Evolution from point defects to arsenic clusters in low-temperature grown GaAs/AlGaAs multiple quantum wells

Optical transient current spectroscopy (OTCS), photoluminescence (PL) spectroscopy and excitonic electroabsorption spectroscopy have been used to investigate the evolution of defects in the low-temperature grown GaAs/AlGaAs multiple quantum well structures during the postgrowth rapid thermal annealing. The sample was grown at 350 degrees C by molecular beam epitaxy on miscut (3.4 degrees off (001) towards (111)A) (001) GaAs substrate. After growth, the sample was subjected to 30s rapid thermal annealing in the range of 500-800 degrees C. It is found that the integrated PL intensity first decreases with the annealing temperature, then gets a minimum at 600 degrees C and finally recovers at higher temperatures. OTCS measurement shows that besides As,, antisites and arsenic clusters, there are several relatively shallower deep levels with excitation energies less than 0.3 eV in the as-grown and 500 degrees C-annealed samples. Above 600 degrees C, OTCS signals from As,, antisites and shallower deep levels become weaker, indicating the decrease of these defects. It is argued that the excess arsenic atoms group together to form arsenic clusters during annealing. (C) 2000 Elsevier Science B.V. All rights reserved.

Effect of arsenic precipitates on Fermi level in GaAs grown by molecular-beam epitaxy at low temperature

A simple model is presented to discuss the effect of As precipitates on the Fermi level in GaAs grown by molecular-beam epitaxy at low temperature (LT-GaAs). This model implements the compensation between point defects and the depletion of arsenic precipitates. The condition that the Fermi level is pinned by As precipitates is attained. The shifts of the Fermi level in LT-GaAs with annealing temperature are explained by our model. Additionally, the role of As precipitates in conventional semi-insulating GaAs is discussed. (C) 2000 American Institute of Physics. [S0021-8979(00)09905-9].