Resumo:
利用高能离子研究了110keV的He+注入Al2O3单晶及随后230MeV的208Pb27+辐照并在不同温度条件下退火样品的光致发光的特性.从测试结果可以清楚地看到在375nm,390nm,413nm和450nm出现了强烈的发光峰.经过600K退火2h后测试结果显示,390nm发光峰增强剧烈,而别的发光峰显示不明显.在900K退火条件下,390nm的发光峰开始减弱相反在510nm出现了较强的发光峰,到1100K退火完毕后390nm的发光峰完全消失,而510nm的发光峰相对增强.从辐照样品的FTIR谱中看到,波数在460—510cm-1间的吸收是振动模式,经过离子辐照后,吸收带展宽,随着辐照量的增大,Al2O3振动吸收峰消失,说明Al2O3振动模式被完全破坏.1000—1300cm-1之间为Al-O-Al桥氧的伸缩振动模式,辐照后吸收带向高波数方向移动.退火后的FTIR谱变化不大.
Resumo:
主要研究了110keV的He~+高温注入Al_2O_3单晶及1.1MeV/u的~(208)Pb~(27+)辐照注氦Al_2O_3样品的光致发光的特性。从测试结果可以清楚地看到在375nm,413nm和450nm处出现了强烈的发光峰。并且在600K,5×10~(16) ions/cm~2剂量点,样品的发光峰是最强的。这表明He~+注入Al_2O_3后使带隙中深的辐射中心复合的效率大幅度提高,极大的增强了其发光强度,而且发光伴随着蓝移现象。而经过高能~(208)Pb~(27+)辐照后的样品,在390nm出现了新的发光峰,从FTIR谱中我们能够看到,可能是~(208)Pb~(27+)辐照相对沉积膜出现一定的晶化,其中含有许多纳米尺寸的Al_2O_3晶粒所致。
Resumo:
介绍了一种弧形靶框夹芯208Pb靶的制备工艺,包括核靶的制备装置和制备方法、核靶厚度和均匀性的控制和测量方法,并对结果进行了讨论。制备采用旋转蒸镀法,该法可以大大提高材料的利用率。所制靶的结构为30μg/cm2C+361μg/cm2208Pb+15μg/cm2C,同一次所制的靶平均厚度为361μg/cm2,不均匀性小于9.8%。其性能能够很好地满足超重核实验研究的要求。
Resumo:
以18 O重离子束轰击厚天然铅靶 ,通过多核子转移反应生成2 0 8Hg核 .辐照铅片放入离线熔化铅靶气相热色谱装置中处理 ,分离并收集汞元素产物 .完成了 4πΔEβγ γ ,γ X(γ)关联事件谱及γ射线时序单谱测量 .建议了 2 1条γ射线 ,以及能量为 1 3 65,1 72 7keV的两条2 0 8Tl新能级的2 0 8Hgβ- 衰变部分γ纲图 .
Resumo:
用半经典模型考虑20Na+208Pb→p+19Ne+208Pb的Coulomb解离过程。用MonteCarlo方法计算前角放置的望远镜阵列对Coulomb解离碎片的探测效率。讨论了天体环境下p+19Ne→20Na俘获反应道的低能级共振截面测量的可行性。
Resumo:
Highly charged ions (HCls) carrying high Coulomb potential energy (E-p) could cause great changes in the physical and chemical properties of material surface when they bombard on the solid surface. In our work, the secondary ion yield dependence on highly charged Pbq+ (q = 4-36) bombardment on Al surface has been investigated. Aluminum films (99.99%) covered with a natural oxide film was chosen as our target and the kinetic energy (E-k) was varied between 80 keV and 400 keV. The yield with different incident angles could be described well by the equation developed by us. The equation consists of two parts due to the kinetic sputtering and potential sputtering. The physical interpretations of the coefficients in the said equation are discussed. Also the results on the kinetic sputtering produced by the nuclear energy loss on target Surface are presented.
Resumo:
Surface change of gallium nitride specimens after bombardment by highly charged Pbq+-ions (q = 25, 35) at room temperature is studied by means of atomic force microscopy. The experimental results reveal that the surface of GaN specimens is significantly etched and erased. An unambiguous step-up is observed. The erosion depth not only strongly depends on the charge state of ions, but also is related to the incident angle of Pbq+-ions and the ion dose. The erosion depth of the specimens in 60 incidence (tilted incidence) is significantly deeper than that of the normal incidence. The erosion behaviour of specimens has little dependence on the kinetic energy of ion (E-k = 360, 700 keV). On the other hand, surface roughness of the irradiated area is obviously decreased due to erosion compared with the un-irradiated area. A fiat terrace is formed.
Resumo:
Photodissociation dynamics of ketene following excitation at 208.59 and 213.24 nm have been investigated using the velocity map ion-imaging method. Both the angular distribution and translational energy distribution of the CO products at different rotational and vibrational states have been obtained. No significant difference in the translational energy distributions for different CO rotational state products has been observed at both excitation wavelengths. The anisotropy parameter beta is, however, noticeably different for different CO rotational state products at both excitation wavelengths. For lower rotational states of the CO product, beta is smaller than zero, while beta is larger than zero for CO at higher rotational states. The observed rotational dependence of angular anisotropy is interpreted as the dynamical influence of a peculiar conical intersection between the B-1(1) excited state and (1)A(2) state along the C-S-I coordinate.
Resumo:
Self-ignition tests of a model scramjet combustor were conducted by using parallel sonic injection of gaseous hydrogen from the base of a blade-like strut into a supersonic vitiated airstream. The range of stagnation pressure and temperature studied varied from 1.0 to 4.5 MPa and from 1300 to 2200 K, respectively. Experimental results show that the self-ignition limit, in terms of either global or local quantities of pressure and temperature, exhibits a nonmonotonic behavior resembling the classical homogeneous explosion limit of the hydrogen-oxygen system. Specifically, for a given temperature, increasing pressure from a low value can render a nonignitable mixture to first become ignitable, then nonignitable again, This correspondence shows that, despite the globally supersonic nonpremixed configuration studied herein, ignition is strongly influenced by the intricate chemical reaction mechanism and thereby exhibits the homogeneous explosion character. Consequently, self-ignition criteria based on a global reaction rate approximating the complex chemistry are inadequate. An auxiliary computational study on counterflow ignition was also conducted to systematically investigate the contamination effects of vitiated air. Results indicate that the net contamination effects for the present experimental data are expected to be substantially smaller than contributions from the individual contamination species because of the counterbalancing influences of the H2O-inhibition and NO-promotion reactions in effecting ignition.
Resumo:
A general incremental micromechanical scheme for the nonlinear behavior of particulate composites is presented in this paper. The advantage of this scheme is that it can reflect partly the effects of the third invariant of the stress on the overall mechanical behavior of nonlinear composites. The difficulty involved is the determination of the effective compliance tensors of the anisotropic multiphase composites. This is completed by making use of the generalized self-consistent Mori-Tanaka method which was recently developed by Dai et al. (Polymer Composites 19(1998) 506-513; Acta Mechanica Solida 18 (1998) 199-208). Comparison with existing theoretical and numerical results demonstrates that the present incremental scheme is quite satisfactory. Based on this incremental scheme, the overall mechanical behavior of a hard-particle reinforced metal matrix composite with progressive particle debonding damage is investigated.
Resumo:
采用Bermin的孔洞成核的局部应力准则以及Euler坐标系下大应变有限元方法,分析了平面应变条件下二相粒子与基体在三种不同的界面结合强度下的宏观材料的力学行为.