Facile synthesis and photoluminescent properties of redispersible CeF3, CeF3 : Tb3+, and CeF3 : Tb3+/LaF3 (core/shell) nanoparticles

CeF3, CeF3:Tb3+, and CeF3:Tb3+/LaF3 (core/shell) nanoparticles were prepared by the polyol method and characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), X-ray photoelectron spectra (XPS), UV-vis absorption spectra, photoluminescence (PL) spectra, and lifetimes. The results of XRD indicate that the obtained CeF3, CeF3:Tb3+, and CeF3:Tb3+/LaF3 (core/shell) nanoparticles crystallized well at 200 degrees C in diethylene glycol (DEG) with a hexagonal structure. The TEM images illustrate that the CeF3 and CeF3:Tb3+ nanoparticles are spherical with a mean diameter of 7 nm. The growth of the LaF3 shell around the CeF3:Tb3+ core nanoparticles resulted in an increase of the average size (11 nm) of the nanopaticles as well as in a broadening of their size distribution. These nanocrystals can be well-dispersed in ethanol to form clear colloidal solutions. The colloidal solutions of CeF3 and CeF3:Tb3+ show the characteristic emission of Ce3+ 5d-4f (320 nm) and Tb3+ D-5(4)-F-7(J) (J = 6-3, with D-5(4)-F-7(5) green emission at 542 nm as the strongest one) transitions, respectively. The emission intensity and lifetime of the CeF3:Tb3+/LaF3 (core/shell) nanoparticles increased with respect to those of CeF3:Tb3+ core particles.

Systematic synthesis and characterization of single-crystal lanthanide phenylphosphonate nanorods

Using low-temperature hydrothermal methods, nanoscale lanthanide phenylphosphonates species with different morphologies, namely, nanoparticles and nanorods, have been systematically synthesized. The possible growth mechanism of these nanorods was discussed. X-ray diffraction, transmission electron microscopy, electron diffraction, and photoluminescence spectra were used to characterize these materials. The photoluminescent properties of EU(O3PC6H5)(HO3PC6H5) and La0.91EU0.09(O3PC6H5)(HO3PC6H5) nanorods were discussed.

Morphologies in solvent-annealed thin films of symmetric diblock copolymer

We have systematically studied the thin film morphologies of symmetric poly(styrene)-block-poly(methyl methacrylate) (PS-b-PMMA) diblock copolymer after annealing to solvents with varying selectivity. Upon neutral solvent vapor annealing, terraced morphology is observed without any lateral structures on the surfaces. When using PS-selective solvent annealing, the film exhibits macroscopically flat with a disordered micellar structure. While PMMA-selective solvent annealing leads to the dewetting of the film with fractal-like holes, with highly ordered nanoscale depressions in the region of undewetted films. In addition, when decreasing the swelling degree of the film in the case of PMMA-selective solvent annealing, hills and valleys are observed with the coexistence of highly ordered nanoscale spheres and stripes on the surface, in contrast to the case of higher swelling degree. The differences are explained qualitatively on the basis of polymer-solvent interaction parameters of the different components.

The first synthesis of a water-soluble alpha-cyclodextrin/C-60 supramolecular complex using anionic C-60 as a building block

A novel supramolecular inclusion complex of alpha-CD/C-60 was synthesized using anionic C-60. The reaction progress was monitored in situ by visible and near-IR spectroscopy. The obtained complex was characterized by UV-vis, C-13 NMR, MALDI-TOF, and cyclic voltammetry. The induction and dispersion forces are considered to be the major driving forces for the formation of a resulting alpha-CD/C-60(.-) inclusion complex.

Spectral properties of rare-earth ions in nanocrystalline YAG : Re (Re = Ce3+, Pr3+, Tb3+)

Bulk and nanoscale powders of YAG:Re (Re = Ce, Pr, Tb) were synthesized by solid-state and sol-gel method. The changes of spectra and energy level were studied. Compared with the bulk YAG:Re (Re = Ce, Pr, Tb) crystals, the lattice parameter of YAG:Re (Re = Ce, Pr, Tb) nanocrystals decreases. It is also found that the excitation peaks of 5d energy levels shift in nanocrystals. The physical reason for spectral and energy level changes is a comprehensive result from the shift of energy centroid of the 5d orbit, the Coulomb interaction between 4f and 5d electrons and the crystal field splitting of the 5d energy level.

Site-selective self-assembly of MPA-bridged CuHCF multilayers on APTMS-supported gold colloid electrodes

(3-Aminopropyl)trimethoxysilane (APTMS)-supported gold colloid electrode was constructed by virtue of a recently developed solution-based self-assembly strategy. The preparing procedure of 3-mercaptopropionic acid (MPA)-bridged copper hexacyanoferrate (CuHCF) multilayers on a planar macroelectrode (Bharathi et al. Langmuir 2001, 17, 7468) was copied to the as-prepared colloid electrode. The optical spectra, atomic force microscopy, and electrochemistry demonstrate successful copy of the multilayer system on a macroelectrode to the as-prepared colloid electrode. Remarkably, it was found that multilayer growth is highly selective to the nanoscale sites where gold nanoparticles are immobilized, and multilayer growth does not take place on the sites without nanoparticles. Interestingly, a preliminary electrochemical investigation indicates that electrochemical properties of multilayers systems on the colloid electrode are different from their counterparts on a planar macroelectrode, which might be due to high curvature effects of the gold nanoparticles. This indicates a different motif of multilayers on the colloid electrode from that on a planar macroelectrode.

Effects of surfactant loadings on the dispersion of clays in maleated polypropylene

A series of organically modified clays (OMCs) with a surfactant loading range from 0.625 to 2.5 times the cation exchange capacity (CEC) were melt-mixed with maleated polypropylene (PPMA). Wide-angle X-ray diffraction and transmission electron microscopy results of these narrocomposites show that dispersion of clays becomes unfavorable in the PPMA matrix during melt intercalation as the surfactant loading increases in the process of modifying clays, though larger interlayer distances are obtained in their corresponding OMCs. It is even important that clays uniformly disperse at the nanoscale level in the PPMA matrix when the surfactant loadings are below the CEC, which implies that incomplete exchange of inorganic cations in the process of modifying clay benefits the dispersion of clays in the PPMA matrix.

Preparation and properties of polyethylene/montmorillonite nanocomposites by in situ polymerization

Polyethylene (PE)/montmorillonite (MMT) nanocomposites were prepared by in situ coordination polymerization using a MMT/MgCl2/TiCl4 catalyst activated by AI(Et),. The catalyst was prepared by first diffusing MgCl2 into the swollen MMT layers, followed by loading TiCl4 on the inner/outer layer surfaces of MMT where MgCl2 was already deposited. The intercalation of MMT layers by MgCl2 and TiCl, was demonstrated by the enlarged interlayer spacing determined by WAXD. The nanoscale dispersion of MMT layers in the polyethylene matrix was characterized by WAXD and TEM. As a consequence, the crystallinity of the nanocomposite decreased sharply, whereas the tensile strength was significantly improved compared to that of virgin polyethylene of comparable molecular weight. The confinement of the nanodispersed MMT layers to molecular chain and the strong interaction between the nanoscale MMT layers and the resin matrix were thought to account for the decrease of crystallinity and the remarkable enhancement of strength.

Conductive hybrids from water-borne conductive polyaniline and (3-glycidoxypropyl)trimethoxysilane

Free-standing conductive films of organic-inorganic hybrids were prepared employing the sol-gel process of (3-glycidoxypropyl)trimethoxysilane (GPTMS) and water-borne conductive polyaniline (cPANI) in water/ethanol solution. The hybrids displayed a percolation threshold for electrical conductivity at a volume fraction of 2.1% polyaniline (PANI); the maximum conductivity of the hybrids reached 0.6 S/cm. GPTMS showed good compatibility with water-borne cPANI during the sol-gel process, and freestanding conductive films were obtained at room temperature. Transmission electron microscopy images of the hybrids indicated that the cPANI was dispersed in the inorganic phase in nanoscale. Because of good confinement of cPANI chains in the inorganic network, water resistance of the hybrid films was significantly improved compared with that of pure cPANI; the electrical conductivity of the films kept stable for 6-7 days soaking in water, whereas it decreased sharply for 1 day soaking for the pure cPANI.

Gold nanoparticles as fine tuners of electrochemical properties of the electrode/solution interface

Recently, a novel approach for preparing SERS and SPR substrates was developed, which indicates a potential application in tailoring the interfacial structure of an electrode surface. In this study, (3-mercaptopropyl)trimethoxysilane (MPTMS) was selected as a polymeric adhesive layer, and a low concentration of colloid Au solution was used to achieve a more accurate control over interface morphology at nanoscale dimensions due to slow self-assembling kinetics of gold nanoparticle's. Subsequent seeding growth of these MPTMS-supported submonolayers of gold nanoparticles in Au3+/NH2OH aqueous solution enlarges particle size and eventually results in the generation of conductive gold films (similar to previous (3-aminopropyl)trimethoxysilane-supported gold films). Such tunable interface structure was evaluated by atomic force microscopy (AFM). Also, ac impedance spectroscopy (ACIS) and cyclic voltammograms were performed to evaluate electrochemical properties of the as-prepared interfaces by using Fe(CN)(6) (3-/4-) couples as a probe. Furthermore, relevant theories of microarray electrodes were introduced into this study to explain the highly tunable electrochemical properties of the as-prepared interfaces. As a result, it is concluded that the electrochemical properties toward Fe(CN)(6) (3-/4-) couples are highly dependent on the active nanoelectrode (nanoparticles) area fraction and nanoparticles are fine-tuners of interfacial properties because the number density. (numbers/unit area) and size of nanoparticles are highly tunable by self-assembling and seeding growth time scale control. This is in agreement with the theoretical expectations for a microarray electrode if a single nanoparticle tethered to a blocking SAM is taken as a nanoelectrode and 2-D nanoparticle assemblies are taken as nanoelectrode arrays.

Photoelectrochemical reduction of CO2 mediated with methylviologen at roughened silver electrodes

The photoelectrocatalytic effect for the reduction of CO2 mediated with methylviologen (MV) was studied at mercury, polished silver and roughened silver electrodes using electrochemical and surface-enhanced Raman scattering (SERS) techniques. A large photoelectrocatalytic effect for the reduction of CO2 in the presence of MV was observed at the roughened silver electrode, whereas there was only a very small photoelectrocatalytic current at a more negative potential on mercury and polished silver electrodes. The SERS spectra of MV in the presence and absence of CO2, along with the electrochemical results, demonstrate that the surface adsorbed complexes, MV+ -Ag and MV0-Ag, played a role as the mediator for photoinduced electron transfer to CO2 in the solution. The results also suggest that the surface plasmon resonance of the nanoscale silver particle contributes to the overall photoelectrocatalytic effect on a roughened silver electrode.

Nanostructured hybrid organic-inorganic lanthanide complex films produced in situ via a sol-gel approach

Communication: Nanostructural hybrid organic-inorganic lanthanide complex films were prepared in situ by use of a novel sol-gel precursor containing pendant triethoxy-silyl and carboxyl groups (see Figure). The resulting transparent and crack-free films gave rise to strong red or green emission, even at low lanthanide ion concentration. Phase separation and lanthanide ion aggregation were controlled at the nanoscale.

Ultrathin multilayer films incorporating Keggin-type heteropolyanion clusters

Two new ultrathin multiplayer films have been successfully prepared fi-om Keggin-type heteropoly acids H-4[SiW12O40] and H-3[PMo12O40] with polyelectrolytes PEI, PSS, and PAH, using the electrostatic layer-by-layer self-assembly, technique. The XR results reveal their film thickness at nanoscale (similar to 20 nm). According to the AFM images, it is believed that the surface roughness (rough degree of film surface) of the polyelectrolyte-polyoxometalate film greatly depends on the kind of polyoxometalates.

Preparation of poly(4-vinylpyridine)/silica hybrids supported cyclopentadienyltitanium trichloride (CpTiCl3) catalyst and styrene polymerization

Poly(4 - vinylpyridine)/silica( PVP/SiO2) organic - inorganic nanoscale hybrid was prepared using sol - gel method, in which PVP was used as an organic component and TEOS as a SiO2 precusor, This hybrid was used as CpTiCl3 support. The XPS and IR measurements showed that two kinds of catalytic active site were formed through analyzing the interaction mode between support and CpTiCl3. The results of styrene polymerization showed that syndiotactic was the highest at 50 degreesC. The catalytic activity was 1.09 x 10(6) g PS/ (mol Ti . h) at 70 degreesC when n(Al)/n(Ti) = 1500. GPC results showed a bimodal molecular weight distribution.

Morphology and structure of micro-fibrillar crystal of nylon 10 10

The nanoscale and microscale fibrillar crystals of nylon 10 10 were obtained by atomizing the very dilute formic acid solution. The length-diameter ratio of these fibrillar crystals increases as the concentration of the atomizing solution increases. Electron diffraction (ED) analysis showed that the hydrogen-bonded sheet in these solution-grown fibrillar crystals was imperfect and had a lower order. Both electron diffraction and characteristic morphology show that melt-crystallized fibrillar crystals always possess perfect packing order and stable structure. A rather perfect ED pattern of the triclinic form of nylon 10 10 along the [001] zone was obtained by tilting the specimen 41 degrees along the elongated direction of the crystal. Fibrillar crystals from bulk have a great tendency to aggregate with parallel packing to form crystal clusters, which look like shish kebabs in morphology. Spherulite is observed occasionally in the domains with very rich sample. (C) 2001 Elsevier Science Ltd. All rights reserved.