Shear localization and recrystallization in dynamic deformation of 8090 Al-Li alloy

The microstructural evolution in localized shear deformation was investigated in an 8090 Al-Li alloy by split Hopkinson pressure bar (strain rate of approximately 10(3) s(-1)) at ambient temperature and 77 K. The alloy was tested in the peak-, over-, under-, and natural-aged conditions, that provide a wide range of microstructural parameters and mechanical properties. Two types of localized shear bands were distinguished by optical microscopy: the deformed shear band and the white-etching shear band. They form at different stages of deformation during localization. There are critical strains for the occurrence of deformed and white-etching localized shear deformation, at the imposed strain rate. Observations by transmission electron microscopy reveal that the white-etching bands contain fine equiaxed grains; it is proposed that they are the result of recrystallization occurring during localization. The deformed-type bands are observed after testing at 77 K in all heat treatment conditions, but they are not as well defined as those developed at ambient temperature. Cracking often occurs along the localized shear at ambient temperature. The decrement in temperature is favorable for the nucleation, growth and coalescence of the microcracks along the shear bands, inducing fracture.

Microstructures of explosively consolidated rapidly solidified aluminum and Al-Li alloy powders

The microstructures and the characteristics of water-atomized, nitrogen gas-atomized Al powders and ultrasonic argon gas-atomized Al-Li alloy powder were investigated by means of metallography, SEM, Auger electron spectroscopy and X-ray diffraction techniques. Rapidly solidified powders were explosively consolidated into different sized cylinders under various explosive parameters. The explosively consolidated compacts have been tested and analysed for density microhardness, retention of rapidly solidified microstructures, interparticle bonding, fractography and lattice distortion. It is shown that the explosive consolidation technique is an effective method for compacting rapidly solidified powders. The characteristics of surface layers play a very important role in determining the effectiveness of the joints sintered, and the Al-Li alloy explosive compacts present an abnormal softening appearance compared to the original powder.

Crystallization of mechanically alloyed amorphous W-Mg alloy under high pressure

Pure metal powder mixtures of W and Mg at the desired composition were milled in conventional high-energy ball mill, and amorphous alloy W50Mg50 was obtained after milling for 20 h. The structure evolution of elemental powder mixtures was studied following milling and subsequent high pressure and high temperature treatment. The amorphous alloy transform into a nanocrystalline material below 1050 degreesC at 4.0 GPa. On increasing the temperature, it transforms into a mixture of several new crystal phases under high-pressure condition. It also found that both mechanical alloying and high pressure treatment are the two necessary processes to form the nanocrystalline and the new phases.

稀土对Al-Mg-Si系合金结构和性能的影响

本文用ＸＲＤ和ＳＥＭ方法研究了稀土对Ａｌ－Ｍｇ－Ｓｉ系合金微观结构的影响，同时还测定了这些合金的耐腐蚀及力学性能。结果表明，该体系的稀土铝合金中大约含０．１０％稀土就可以细化组织，提高使用性能。具有很好的应用前景。

稀土对Al-Mg-Si建筑铝型材性能的影响

研究了稀土对Ａｌ－Ｍｇ－Ｓｉ建筑铝型材性能的影响。其微观结构及组成采用金相显微镜、扫描电子显微镜及光电子能谱分析，同时测量了样品的机械强度和耐蚀性能。结果表明其挤压预热温度降至４３０℃，速度达到６．２８～７．３６ｍｍ／ｓ，在Ａｌ－Ｍｇ－Ｓｉ材料中加入适量的稀土可以细化晶粒并且增加了材料的机械强度和耐蚀性能。

稀土对Al-Mg-Si合金性能影响和稀土作用机理研究

本文研究了稀土对铝镁硅合金性能的影响通过添加稀土改善合金的综合性能,提高合金的成品率,表面光泽性和致密度,讨论了稀土对铝镁硅合金的作用机理,为稀土在铝镁硅合金型材中的推广应用提供了有力的实验依据。

Characteristics of anodic coatings oxidized to different voltage on AZ91D Mg alloy by micro-arc oxidization technique

With increasing applied voltage, three types of anodic coatings, passive film, micro-spark ceramic coating and spark ceramic coating were made by micro-arc oxidization (MAO) technique on AZ91D magnesium alloy in alkali-silicate solution. The structure, composition characteristics and the electrochemical properties of coatings were also studied with SEM, XRD and EIS (electrochemical impedance spectroscopy) technique, respectively. It is found that the electrochemical properties are closely related to the structure and composition characteristics of the anodic coatings. At the same time, the characteristics of the three types of anodic coatings differ significantly, among them, the micro-spark ceramic coating, prepared in the voltage range of 170similar to220V exhibits compact, homogeneous structure and highest corrosion-resistance.

Study on growth factors of intermetallic layer within hot-dipped 25% Al-Zn alloy coating on steel

25%Al-Zn alloy coating performs better than hot dip galvanized coating and 55%Al-Zn-Si coating with regard to general seawater corrosion protection. This study deals with the interfacial intermetallic layer's growth, which affects considerably the corrosion resistance and mechanical properties of 25%Al-Zn alloy coatings, by means of three-factor quadratic regressive orthogonal experiments, The regression equation shows that the intermetallic layer thickness decreases rapidly with increasing content of Si added to the Zn-Al alloy bath, increases with rise in bath temperature and prolonging dip time. The most effective factor that determined the thickness of intermetallic layer was the amount of Si added to Zn-Al alloy bath, while the effect of bath temperature and dip time on the thickness of intermetallic layer were not very obvious.

Thermodynamics and kinetics analysis of in-situ synthesizing AlN

AIN powders were prepared by in-situ synthesis technique. It is a reaction of binary molten Al-Mg alloys with highly pure nitrogen. It was confirmed through thermodynamics calculation that Mg element in Al-Mg alloys can decrease oxygen content in the reacting system. Thus, nitridation reaction can be performed to form AIN. Moreover, an analysis of kinetics shows that the nitridation reaction of Al-Mg alloys can be accelerated and transferred rapidly with the increment of Mg content.

Mg-Al-Mn-RE系合金组织与性能研究

利用金属型铸造制备了Mg-5Al-0.3Mn-xRE (x = 0~4, wt%，RE = Ce, Nd, Sm, Y和(CeLa)混合稀土)系列合金，研究了铸态合金的组织和力学性能。利用轧制和挤压技术对优化出的合金进行了变形加工处理，并研究了合金加工后的组织和力学性能。 对于铸态合金，稀土元素不仅可以细化合金的晶粒，而且形成不同类型的Al-RE化合物，含Ce的合金中生成Al11Ce3相，含Nd或Sm的合金中，主要生成Al11Nd3 (Al11Sm3)相和少量的Al2Nd (Al2Sm)相，含Y的合金中生成Al2Y相。另外，添加稀土可以改变Mg17Al12相的形貌，使其变得更加细小、弥散。添加适量的稀土可以明显提高铸态合金在室温和150℃下的力学性能，Mg-5Al-0.3Mn-1.5Ce, Mg-5Al-0.3Mn-2Nd和Mg-5Al-0.3Mn-2Sm合金在各自的体系中具有最佳的综合力学性能。合金力学性能提高的主要原因是细晶强化、Al-RE化合物第二相强化以及减弱Mg17Al12相对合金高温力学性能的不利影响。 对Mg-5Al-0.3Mn-(1.0, 1.5, 2.0)Ce，Mg-5Al-0.3Mn-2Nd，Mg-5Al-0.3Mn-1.5(CeLa)和Mg-5Al-0.3Mn-3Y合金在300-400℃下进行了热轧制或挤压变形，与铸态合金相比，轧制和挤压合金具有更高的力学性能。轧制合金的室温抗拉强度为290-340 MPa，较铸态合金提高约50％，屈服强度约为210-260 MPa，较铸态合金提高约2倍。挤压态合金的抗拉强度为260-270 MPa，屈服强度为160-190MPa，伸长率为20-22％；150℃的力学性能也得到了明显改善。 结合热力学计算、合金化元素之间的电负性差、化合物相的生成焓数据以及相图计算，阐述了稀土化合物相的生成机制，稀土元素与Al元素之间的电负性差大于其与Mg之间的电负性差，且Al-RE相的生成焓远低于Mg-RE和Mg-Al相的生成焓，因此在Mg-Al合金中加入RE后，RE优先与Al形成Al-RE化合物。从晶粒细化、化合物强化相的生成和演变、变形加工处理的位错交互作用等方面讨论了合金的强化机制，认为细晶强化、第二相强化及形变强化是提高合金力学性能的主要机制。

Microstructure, tensile properties, and creep behavior of high-pressure die-cast Mg-4Al-4RE-0.4Mn (RE = La, Ce) alloys

High-pressure die-cast (HPDC) Mg-4Al-4RE-0.4Mn (RE = La, Ce) magnesium alloys were prepared and their microstructures, tensile properties, and creep behavior have been investigated in detail. The results show that two binary Al-Ce phases, Al11Ce3 and Al2Ce, are formed mainly along grain boundaries in Mg-4Al-4Ce-0.4Mn alloy, while the phase composition of Mg-4Al-4La-0.4Mn alloy contains only alpha-Mg and Al11La3. The Al11La3 phase comprises large coverage of the grain boundary region and complicated morphologies. Compared with Al11Ce3 phase, the higher volume fraction and better thermal stability of Al11La3 have resulted in better-fortified grain boundaries of the Mg-4Al-4La-0.4Mn alloy. Thus higher tensile strength and creep resistance could be obtained in Mg-4Al-4La-0.4Mn alloy in comparison with that of Mg-4Al-4Ce-0.4Mn. Results of the theoretical calculation that the stability of Al11La3 is the highest among four Al-RE intermetallic compounds supports the experimental results further.

Investigations of the properties of Mg-5Al-0.3Mn-xCe (x=0-3, wt.%) alloys

Mg-5Al-0.3Mn-xCe (x = 0-3, wt.%) alloys were prepared by metal mould casting method. The microstructures and mechanical properties were investigated. The results revealed that the main phases of as-cast Mg-5Al-0.3Mn alloy consist of alpha-Mg matrix and beta-Mg17Al12 phase. With the addition of Ce element, Al11Ce3 precipitates were formed and mainly aggregated along the grain boundaries. The amount of the Al11Ce3 precipitates increased with increasing addition of Ce, but the amount of beta-Mg17Al12 phase decreased. The highest tensile strength was obtained in Mg-5Al-0.3Mn-1.5Ce alloy. The ultimate tensile strength (UTS), yield strength (YS) and elongation at room temperature are 203 MPa, 88 MPa and 20%, separately.

Effects of spark discharge on the anodic coatings on magnesium alloy

Spark discharge was the representative phenomenon of Micro-arc oxidation (MAO) method distinguished from other electrochemical oxidation methods. Under the spark discharge treatment, characteristics of the anodic layer were significantly changed. To investigate the influences of the spark discharge, a piece of magnesium alloy AZ91D specimen was partly treated by MAO method in alkaline silicate solution. And the microstructure, element distributions as well as the surface potential distributions of the specimen were studied by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and scanning Kelvin probe (SKP) technique. As a result of intensive spark discharge treatment, porous external layer with dense internal layer were formed on Mg alloy surface. At the same time, the depositions of OH- and SiO32- ions were accelerated, which resulted in the enrichment of element oxygen and silicon at the spark discharge region. Moreover, due to the compact internal layer, the intensive spark discharge region exhibited more positive potentials with respect to other regions, which meant this region could restrain the ejection of electron and provide effective protection to the substrate. In addition, it was found that oxygen played a vital role in determining the intensity and size of sparks, and abundant oxygen resulted in intensive and larger sparks. (c) 2005 Elsevier B.V. All rights reserved.

Synthesis of composite AIN powder mixed with sintering additives by the Lanxide method

Composite AlN powder, mixed with the sintering additive Y2O3, was synthesized by the direct nitridation of molten Al-Mg-Y alloys. The character of products was determined by means of electron microscopy, X-ray diffraction, granularmetric analysis and chemical composition analysis etc. The results show that the nitridation rate of the raw alloys is higher, and the nitridation products axe porous enough to be easily crushed. Composite AlN powder, obtained by the Lanxide method, has excellent characters such as high purity, especially low oxygen content, and narrow well-distributed grain size and so on.

In-situ synthesis of AlN powders and composite AlN powders with yttrium addition

Using Al-Mg and Al-Mg-Y alloys as raw materials and nitrogen as gas reactants, AIN powders and composite AIN powders by in-situ synthesis method were prepared. AIN lumps prepared by the nitriding of Al-Mg and Al-Mg-Y alloys have porous microstructure, which is favorable for pulverization. They have high purity, containing 1.23 % (mass fraction) oxygen impurity, and consisted of AIN single phase . The average particle size of AIN powders is 6.78 mum. Composite AlN powders consist of AlN phases and rare, earth oxide Y2O3 phase. The distribution of particle size of AIN powders shows two peaks. In view, of packing factor, AIN powders with such size distribution can easily be sintered to high density.