Localized Solid-State Amorphization at Grain Boundaries in a Nanocrystalline Al Solid Solution Subjected to Surface Mechanical Attrition

Using high-resolution electron microscopy, localized solid-state amorphization (SSA) was observed in a nanocrystalline (NC) Al solid solution (weight per cent 4.2 Cu, 0.3 Mn, the rest being Al) subjected to a surface mechanical attrition treatment. It was found that the deformation-induced SSA may occur at the grain boundary (GB) where either the high density dislocations or dislocation complexes are present. It is suggested that lattice instability due to elastic distortion within the dislocation core region plays a significant role in the initiation of the localized SSA at defective sites. Meanwhile, the GB of severely deformed NC grains exhibits a continuously varying atomic structure in such a way that while most of the GB is ordered but reveals corrugated configurations, localized amorphization may occur along the same GB.

Nanocavity shrinkage and preferential amorphization during irradiation in silicon

We model the recent experimental results and demonstrate that the internal shrinkage of nanocavities in silicon is intrinsically associated with preferential amorphization as induced by self-ion irradiation. The results reveal novel thermodynamic nonequilibrium properties of such an open-volume nanostructure in condensed matter and also of covalently bound amorphous materials both at nanosize scale and during ultrafast interaction with energetic beam.

Shear Localization In Dynamic Deformation: Microstructural Evolution

Investigations made by the authors and collaborators into the microstructural aspects of adiabatic shear localization are critically reviewed. The materials analyzed are low-carbon steels, 304 stainless steel, monocrystalline Fe-Ni-Cr, Ti and its alloys, Al-Li alloys, Zircaloy, copper, and Al/SiCp composites. The principal findings are the following: (a) there is a strain-rate-dependent critical strain for the development of shear bands; (b) deformed bands and white-etching bands correspond to different stages of deformation; (c) different slip activities occur in different stages of band development; (d) grain refinement and amorphization occur in shear bands; (e) loss of stress-carrying capability is more closely associated with microdefects rather than with localization of strain; (f) both crystalline rotation and slip play important roles; and (g) band development and band structures are material dependent. Additionally, avenues for new research directions are suggested.

Molecular Dynamics Study Of The Mechanical Behavior Of Nickel Nanowire: Strain Rate Effects

We present the analysis of uniaxial deformation of nickel nanowires using molecular dynamics simulations, and address the strain rate effects on mechanical responses and deformation behavior. The applied strain rate is ranging from 1 x 10(8) s(-1) to 1.4 x 10(11) s(-1). The results show that two critical strain rates, i.e., 5 x 10(9) s(-1) and 8 x 10(10) s(-1), are observed to play a pivotal role in switching between plastic deformation modes. At strain rate below 5 x 10(9) s(-1), Ni nanowire maintains its crystalline structure with neck occurring at the end of loading, and the plastic deformation is characterized by {111} slippages associated with Shockley partial dislocations and rearrangements of atoms close to necking region. At strain rate above 8x10(10) s(-1), Ni nanowire transforms from a fcc crystal into a completely amorphous state once beyond the yield point, and hereafter it deforms uniformly without obvious necking until the end of simulation. For strain rate between 5 x 10(9) s(-1) and 8 x 10(10) s(-1), only part of the nanowire exhibits amorphous state after yielding while the other part remains crystalline state. Both the {111} slippages in ordered region and homogenous deformation in amorphous region contribute to the plastic deformation. (C) 2007 Published by Elsevier B.V.

Size effects on the melting of nickel nanowires: a molecular dynamics study

The melting process of nickel nanowires are simulated by using molecular dynamics with the quantum Sutten-Chen many-body force field. The wires studied were approximately cylindrical in cross-section and periodic boundary conditions were applied along their length; the atoms were arranged initially in a face-centred cubic structure with the [0 0 1] direction parallel to the long axis of the wire. The size effects of the nanowires on the melting temperatures are investigated. We find that for the nanoscale regime, the melting temperatures of Ni nanowires are much lower than that of the bulk and are linear with the reciprocal of the diameter of the nanowire. When a nanowire is heated up above the melting temperature, the neck of the nanowire begins to arise and the diameter of neck decreases rapidly with the equilibrated running time. Finally, the breaking of nanowire arises, which leads to the formation of the spherical clusters. (C) 2004 Elsevier B.V. All rights reserved.

Atomistic Simulation On Size-Dependent Yield Strength And Defects Evolution Of Metal Nanowires

A simple derivation based on continuum mechanics is given, which shows the surface stress is critical for yield strength at ultra-small scales. Molecular dynamics (MD) simulations with modified embedded atom method (MEAM) are employed to investigate the mechanical behaviors of single-crystalline metal nanowires under tensile loading. The calculated yield strengths increasing with the decrease of the cross-sectional area of the nanowires are in accordance with the theoretical prediction. Reorientation induced by stacking faults is observed at the nanowire edge. In addition. the mechanism of yielding is discussed in details based on the snapshots of defects evolution. The nanowires in different crystallographic orientations behave differently in stretching deformation. This study on the plastic properties of metal nanowires will be helpful to further understanding of the mechanical properties of nanomaterials. (C) 2009 Elsevier B.V. All rights reserved.

Nanoinstabilities as revealed by shrinkage of nanocavities in silicon during irradiation

While the thermodynamic nonequilibrium properties of nanoparticles are being extensively studied, the thermodynamic nonequilibrium properties of their counterpart: nanocavities, however, are less noticed. Here, we systematically review and comprehensively model the recently published results on the newly-found thermodynamic nonequilibriurn properties of nanocavities in covalently bound materials during energetic beam irradiation. We also review and model the thermodynamic nonequilibrium properties of nanoparticles. The review and modelling not only demonstrates the novel nonequilibriurn properties of such an open-volume nanostructure during external excitation but also gives a deep insight into the nonequilibrium thermodynamics of amorphous structures and the difference in the behaviours of defects in crystalline and in amorphous silicon. Especially, the review and modelling leads to two new concepts:anti-symmetry relation between a nanoparticle and a nanocavity；energetic beam induced-soft mode and lattice instability in condensed matter；which reveals that structure of a condensed matter would be unstable not only at nanosize scale but also at a nanotime scale in general. It is also reveals that such nanoinstabilities would be more pronounced in an amorphous structure than in a crystalline structure.

Shrinkage of nanocavities in silicon during electron beam irradiation

An internal shrinkage of nanocavity in silicon was in situ observed under irradiation of energetic electron on electron transmission microscopy. Because there is no addition of any external materials to cavity site, a predicted nanosize effect on the shrinkage was observed. At the same time, because there is no ion cascade effect as encountered in the previous ion irradiation-induced nanocavity shrinkage experiment, the electron irradiation-induced instability of nanocavity also provides a further more convincing evidence to demonstrate the predicted irradiation-induced athermal activation effect. (c) 2006 American Institute of Physics.

RBS STUDIES OF THE LATTICE DAMAGE CAUSED BY 1 MEV SI+ IMPLANTATION INTO AL0.3GA0.7AS/GAAS SUPERLATTICES AT ELEVATED-TEMPERATURE

The lattice damage accumulation in GaAs and Al0.3Ga0.7As/GaAs superlattices by 1 MeV Si+ irradiation at room temperature and 350-degrees-C has been studied. For irradiations at 350-degrees-C, at lower doses the samples were almost defect-free after irradiation, while a large density of accumulated defects was induced at a higher dose. The critical dose above which the damage accumulation is more efficient is estimated to be 2 x 10(15) Si/cm2 for GaAs, and is 5 x 10(15) Si/cm2 for Al0.8Ga0.7As/GaAs superlattice for implantation with 1.0 MeV Si ions at 350-degrees-C. The damage accumulation rate for 1 MeV Si ion implantation in Al0.3Ga0.7As/GaAs superlattice is less than that in GaAs.

The SPER and characteristics of Si1-yCy alloys

\Si1-yCy alloys with carbon composition of 0.5 at.% were successfully grown on n-Si(100) substrate by solid phase epitaxy recraystallization. The result was presented in this paper. With the help of the SiO2 capping layer, rather uniform carbon profile in amorphous Si layer was obtained by dual-energy implantation. Since ion-flow was small and implantation time was long enough, the emergency of beta-SiC was avoided and the dynamic annealing effect was depressed. The pre-amorphization of the Si substrate increased the fraction of the substitutions carbon and the two-step annealing reduced point defects. As a result, Si1-yCy alloys with high quality was recrystallized on Si substrate.

碳化硅中氦离子高温注入引入的缺陷及其退火行为的光谱研究

对氦(He)离子高温(600K)注入6H-SiC中的辐照缺陷,在阶梯温度退火后演化行为的拉曼光谱和室温光致发光谱的特征进行了分析.这两种方法的实验结果表明,离子注入所产生晶格损伤的程度与注入剂量有关;高温退火导致损伤的恢复,不同注入剂量造成的晶格损伤需要不同的退火温度才可恢复.在阶梯温度退火下呈现出了点缺陷的复合、氦-空位团的产生、氦泡的形核、长大等特性.研究表明:高温(600K)注入在一定剂量范围内是避免注入层非晶化的一个重要方法,为后续利用氦离子注入空腔掩埋层吸杂或者制备低成本、低缺陷密度的绝缘层上碳化硅(SiCOI)材料提供了可能.