Laser-induced well-ordered and controllable wavy patterns are constructed in the deposited metal thin film. The micrometer-sized structure and orientation of the wavy patterns can be controlled via scanning a different size of rectangle laser spot on the films. Ordered patterns such as aligned, crossed, and whirled wave structures were designed over large areas. This patterning technique may find applications in both exploring the reliability and mechanical properties of thin films, and fabricating microfluidic devices. (C) 2004 American Institute of Physics.

Thermodynamic model of hydrogen-induced silicon surface layer cleavage

A thermodynamic model of hydrogen-induced silicon surface layer splitting with the help of a bonded silicon wafer is proposed in this article. Wafer splitting is the result of lateral growth of hydrogen blisters in the entire hydrogen-implanted region during annealing. The blister growth rate depends on the effective activation energies of both hydrogen complex dissociation and hydrogen diffusion. The hydrogen blister radius was studied as a function of annealing time, annealing temperature, and implantation dose. The critical radius was obtained according to the Griffith energy condition. The time required for wafer splitting at the cut temperature was calculated in accordance with the growth of hydrogen blisters. (C) 2001 American Institute of Physics.

Surface morphology of He-implanted single-crystalline silicon

Single-crystalline Si (100) samples were implanted with 30 keV He2+ ions to doses ranging from 2.0x10(16) to 2.0x10(17) ions/cm(2) and subsequently thermally annealed at 800 degrees C for 30min. The morphological change of the samples with the increase of implantation dose was investigated using atomic force microscopy (AFM). It was found that oblate-shaped blisters with an average height around 4.0nm were found on the 2.0 x 10(16) ions /cm(2) implanted sample surface; spherical-shaped blisters with an average height wound 10.0nm were found on the 5.0 x 10(16) ions/cm(2) implanted sample surface; strip-shaped and conical cracks were observed on the sample He-implanted to a dose of 1.0 X 10(17) ions /cm(2). Exfoliations occurred on the sample surface to a dose of 2.0 x10(17) ions /cm(2). Mechanisms underlying the surface change were discussed.