Optical responses of ZnSe quantum dots in silica gel glasses

The characteristic features of the absorption and photoluminescence spectra of ZnSe quantum dots (QDs) inside a silica matrix derived from a sol-gel method were studied at room temperature. Compared with the bulk materials, the absorption edges of ZnSe QDs in silica gel glass were shifted to higher energies and the spectra exhibited the discrete excitonic features due to the quantum confinement effects. Besides the band-edge emission, photoluminescence at ultraviolet excitation also showed the emissions related to the higher excitonic states. (C) 2004 Elsevier B.V. All rights reserved.

Solid-core tellurite glass fiber for infrared and nonlinear applications

By optimizing glass composition and using a multistage dehydration process, a ternary 80TeO(2)-10ZnO-10Na(2)O glass is obtained that shows excellent transparency in the wavelength range from 0.38 mu m up to 6.10 mu m. Based on this optimized composition, we report on the fabrication of a single-mode solid-core tellurite glass fiber with large mode area of 103 mu m(2) and low loss of 0.24 similar to 0.7 dB/m at 1550 nm. By using the continuous-wave self-phase modulation method, the non-resonant nonlinear refractive index n(2) and the effective nonlinear parameter gamma of this made tellurite glass fiber were estimated to be 3.8x10(-1)9 m(2)/W and 10.6 W-1.m(-1) at 1550 nm, respectively. (C) 2009 Optical Society of America

Tellurium enhanced non-resonant third-order optical nonlinearity in a germano-silicate optical fiber

碲掺杂的高非线性石英光纤

All-optical switching application of germano-silicate optical fiber incorporated with Ag nanocrystals

银纳米晶体掺杂的高非线性石英光纤的全光转换应用

Broad-spectrum and long-lifetime emissions of Nd3+ ions in lead fluorosilicate glass

A novel Nd3+-doped lead fluorosilicate glass (NPS glass) is prepared by a two-step melting process. Based on the absorption spectrum a Judd-Ofelt theory analysis is made. The emission line width of NPS glass is 44.2nm. The fluorescence decay lifetime of the 4F3/2 level is 586±20μsec, and the stimulated emission cross-section is 0.87×10-20cm2 at 1056nm. A laser oscillation is occurred at 1062nm when pumped by 808nm Diode Laser. The slope efficiency is 23.7% with a 415mJ threshold. It is supposed that NPS glass is a good candidate for using in ultra-short pulse generation and amplification by the broad emission bandwidth and long fluorescence lifetime.

Formation and Properties of a Novel Heavy-Metal Chalcogenide Glass Doped with a High Dysprosium Concentration

A novel heavy-metal chalcogenide glass doped with a high dysprosium ion (Dy(3+)) concentration was prepared by the well-established melt-quenching technique from high-purity elements. The results show that when Cadmium (Cd) is introduced into chalcogenide glass, the concentration of Dy(3+) ions doped in GeGaCdS glasses is markedly increased, the thermodynamic performance improves, and the difference between T(g) and T(x) is >120 degrees C. The Vickers microhardness is also modified greatly, about 245 kgf/mm(2). The optical spectra indicate that all absorption and emission bands of Dy(3+) are clearly observed and red-shifted with increasing Dy(3+) concentration.

Ultra-dry oxygen atmosphere to protect tellurite glass fiber from surface crystallization

In this study we report on surface crystallization phenomena and propose a solution for the fabrication of long and robust tellurite glass fibers. The bulk tellurite glasses of interest were prepared by melting and quenching techniques. Tellurite glass preforms and fibers were fabricated by suction casting and rod-in-tube drawing methods, respectively. The surfaces of the tellurite bulk glass samples and of the drawn fibers prepared under different controlled atmospheres were examined by X-ray diffraction. When the tellurite glass fibers were drawn in ambient air containing water vapor, four primary kinds of small crystals were found to appear on the fiber surface, alpha-TeO(2), gamma-TeO(2), Zn(2)Te(3)O(8) and Na(2)Zn(3)(CO(3))(4)center dot 3H(2)O. A mechanism for this surface crystallization is proposed and a solution described, using an ultra-dry oxygen gas atmosphere to effectively prevent surface crystallization during fiber drawing. (C) 2010 Elsevier B.V. All rights reserved.

Some new observation on the formation and optical properties of CdS clusters in zeolite-Y

CdS clusters in zeolite-Y have been prepared by the exchange of Cd2+ into the zeolite following by sulfurization with Na2S in solution. Blue-shifts from the bulk caused by quantum size effect and the change of absorption upon CdS loading are observed. Two absorption bands are detected for one of the sample and are assigned to the 1s-1s band and exciton transition, respectively. The exciton feature is more pronounced in the excitation spectrum than in the absorption spectrum, and the luminescence excited at the exciton band is stronger than that at the 1s-1s band. Copyright (C) 1996 Elsevier Science Ltd

Thermally Stable Guest-Host Polyetherketone Poled Polymer for Electro-Optical Applications

The high glass transition temperature polymer polyetherketone doped with disperse red 13 (DR13/PEK-c) has been prepared by the spin-coating method. Through in situ second-harmonic generation, the corona poling temperature was optimized by measuring the temperature dependence of the in situ second-harmonic generation signal intensity under the poling electric field. The linear electro-optic coefficients of the poled polymer films have been determined at 632.8 nm by using a simple interferometric technique. The polymer system was measured after 13 000 h, and found that it remained at 80% of its initial value.