Resumo:
稀土掺杂氧氟玻璃是一种优良的上转换发光材料,制备了组分为35SiO2—15AlO1.5-(45-x)PbF2-xCdF2—0.1TmF3—1.5YbF3(x=0,10,20,30)的氧氟硅酸盐玻璃,系统研究了CdF2含量对其热学性能和光学性能的影响。研究表明用CdF2部分替代PbF,可以提高玻璃的热稳定性、使紫外吸收截至边向短波方向移动;随着CdF2含量的增加,开始Tm^3+蓝光和红光上转换发光增强缓慢,而后迅速增强.而近红外上转换发射先显著增强后增强放缓;由于蓝光和近红外发光强度远大于红光发光强度,所以
Resumo:
The near-IR emission spectra of Er3+-Tm3+ codoped 70GeS(2)-20In(2)S(3)-10CsI chalcohalide glasses were studied with an 808 nm laser as an excitation source. A broad emission extending from 1.35 to 1.7 mu m with a FWHM of similar to 160 nm was recorded in a 0.1 mol.% Er2S3, 0.5 mol.% Tm2S3 codoped chalcohalide glass. The fluorescence decay curves of glasses were measured by monitoring the emissions of Tm3+ at 1460 nm and Er3+ at 1540 nm, and the lifetimes were obtained from the first-order exponential fit. The luminescence mechanism and the possible energy-transfer processes are discussed with respect to the energy-level diagram of Er3+ and Tm3+ ions. (C) 2008 Optical Society of America
Resumo:
We report on cooperative downconversion in Yb3+-RE3+ (RE = Tm or Pr) codoped lanthanum borogermanate glasses (LBG), which are capable of splitting a visible photon absorbed by Tm3+ or Pr3+ ions into two near-infrared photons. The results indicate that Pr3+-Yb3+ is a more efficient ion couple than Tm3+-Yb3+ in terms of cooperative downconversion. We have obtained a highest quantum yield of 165% and 138% for Pr3+-Yb3+ and Tm3+-Yb3+ codoped LBG glasses under 468 nm excitation, respectively. However, ultraviolet light excitation to the charge transfer band of Yb3+ does not result in quantum splitting as rapid relaxation from the charge transfer band to 4f(13) levels of Yb3+ dominates. (C) 2008 Optical Society of America
Resumo:
Three-dimensional flowerlike Lu2O3 and Lu2O3:Ln(3+) (Ln = Eu, Th, Dy, Pr, Sm, Er, Ho, Tm) microarchitectures have been successfully synthesized via ethylene glycol (EG)-mediated hydrothermal method followed by a subsequent heat treatment process. X-ray diffraction, Fourier transform infrared spectroscopy, energy-dispersive X-ray spectra, thermogravimetric and differential thermal analysis, elemental analysis, inductively coupled plasma atomic absorption spectrometric analysis, ion chromatogram analysis, X-ray photoelectron spectra, scanning electron microscopy, transmission electron microscopy, photoluminescence spectra as well kinetic decays, and cathodoluminescence spectra were used to characterize the samples. Hydrothermal temperature, EG, and CH3COONa play critical roles in the formation of the lutetium oxide precursor microflowers. The reaction mechanism and the self-assembly evolution process have been proposed. The as-formed lutetium oxide precursor could transform to Lu2O3 With their original flowerlike morphology and slight shrinkage in the size after postannealing process.
Resumo:
介绍了一种基于3×3和2×2光纤耦合器构成的非平衡马赫-曾德尔干涉仪的波长解调方案。理论分析和数据对比表明,相对于由两个2×2光纤耦合器构成的马赫-曾德尔干涉仪,本干涉仪具有宽谱的灵敏度、能跟踪波长的变化方向和相位展开的优点,实验方案用于测量固定在悬臂梁上的传感光纤布拉格光栅(FBG)的峰值波长变化,获得了±1pm的静态波长解调精度,在10Hz处的动态分辨率为27nε/√Hz。相位展开算法使得应变测量范围达到了2014με,对应的相位变化为3.22π。
Resumo:
We investigated the use of a deep-etched fused-silica grating with triangular-shaped grooves as a highly efficient polarizing beam splitter (PBS). A triangular-groove PBS grating is designed at a wavelength of 1550 nm to be used in optical communication. When it is illuminated in Littrow mounting, the transmitted TE- and TM-polarized waves are mainly diffracted in the minus-first and zeroth orders, respectively. The design condition is based on the average differences of the grating mode indices, which is verified by using rigorous coupled-wave analysis. The designed PBS grating is highly efficient over the C+L band range for both TE and TM polarizations (> 97.68 %). It is shown that such a triangular-groove PBS grating can exhibit a higher diffraction efficiency, a larger extinction ratio, and less reflection loss than the binary-phase fused-silica PBS grating. (C) 2008 Optical Society of America.
Resumo:
2μm激光器由于其在遥感、雷达和医疗等领域具有重要的应用前景而受到越来越广泛的重视。Tm3+具有长的荧光寿命,且其吸收带与商用的激光二极管相匹配。YAP具有与YAG近似的机械和热性能,其双折射特性使得Tm:YAP激光器可以直接得到线偏振的激光输出,并且可以降低热退偏效应。795nm连续抽运光经透镜组耦合进薄片板条1mm×5mm晶体端面,采用平凹腔结构,分析比较了1%,4%和5%掺杂浓度的Tm:YAP的激光特性。
Resumo:
We demonstrate passive Q-switching of short-length double-clad Tm3+-doped silica fiber lasers near 2 mu m pumped by a laser diode array (LDA) at 790 nm. Polycrystalline Cr2+:ZnSe microchips with thickness from 0.3 to 1 mm are adopted as the Q-switching elements. Pulse duration of 120 ns, pulse energy over 14 mu] and repetition rate of 53 kHz are obtained from a 5-cm long fiber laser. As high as 530 kHz repetition rate is achieved from a 50-cm long fiber laser at similar to 10-W pump power. The performance of the Q-switched fiber lasers as a function of fiber length is also analyzed. (c) 2008 Elsevier B.V. All rights reserved.
Resumo:
Demonstrations of cw lasing in Cr2+:ZnSe poly-crystal are reported. The laser consists of a 1.7-mm-thick Cr2+:ZnSe poly-crystal disc pumped by a Tm-silica double-clad fibre laser at 2050nm. Using a concave high-reflection mirror with a radius of curvature of 500mm as the rear mirror, the laser delivers up to 1030mW of radiation around 2.367 mu m.