Photoluminescence properties of a GaN0.015As0.985/GaAs single quantum well under short pulse excitation

Under short pulse laser excitation, we have observed an extra high-energy photoluminescence (PL) emission from GaNAs/GaAs single quantum wells (QWs). It dominates the PL spectra under high excitation and/or at high temperature. By measuring the PL dependence on both temperature and excitation power and by analyzing the time-resolved PL results, we have attributed the PL peak to the recombination of delocalized excitons in QWs. Furthermore, a competition process between localized and delocalized excitons is observed in the temperature-dependent PL spectra under the short pulse excitation. This competition is believed to be responsible for the temperature-induced S-shaped PL shift often observed in the disordered alloy semiconductor system under continuous-wave excitation. (C) 2001 American Institute of Physics.

Hydrostatic pressure effect on photoluminescence from a GaN0.015As0.985/GaAs quantum well

Photoluminescence from a GaN0.015As0.985/GaAs quantum well has been measured at 15 K under hydrostatic pressure up to 9 GPa. Both the emissions from the GaNAs well and GaAs barrier are observed. The GaNAs-related peak shows a much weaker pressure dependence compared to that of the GaAs band gap. A group of new peaks appear in the spectra when the pressure is beyond 2.5 GPa, which is attributed to the emissions from the N isoelectronic traps in GaAs. The pressure dependence of the GaNAs-related peaks was calculated using the two-level model with the measured pressure coefficients of the GaAs band gap and N level as fitting parameters. It is found that the calculated results deviate seriously from the experimental data. An increasing of the emission intensity and the linewidth of the GaNAs-related peaks was also observed and briefly discussed. (C) 2001 American Institute of Physics.

Optical transitions in GaNAs/GaAs single quantum well

We have investigated GaNAs/GaAs single quantum wells (SQWs) grown by molecular beam epitaxy (MBE) using photoluminescence (PL), time-resolved PL (TRPL) and photovoltaic (PV) techniques. The low temperature PL is dominated by spatially direct transitions involving electrons confined in GaNAs well and holes localized in the same GaNAs layer. This assignment was supported by PL decay time measurements and absorption line-shape analysis derived from the PV measurements. By fitting the experimental data with a simple calculation, the band offset of the GaN0.015As0.985/GaAS heterostructure was estimated, and a type II band lineup in GaN0.015As0.985/GaAs QWs was suggested. Moreover, DeltaE(C), the discontinuity of conductor band, is found to be a nonlinear function of the nitrogen (N) composition (x), and the average variation of DeltaE(C) is about 0.110eV per %N, The measured band bowing coefficient shows a strong function of x, giving an experimental support to the theoretic calculation of Wei et al [Ref.2].