SYNTHESIS AND MOLECULAR-STRUCTURE OF (CH3CP)2YB.DME AND ITS CATALYTIC ACTIVITY FOR THE POLYMERIZATION OF METHYL-METHACRYLATE

The complex of (CH3Cp)2Yb . DME (DME = dimethoxyethane) has been synthesized by the reduction with metallic sodium of the corresponding chloride (CH3CP)2YbCl. (CH3CP)2Yb . DME crystallized from DME in the monoclinic space group Cm, with cell constants a = 11.068(3), b = 12.338(4), c = 12.479(4) angstrom; beta = 100.51(2)-degrees, V = 1675(l) angstrom3, and D0 = 1.66 g/cm3 for Z = 4. Least-squares refinement of 1420 unique observed reflections led to final R of 0.0487. This complex can be used as a catalyst for the polymerization of methyl methacrylate (MMA).

THE EFFECT OF MOBILITY OF MOLECULES ON RADIATION-INDUCED CHAIN SCISSION AND RACEMIZATION OF ISO-POLY(METHYL METHACRYLATE)

The radiation-induced chain-scission and racemization of isotactic poly(methylmethacrylate)(iso-PMMA) in amorphous and semi-crystalline state as well as in solution have been studied with nuclear magnetic resonance and molar mass deter-mination. It is shown that the chain-scission is dominant for iso-PMMA in dilute solution while the racemization reaction is not favorable in this case. On the contrary, the racemization is favorable when iso-PMMA was irradiated in its crystalline state while chain-scission is not. Such experimental results could be well explained by the mobility of molecules and "cage effect". The hypothesis, we proposed previously that the chain-scission, racemization and recombination are in competition and the final result depends on the state of molecular motion at which iso-PMMA was irradiated, has been verified verified once again.

THE COMPATIBILITY AND CRYSTALLIZATION OF THE MIXTURES OF POLY (TETRAHYDROFURAN-b-METHYL METHACRYLATE) DIBLOCK COPOLYMER WITH POLYVINYL CHLORIDE HOMOPOLYMER

The compatibility and crystallization behaviour of the mixtures of poly (tetrahydrofuran-methyl methacrylate) diblock copolymer (PTHF-b-PMMA) with polyvinyl chloride has been studied. We found that the compatibility of these blends, in which there is special interaction between the homopolymer and the PMMA block of the copolymer, is much better than that of the AB/A type blends; and that the crystallization rate and crystallinity of PTHF microdomain changed greatly due to the swollen by PVC homopolymer. In this paper, these changes in cryatallization are well explained according to the theories of block copolymer blends and the density gradient model presented by JIANG Ming.

STUDY ON OPTICAL-ROTATORY OF HELIX POLYMER POLY(TRIPHENYLMETHYL METHACRYLATE)

The optical rotatory of helix polymer poly(triphenylmethyl methacrylate) (PTrMA) has been studied. The specific rotation of PTrMA is related with the length of helical chain linearly, while P(n)BAR<6 and P(n)BAR greater-than-or-equal-to 15. When P(n)BAR greater-than-or-equal-to 15, [alpha]D/20 = 1.6 P(n)BAR + 290-degrees. The contribution of each repeating unit to [alpha]D/20 is 1.6-degrees. In the 300-600 nm region, the ORD of PTrMA obeys both the Drude equation and Moffitt equation. The relationship between the [alpha]D of PTrMA and the solvent, concentration and temperature has also been investigated.

DYNAMIC SCALING AND FRACTAL BEHAVIOR OF SPINODAL PHASE-SEPARATION IN POLYMER MIXTURES OF POLY(METHYL METHACRYLATE) WITH POLY(STYRENE-CO-ACRYLONITRILE)

Dynamic scaling and fractal behaviour of spinodal phase separation is studied in a binary polymer mixture of poly(methyl methacrylate) (PMMA) and poly(styrene-co-acrylonitrile) (SAN). In the later stages of spinodal phase separation, a simple dynamic scaling law was found for the scattering function S(q,t):S(q,t) approximately q(m)-3S approximately (q/q(m)). The possibility of using fractal theory to describe the complex morphology of spinodal phase separation is discussed. In phase separation, morphology exhibits strong self-similarity. The two-dimensional image obtained by optical microscopy can be analysed within the framework of fractal concepts. The results give a fractal dimension of 1.64. This implies that the fractal structure may be the reason for the dynamic scaling behaviour of the structure function.

DYNAMIC SCALING OF THE STRUCTURE-FUNCTION FOR SPINODAL DECOMPOSITION IN CRITICAL AND NONCRITICAL MIXTURES OF POLY(VINYL ACETATE) POLY(METHYL METHACRYLATE)

The dynamics of phase separation in a binary polymer blend of poly(vinyl acetate) with poly(methyl methacrylate) was investigated by using a time-resolved light-scattering technique. In the later stages of spinodal decomposition, a simple dynamic scaling law was found for the scattering function S(q, t)(S(q, t) approximately I(q, t)): S(q, t)q(m)-3 S approximately (q/q(m)). The scaling function determined experimentally was in good agreement with that predicted by Furukawa, S approximately (X) approximately X2/(3 + X8) for critical concentration, and approximately in agreement with that predicted by Furukawa, S approximately (X) approximately X2/(3 + X6) for non-critical mixtures. The light-scattering invariant shows that the later stages of the spinodal decomposition were undergoing domain ripening.

CONFORMATION OF PHENYL RINGS IN THE HELICAL CHAIN POLYMER POLY(TRIPHENYLMETHYL METHACRYLATE)

The conformation of phenyl rings in the side groups of the helical chain polymer poly(tripenyl-methyl methacrylate) (1) in solution was studied by spectroscopic methods. According to the Raman spectrum the phenyl rings of 1 and triphenylmethyl methacrylate in solution have the same depolarization ratio at 1002 cm-1. The electronic spectra (ultraviolet and fluorescence) of 1 are similar to those of model substances, except for the "red shift" of the spectra of about 5 nm. It was concluded that the phenyl rings can rotate around the phenyl-C bond.

RADIATION-INDUCED CROSS-LINKING OF POLY(METHYL METHACRYLATE)-POLY(ETHYLENE OXIDE) BLEND

Radiation-induced crosslinking of poly(methyl methacrylate) (PMMA)-poly(methylene oxide) (PEO) blends was studied. It was found that PMMA in PMMA-PEO blend can be crosslinked in the range of certain doses (1 approximately 20 x 10(4) Gy) and composition (PMMA% = 30 approximately 70) under the absence of oxygen. Moreover, it was also found that the crosslinking degree of PMMA in the blend in which the content of PMMA is 70% is the largest. The crosslinking degree of PMMA in the blend is closely related with the polymer miscibility. The crosslinking degree of the blend prepared at 60-degrees-C is far higher than one at ambient temperature.

MORPHOLOGY AND DYNAMIC MECHANICAL-PROPERTIES OF AB CROSS-LINKED POLYMERS BASED ON POLYURETHANES

Polyoxypropylene glycol (PPG) (or castor oil) and toluene diisocyanate (TDI) were mixed, and the prepolymer polyurethane (PU) (I) was formed. Vinyl-terminated polyurethane (II) was prepared from (I), and hydroxyethyl acrylate, AB crosslinked polymers (ABCPs) were synthesized from (II) and vinyl monomers such as styrene, methyl methacrylate, vinyl acetate, etc. The dynamic mechanical properties and morphology of ABCPs were measured. The ABCPs based on PPG have double glass transition temperatures (T(g)) on the sigma-vs. temperature curves. They display a two-phase morphology with plastic components forming the continous phase and PU-rich domains forming the separated phase on the electron micrographs. Irregular shapes and a highly polydisperse distribution of PU-rich domain sizes were observed. The crosslink density of ABCPs has a notable effect on the morphology and properties. The average diameter of the PU-rich domains depends on the molecular weight of prepolymer PPG. The highly crosslinked structures will produce large numbers of very small domains. ABCPs based on castor oil show a single T(g) relaxation on the dynamic mechanical spectra. The compatibility between the two components is much better in ABCPs based on castor oil than in those based on PPG, because there is a high crosslink density in the former. Comparison of the dynamic mechanical spectra of ABCP and interpenetrating networks (IPN) based on castor oil with similar crosslink density and composition imply that the two components in ABCP are compatible whereas microphase separation occurs in IPN. An improvement in the compatibility is achieved by the crosslinking between the two networks.

INVESTIGATION OF PHASE SEPARATION BEHAVIOR IN POLY (METHYL METHACRYLATE)/POLY (STYRENE-CO-ACRYLONITRILE) MIXTURES WITH PULSED NUCLEAR MAGNETIC RESONANCE

Thermally induced phase separation in the mixture of poly (methyl methacrylate) (PMMA) with poly(styrene-co-acrylonitite (SAN) has intern studied with pulsed nuclear magnetic resonance(NMR) in single spin-lattice retaxation time T-1 of the eornpatibl. mixture two T-1 corresponding to those of PM MA-rich and SAN-rich comairis. Meanwhile, both T-1 gradually changing with annealing time provides the direct evidence that the phase separation takes place with a decomposition mechanism. Diffusion coeffieient was to lac negative, indicating an uphal diffusion characteristics, The basic parameters governing its kinetics were estimated using NMR date which were in good agreement with those evaluated from time-resolved light scattering experiments for a 60/40(PMMA/SAN) mixture annealed at 180.0 degrees C.