A uniform 290 nm periodic square structure on ZnO fabricated by two-beam femtosecond laser ablation

A uniform submicron periodic square structure was fabricated on the surface of ZnO by a technique of two linearly polarized femtosecond laser beams with orthogonal polarizations ablating material alternately. The formed two-dimensional ordering submicron structure consists of close-packed submicron squares with a spacial periodicity of 290 nm, which arises from the intercrossing of two orthogonal submicron ripple structures induced by the two beams respectively. The result demonstrates a noninterference effect of two-beam ablation based on the alternate technique, which should come from the polarization-dependent enhancement of the subwavelength ripple structure and the large interval of two alternate pulses. This two-beam alternate ablation technique is expected to open up prospects for the submicron fabrication of wide-bandgap materials.

Investigation Of Mode Ii Crack Growth Following A Very High Speed Impact

A recoverable plate impact testing technology has been developed for studying fracture mechanisms of mode II crack. With this technology, a single duration stress pulse with submicrosecond duration and high loading rates, up to 10(8) MPam(1/2)s(-1), can be produced. Dynamic failure tests of Hard-C 60# steel were carried out under asymmetrical impacting conditions with short stress-pulse loading. Experimental results show that the nucleation and growth of several microcracks ahead of the crack tip, and the interactions between them, induce unsteady crack growth. Failure mode transitions during crack growth, both from mode I crack to mode II and from brittle to ductile fracture, were observed. Based on experimental observations, a discontinuous crack growth model was established. Analysis of the crack growth mechanisms using our model shows that the shear crack extension is unsteady when the extending speed is between the Rayleigh wave speed c(R) and the shear wave speed c(S). However, when the crack advancing speed is beyond c(S), the crack grows at a steady intersonic speed approaching root 2c(S). It also shows that the transient mechanisms, such as nucleation, growth, interaction and coalescence among microcracks, make the main crack speed jump from subsonic to intersonic and the steady growth of all the subcracks causes the main crack to grow at a stable intersonic speed.

波作用量守恒原理在波流相互作用中的应用

提出了解决Stokes波与指数剖面流同向或反向相遇过程中波传播特征改变问题的五阶理论, 给出了这种相互作用前后波参数间的关系和相应流场的变化, 并与线性结果进行了比较.

考虑晶界滑错的金属多晶体响应的自洽方法

首先建立含有三种介质(各向异性基体、各向异性夹杂、界面层)的平面应变夹杂模型.将基体和夹杂位移场展开为多项式级数,假设界面层很薄,运用变分原理得出这一问题的近似解.将上述夹杂问题的解和HILL自洽方法相结合,给出了考虑晶界滑错效应的金属多晶体弹塑性响应.

盲肠回流的水流运动特性

本文在总结和分析现有研究成果的基础上，系统地论述了盲肠回流的形成原因和运动机理。描述了盲肠回流运动系统的物理模式。根据水槽模型试验结果，对回流的流速分布特性、水面形态、以及影响回流运动强度的因素等进行了分析，并近似求解了盲肠回流的平面流速场。

AR5395活动区中的剪切储能(摘要)

<正> 在太阳活动区AR5395中存在不断地旋转运动。产生了一系列大耀斑之后,活动区的磁场位形重新组建。活动区内的磁场被剪切。本文建立了一个剪切的开放的磁拱模型,利用2(1/2)维的理想磁流体动力学方程组,研究了磁拱底部的磁场剪切储存能量。通

大功率C0_2激光器输出窗口的热应力问题

本文分析了大功率流动CO_2激光器输出窗口的热应力破坏问题。结果表明最主要的破坏原因是窗口内表面被微小杂质玷污造成膜层破坏和局部加热而引起的热应力。如果在设计及工艺上设法解决这个问题,窗口寿命可望显著提高。

LJD状态方程的简便公式

为了实际使用更方便,我们提出了LJD状态方程的一个简便公式。这个简化了的表达式是基于LJD理论在θ从10到290和τ从0.3到1.0范围内的数值结果得来的,而该理论中所用的分子间相互作用势是6-exp(α=13)势。用这式子计算的结果与数值结果相比最大偏差约为10％,而对爆轰产物所涉及的范围则在6％以内。

脉冲激光相变硬化中的二维点阵光强分布设计

激光强度空间分布是影响脉冲激光相变硬化效果的重要因素。现有的二维点阵光束按强度均匀分布设计,不能完全满足应用要求。为此提出基于有限元(FE)分析的光强空间分布逆向设计思路,并给出了实现方法。建立脉冲激光相变硬化有限元模型,考虑了材料热物性参数随温度的变化和相变过程,并用实验进行校核。研究了二维点阵分布参数对温度场的影响,从目标温度场和硬化层形貌出发对二维点阵的分布参数进行调整,获得优化的强度空间分布。针对汽车冲压模具表面强化的工艺要求,应用此方法设计出具有实用价值的激光强度空间分布。

Investigation of Vaporized Kerosene Injection in a Supersonic Model Combustor

Characteristics of vaporized aviation kerosene injection in a supersonic model combustor were preliminarily investigated. The electrically storage type heater has a volume capacity of heating kerosene of 0.8 kg up to 670 K at a pressure of 5.5 Mpa. The temperature to cause pressurized kerosene jet being fully vaporized in Quiescent atmosphere was found to be 550 K at 4 Mpa however the pressurized hot kerosene remains in liquid state within the tube. The correspondent jet spray in Mach 2.5 vitiated air cross-flow were visualized by using stop schlieren photograph.It was found the penetration depth of the hot pressurized kerosene jet is approximately same with the temperature varied from 290 K to 550 k. at pressure of 4 Mpa. This results showed that the atomization process of hot kerosene jet spray in supersonic combustor could be bypassed and directly transferred to be gas state at temperature 550 K and pressure of 4 Mpa.

板壳断裂力学

本书阐明了板壳断裂理论的基础。论证了Reissner型板壳断裂理论的科学性、经典板壳断裂理论的缺陷及在一定范围内仍具有的实用价值；介绍了作者所创意的研究Reissner型板壳断裂纹尖端场的方法等。

目录

Effect of coal-over-coal reburn on furnace temperature and heat flux distributions in 1 MW tangentially fired furnace

The furnace temperature and heat flux distributions of 1 MW tangentially fired furnace were studied during coal-over-coal reburn, and the influences of the position of reburn nozzle and reburn fuel fraction on furnace temperature and heat flux distributions were investigated. Compared with the baseline, the flue gas temperature is 70–90 C lower in primary combustion and 130–150 C higher at furnace exit, and the variations of the flue gas temperature distributions along furnace height are slower. The temperature distribution along the width of furnace wall decreases with the increase of the relative furnace height. In the primary combustion zone and the reburn zone, the temperature and heat flux distributions of furnace wall are much non-uniform and asymmetric along the width of furnace wall, those of furnace wall in the burnout zone are relatively uniform, and the temperature non-uniformity coefficients of the primary combustion zone, the reburn zone and the burnout zone are 0.290, 0.100 and 0.031, respectively.

双套管密相气力输运过程的数值模拟和能耗分析

基于计算流体力学理论,提出一种可用于预测双套管密相气力输送系统能耗的新方法.与以往依靠经验的计算方法不同,本工作将输送管道分为起始段与充分发展段两部分,分别进行详细的计算流体力学模拟后汇总得出整个系统的总能耗.压力梯度为750 Pa/m的情况下,计算所得物料输送速率为10 t/h,耗气量为290 m~3/h,实验所得物料输送速率为8.0 t/h,耗气量240 m~3/h,证明本数模方法是可靠的.

变形镜对千赫兹掺钛蓝宝石飞秒激光频谱相位补偿

尝试用光谱展宽的方法从频谱相位(而非时域相位)的角度利用变形反射镜来补偿1kHz飞秒激光系统输出光路的频谱相位畸变，从而提高飞秒激光脉冲的时域强度衬比度，改善其光束质量。频谱相位补偿实验是在一台1kHz掺钛蓝宝石飞秒激光系统输出光路中，针对超短脉冲光束通过传输介质后的频谱相位畸变，引入变形反射镜进行补偿。应用频谱相位干涉直接电场重构(SPIDER)方法和仪器作为测量手段，建立了一套相位测量补偿系统。实验结果表明用变形反射镜可使激光脉冲的相位畸变得到较好的补偿，脉冲的光束质量得到改善。这种方法的主要思想就是

Thermal analyses, spectral characterization and structural interpretation of Yb3+ doped TeO2-ZnO-ZnCl2 glasses

Bulk-lasses have been prepared in the TeO2-ZnO-ZnCl2 systems. Their characteristic temperatures were determined and analyzed. Raman and FT-IR spectra were used to analyze the effect of ZnCl2 on the structure and spectral properties of tellurite glasses and OH- groups in this glass system. The spectroscopic properties including absorption spectra, emission cross-sections and fluorescence lifetimes of Yb3+ in TeO2-ZnO-ZnCl2 were measured and calculated. It is demonstrated that the progressive replacement less than 20 mol% of TeO2 by ZnCl2 improves the thermal stability, removes the OH- groups, turns TeO4 bipyramidal arrangement into TeO3 (and/or TeO3+1) trigonal pyramids structures and results in the decrease of the symmetry of the structure, which increases the emission cross-sections and lifetimes. But when the content of ZnCl2 up to 30 mol%, the glass system becomes more hygroscopic and introduces more OH- groups, which decrease the emission cross-sections and shorten the lifetimes. The results show that the glass system with (TeO2)-Te-69-(ZnO)-Zn-10-20ZnCl(2)-1Yb(2)O(3) is a desirable component for active laser media for high power generation. (c) 2005 Elsevier B.V. All rights reserved.