processes are observed at around 5.7 T for Sm3Fe26.7V2.3 and around 2.8 T for Sm3Fe24.0Cr5.0 and Sm3Fe24.0Cr5.0N4, respectively. The spin reorientation of the easy magnetization direction of Sm3Fe26.7V2.3 is observed at around 230 K. As a preliminary result, the maximum remanence B-r of 0.94 T, the coercivity mu(0)H(C) of 0.75 T, and the maximum energy product (BH) of 108.5 kJ/m(3) for the nitride magnet Sm3Fe26.7V2.3N4 are achieved by ball-milling at 293 K.

Crystallographic and magnetic properties of R3Fe29-xVxN4 (R = Y, Ce, Nd, Sm, Gd, Tb, and Dy)

A systematic investigation of crystallographic and magnetic properties of nitride R3Fe29-xVxN4 (R = Y, Ce, Nd, Sm, Gd, Tb, and Dy) has been performed. Nitrogenation leads to a relative volume expansion of about 6%. The lattice constants and unit cell volume decrease with increasing rare-earth atomic number from Nd to Dy, reflecting the lanthanide contraction. On average, the Curie temperature increases due to the nitrogenation to about 200 K compared with its parent compound. Generally speaking, nitrogenation also results in a remarkable improvement of the saturation magnetization and anisotropy fields at 4.2 K and room temperature for R3Fe29-xVxN4 compared with their parent compounds. The transition temperature indicates the spin reorientations of R3Fe29-xVxN4 for R = Nd and Sm are at around 375 and 370 K which are higher than that of R3Fe29-xVx, for R = Nd and Sm 145 and 140 K, respectively. The magnetohistory effects of R3Fe29-xVxN4 (R = Ce, Nd, and Sm) are observed in low fields of 0.04 T. After nitrogenation the easy magnetization direction of Sm3Fe26.7V2.3 is changed from an easy-cone structure to the b-axis. As a preliminary result, a maximum remanence B-r of 0.94 T, an intrinsic coercivity mu(0)H(C) of 0.75 T, and a maximum energy product (B H)(max) of 108.5 kJ m(-3) for the nitride magnet Sm3Fe26.7V2.3N4 are achieved by ball-milling at 293 K.

Magnetic properties of ZnO-doped cobalt ferrite

The cobalt ferrites with chemical composition Co1+xZnxFe2-2xO4 (r=0.0, 0.1, 0.2, 0.4) were obtained with conventional solid reaction. The ZnO-doped samples have lower lattice constant than CoFe2O4 by adjusting Co ions to the octahedral sites. The results show that doping ZnO could extremely improve the magnetic properties. In comparison with pure CoFe2O4, the little ZnO-doped sample has higher permeability and much lower coercivity at the condition of a little decrease of magnetization saturation. Sample with x=0.1 shows evident magnetostrictive effect at the magnetic field of 30-60 mT while pure cobalt ferrite sample does not, though the saturation magnetostriction decreases. These indicate that ZnO-doping improves the magnetostrictive sensitivity of the cobalt ferrites and have potential applications in magnetoelectric devices and magnetic detector.