Facile preparation of macroscopic soft colloidal crystals with fiber symmetry

A facile, efficient way to fabricate macroscopic soft colloidal crystals with fiber symmetry by drying a latex dispersion in a tube is presented. A transparent, stable colloidal crystal was obtained from a 25 wt % latex dispersion by complete water evaporation for 4 days. The centimeter-long sample was investigated by means of synchrotron small-angle X-ray diffraction (SAXD). Analysis of a large number of distinct Bragg peaks reveals that uniaxially oriented colloidal crystals with face-centered cubic lattice structure were formed.

Enhanced infrared emission from colloidal HgTe nanocrystal quantum dots on silicon-on-insulator photonic crystals

A two dimensional silicon-on-insulator based photonic crystal structure is used to enhance the emission from colloidal HgTe nanocrystal quantum dots embedded in a thin polymer film. The enhancement is resonant to the leaky eigenmodes of the photonic crystals due to coherent scattering effects. Transmittance and photoluminescence experiments are presented to map the leaky mode dispersion and the angle dependence of the emission enhancement factor, which reaches values up to 80 (650) for vertical (oblique) emission in the telecommunication wavelength range.

Optical intensity gradient by colloidal photonic crystals with a graded thickness distribution

Gradient colloidal crystals with a thickness gradient were prepared by the vertical deposition technique with vertically graded concentration suspensions. The thickness of the gradient colloidal crystal gradually changes at different positions along the specific gradient direction of the crystal. The thickness gradient was determined by the concentration gradient, depending on the initial colloidal concentration and the settling time. The optical transmission intensity at the dip wavelength can be tuned by changing the thickness of the colloidal crystals. The gradient colloidal crystals lead to a gradient of optical intensity at the dip in transmission light. The gradient of optical intensity at the dip increases as the thickness gradient of the colloidal crystal increases.

Influence Of Gravity On Structure Of Colloidal Crystal Using Simulated Microgravity

Liquid mixtures of water and deuterium oxide as the liquid phase, were used to match the density of charged colloidal particles. Kossel diffraction method was used to detect the crystal structures. The experiments under the density-matched (g=0) and unmatched (g=1) conditions are compared to examine the influence of gravity on the crystal structures formed by self-assembly of 110 nm (in diameter) polystyrene microspheres. The result shows that die gravity tends to make the lattice constants of colloidal crystals smaller at lower positions, which indicates that the effect of gravity should be taken into account in the study of the colloidal crystals.

Reversibly strain-tunable elastomeric photonic crystals

Reversibly strain-tunable polymeric photonic crystals made of thermoplastic polyester elastomer (TPEE) were fabricated by using the self-assembled silica opals as templates. The stop band of the polymeric photonic crystal locates at the near infrared (IR) regime in its transmission spectrum, and exhibits a blue shift with the increase of the incident angle. Because of the elasticity of the TPEE, the stop band of the TPEE photonic crystal can also be reversibly tuned at ambient temperature through to and fro uniaxially or biaxially stretching and recovering by changing the lattice spacing and the symmetry of the crystal along (1 1 1) plane.

Non-affine structural evolution of soft colloidal crystalline latex films under stretching as observed via synchrotron X-ray scattering

A polymer dispersion consisting of soft latex spheres with a diameter of 135 nm was used to produce a crystalline film with face-centered cubic (fcc) packing of the spheres. Different from conventional small-molecule and hardsphere colloidal crystals, the crystalline latex film in the present case is soft (i.e., easily deformable). The structural evolution of this soft colloidal latex film under stretching was investigated by in-situ synchrotron ultra-small-angle X-ray scattering. The film exhibits polycrystalline scattering behavior corresponding to fcc structure. Stretching results not only in a large deformation of the crystallographic structure but also in considerable nonaffine deformation at high draw ratios. The unexpected nonaffine deformation was attributed to slippage between rows of particles and crystalline grain boundaries. The crystalline structure remains intact even at high deformation, suggesting that directional anisotropic colloidal crystallites can be easily produced.

Tunable photonic crystals by mixed liquids

Tunable photonic crystals were prepared by infiltrating mixed liquids into the voids of silica opals. The stop bands of the tunable photonic crystals were continuously tuned by changing the relative refraction index contrast n(mix)/ns(pheres) of the spheres and the mixed liquids by varying the volume fraction of the component of the mixed liquids. The peak wavelengths of the stop band have a red shift as the refractive index of the mixed liquids increases. The transmittance at the stop band decreases with the increase of the refractive index contrast n(mix)/n(spheres). The larger the diameter of silica opals is, the wider the tunable range of the stop band is. The position and transmittance of the peak wavelength obtained by the photonic band calculations agreed very well with the experimental data.

二元体系胶体晶体性质的实验研究

利用Kossel衍射技术和反射光谱对由总体积分数为0.02的二元聚苯乙烯胶体体系(94 nm+141 nm)形成的胶体晶体的性质进行了研究,实验结果显示胶体晶体的形成时间,平均粒子间距,晶体结构都与二元胶体体系中两种粒子的数密度比相关,当94 nm聚苯乙烯粒子相对于141 nm聚苯乙烯粒子的数密度比趋向1∶1时,胶体晶体的形成时间延长,当94 nm聚苯乙烯粒子相对于141 nm聚苯乙烯粒子的数密度比由1∶0向0∶1变化时,胶体晶体的平均粒子间距变大,另外实验中发现在两种粒子的数密度比为5∶1时,胶体晶体出现了超晶格结构. 

Characterization Of Crystal Structure In Binary Mixtures Of Latex Globules

Colloidal crystals formed by two types of polystyrene particles of different sizes (94 and 141 nm) at various number ratios (94:141 nm) are studied. Experiments showed that the formation time of crystals lengthens as the number ratio of the two components approaches 1:1. The dependence of the mean interparticle distance (D-0), crystal structure and alloy structure on the number ratio of the two types of particles was Studied by means of Kossel diffraction technique and reflection spectra. The results showed that as the number ratio decreased, the mean interparticle distance (D-0) became larger. And the colloidal crystal in binary mixtures is more preferably to form the bcc structure. This study found that binary systems form the substitutional solid solution (sss)-type alloy structure in all cases except when the number ratio of two types of particles is 5:1, which results instead in the superlattice structure. (C) 2008 Elsevier Inc. All rights reserved.

Rapidly Infrared-Assisted Cooperatively Self-Assembled Highly Ordered Multiscale Porous Materials

In this paper, cooperative self-assembly (CSA) of colloidal spheres with different sizes was studied. It was found that a complicated jamming effect makes it difficult to achieve an optimal self-assembling condition for construction of a well-ordered stacking of colloidal spheres in a relatively short growth time by CSA. Through the use of a characteristic infrared (IR) technique to significantly accelerate local evaporation on the growing interface without changing the bulk growing environment, a concise three-parameter (temperature, pressure, and IR intensity) CSA method to effectively overcome the jamming effect has been developed. Mono- and multiscale inverse opals in a large range of lattice scales can be prepared within a growth time (15-30 min) that is remarkably shorter than the growth times of several hours for previous methods. Scanning electron microscopy images and transmittance spectra demonstrated the superior crystalline and optical qualities of the resulting materials. More importantly, the new method enables optimal conditions for CSA without limitations on sizes and materials of multiple colloids. This strategy not only makes a meaningful advance in the applicability and universality of colloidal crystals and ordered porous materials but also can be an inspiration to the self-assembly systems widely used in many other fields, such as nanotechnology and molecular bioengineering.

带电胶体粒子结晶过程的实验研究

利用带电单分散聚苯乙烯胶体粒子,通过自组装机理,制备了体积百分比为4·8%的具有多晶结构的胶体晶体,并用Kossel衍射技术和紫外可见分光光度计分别对晶体的生长过程进行了监测.通过对Kossel的图像分析检测不同阶段相应的晶格结构,发现胶体结晶过程晶体结构演变顺序为由液态—随机层结构—堆无序结构—面心立方孪晶结构到面心立方结构.定量地确定了结晶过程中晶体不同晶面的晶面间距和晶体的晶格常数,通过紫外可见分光光度计测量的晶体透射谱图,计算得到111晶面的晶面间距和晶体的晶格常数,与用Kossel衍射技术得到的结果相一致,还发现随样品放置时间的延长,衰减峰变窄和加深,并向短波方向移动,对应着晶体的晶格常数减小的现象.

带电悬浮粒子胶体晶体的固定化

采用光固化技术, 以丙烯酰胺单体与亚甲基双丙烯酰胺交联剂在紫外光的照射下发生光聚合反应, 嵌入聚苯乙烯胶体晶体, 实现了胶体晶体的固定化. 结合反射光谱和Kossel衍射技术研究对照了固定化前后胶体晶体的变化, 实验结果表明, 通过这种水凝胶固定化的胶体晶体保存了未固定前悬浮液中胶体晶体的结构. 但固定化后的胶体晶体的晶面间距和晶体的尺寸都略微减小. 通过对固定化后的水凝胶长时间的反射光谱观测, 发现固定化后胶体晶体在Milli-Q水中起初会发生溶胀, 经过2-5天溶胀-消溶胀过程达到平衡, 平衡后的水凝胶胶体晶体十分稳定, 可以长时间保持胶体晶体的结构. 因此, 胶体晶体固定化不但极大地提高了悬浮液中胶体晶体的抗剪切能力, 还克服了悬浮液中胶体晶体对离子、外界干扰的敏感性, 扩大了胶体晶体的实际应用价值.

Tunable Multiresponsive Methacrylic Acid Based Inverse Opal Hydrogels Prepared by Controlling the Synthesis Conditions

Methacrylic acid based inverse opal hydrogels (MIOHs) have been prepared by controlling the synthesis conditions, including cross-linker content, solvent content, and water content in solvent mixtures to explore the effect of the synthesis conditions (especially solvent content and mixture) on the response performance. Various response events (pH, solvent, ionic strength, 1,4-phenylenediamine dihydrochloride (PDA) response) have been investigated. For pH, solvent response, the same response behaviors have been observed: both the increased solvent (only ethanol) content and the enhanced water content in solvent will lead to the reduced response level of MIOHs compared to that of the increased cross-linker content. However, two different kinds of response behaviors for ionic strength response have been found by adjusting the synthesis conditions. The kinetics of pH response shows characteristics of a diffusion-limited process, and the equilibrium response time is about 20 min, which cannot be reduced by changing the synthesis conditions.