MoNi/gamma-Al2O3 Catalyst: Preparation and Catalytic Activity for Acetic Acid Hydrotreating

MoNi/gamma-Al2O3 catalysts were prepared by the impregnation method. The catalyst samples were characterized by XRD and TPR. The effects of Mo promoter content and the catalyst reducing temperature Oil hydrotreatment activity of the catalyst were studied under 200 degrees C and 3 MPa hydrogen pressure using acetic acid as the model compound. The XRD results indicate that the addition of Mo promoter is beneficial to the uniformity of nickel species on the catalyst and decreases the Interaction between nickel species and the support Which results in the decrease the of NiAl2O4 spinel formation. The addition of Mo promoter also decreases the reducing temperature of the catalyst. After the catalyst of 0.06 MoNi/gamma-Al2O3 being reduced Under the atmosphere of H-2/N-2(5/95, V/V), nickel oxide was reduced to Ni-0. The reaction was promoted obviously upon the addition of the MoNi/gamma-Al2O3 catalyst reduced at 600 degrees C. The Mo-modified Ni/gamma-Al2O3 catalyst reduced at 600 degrees C displayed the highest activity during the reaction, the conversion of acetic acid reached the highest point of 33.2%. The products included ethyl acetate and water.

An in-situ modified sol-gel process for monolith catalyst preparation used in the partial oxidation of methane

An in-situ modified sol-gel method for the preparation of a Ni-based monolith-supported catalyst is reported. With the presence of a proper amount of plasticizer and binder, and at an optimized pH value, the stable boehmite sol was modified with metal ions (Ni, Li, La) successfully without distinct growth of the particle size. Monolith-supported Ni-based/gamma-Al2O3 catalysts were obtained using the modified sol as the coating medium with several cycles of dip-coating and calcination. Combined BET, SEM-EDS, XRD and H-2-TPR investigations demonstrated that the derived monolith catalysts had a high specific surface area, a relatively homogeneous surface composition, and a high extent of interaction between the active component and the support. These catalysts showed relatively stable catalytic activities for partial oxidation of methane (POM) to syngas under atmospheric pressure. The monolith catalysts prepared by this sol-gel method also demonstrated an improved resistance to sintering and loss of the active component during the reaction process.

Preparation and application of a novel core-shell-particle-supported zirconocene catalyst

The use of functional groups bearing silica/poly(styrene-co-4-vinylpyridine) core-shell particles as a support for a zirconocene catalyst in ethylene polymerization was studied. Several factors affecting the behavior of the supported catalyst and the properties of the resulting polymer, such as time, temperature, Al/N (molar ratio), and Al/Zr (molar ratio), were examined. The conditions of the supported catalyst preparation were more important than those of the ethylene polymerization. The state of the supported catalyst itself played a decisive role in both the catalytic behavior of the supported catalyst and the properties of polyethylene (PE). IR and X-ray photoelectron spectroscopy were used to follow the formation of the supports. The formation of cationic active species is hypothesized, and the performance of the core-shell-particle-supported zirconocene catalyst is discussed as well. The bulk density of the PE formed was higher than that of the polymer obtained from homogeneous and polymer-supported Cp2ZrCl2/methylaluminoxane catalyst systems. (C) 2001 John Wiley & Sons, Inc.

Preparation of SiO2-ligated Metallo-phthalocyanine (MPc) and it's Role in the Activation of Dioxygen

The metal phthalocyanines (MPc, M-Fe, Co, Cu) were supported on the surface of silica gel by chemical linking. They could not be washed out with organic solvents such as Py. UV-Vis diffuse reflectance spectra indicated that MPc's were supported on silica

Investigations on the promoting effect of metal oxides on La-V-O catalyst in propane oxidative dehydrogenation

The addition of reducible metal oxides as promoters shows a positive effect on the catalytic behavior of lanthanum vanadate (LaVO4). A C3H6 yield increase of 6.5% is observed at 500 degreesC on molybdenum-promoted LaVO4, which can be attributed to the change of the redox properties, the blocking of the strong oxidation sites of the catalysts and to an increase of the accessibility of the labile oxygen toward the reactant. The influence of the catalyst preparation method and of the Mo loading as well as the additional promoting effect of CO2 in the gas feed was also examined.

Epoxidation of propylene over Ag-CuCl catalysts using air as the oxidant

Ag-CuCl catalysts were found to be active and selective for the epoxidation of propylene using air as the oxidant. Ag catalyst gives a propylene conversion of 31.6%, with a propylene oxide (PO) selectivity of 0.42% at a reaction temperature of 350 degreesC after 220 min of reaction. Addition of CuCl significantly improves the selectivity to PO, and suppresses the conversion of propylene. The Ag-CuCl (1/0.6) catalyst gives propylene conversion of about 3% and a PO selectivity of about 30% at a reaction temperature of 350 degreesC after 500 min of reaction. The activity of the Ag-CuCl catalyst increases with the reaction time and the selectivity to PO is very stable for this catalyst. It is found that AgCl and CuO phases formed during the catalyst preparation are beneficial to the epoxidation of propylene.

A Mossbauer study of In-Fe2O3/HZSM-5 catalysts for the selective catalytic reduction of NO by methane

The selective catalytic reduction of NO by CH4 was compared over In-Fe2O3/HZSM-5 catalysts prepared by impregnation and co-impregnation methods. It was found that the catalyst preparation method greatly affected the catalyst activity. The impregnated catalyst was very active, but the co-impregnated one showed poor activity. The In Fe2O3/HZSM-5 catalysts were investigated by Mossbauer spectroscopy. The results showed that indium cations entered into the iron oxide lattice in the co-impregnated catalyst, while the impregnated catalyst exhibited a more stable structure, when both of the catalysts were treated severely in the reaction atmosphere. Characterization by means of combined in situ temperature programmed reduction (TPR)- Mossbauer spectroscopy further revealed that the performances of the two catalysts were different in the TPR processes.

Rare Earth Pyrophosphates: Effective Catalysts for the Production of Acrolein from Vapor-phase Dehydration of Glycerol

Vapor-phase dehydration of glycerol to produce acrolein was investigated at 320 A degrees C over rare earth (including La, Ce, Nd, Sm, Eu, Gd, Tb, Ho, Er, Tm, Yb, Lu) pyrophosphates, which were prepared by precipitation method. The most promising catalysts were characterized by means of XRD, FT-IR, TG-DTA, BET and NH3-TPD measurements. The excellent catalytic performance of rare earth pyrophosphate depends on the appropriate surface acidity which can be obtained by the control of pH value in the precipitation and the calcination temperature, e.g. Nd-4(P2O7)(3) precipitated at pH = 6 and calcined at 500 A degrees C in the catalyst preparation.

Synergetic effect between NiO and Ni3V2O8 in propane oxidative dehydrogenation

The oxidative dehydrogenation (ODH) of propane was investigated on Ni-V-O catalysts in a wide range of vanadium contents (5-40%). The addition of a small amount of vanadium significantly increased the catalytic activity of NiO for oxidative dehydrogenation of propane to propene. The formation of propene has a good correlation with the coexistence of NiO and Ni3V2O8. This result strongly suggests that a synergetic effect exists between them in NiXV1-XOY (X = 0.95 to 0.6). The best results were obtained with a high Ni/V ratio (e.g. X = 0.95 to 0.85). The active sites and selective oxygen species are discussed. The influence of the catalyst preparation technique and the redox properties of the catalyst were also examined.

Enhancement of the catalytic performance of supported-metal catalysts by pretreatment of the support

We report an interesting finding that the catalytic performance of supported Ag/SiO2 catalysts toward selective catalytic oxidation of CO in hydrogen at low temperatures can be greatly enhanced by pretreatment of the SiO2 support before catalyst preparation. Calcination of SiO2 at appropriate temperatures preferentially removes the H-bonded SiOH, which results in the highly dispersive Ag/SiO2 catalyst and thus improves the catalytic performance. (c) 2005 Elsevier Inc. All rights reserved.