Single crystal beta-Ga2O3: Cr grown by floating zone technique and its optical properties

beta-Ga2O3: Cr single crystals were grown by floating zone technique. Absorption spectra and fluorescence spectra were measured at room temperature. The values of field splitting parameter Dq and Racah parameter B were obtained by the peak values of absorption spectra. The value 10Dq/B=23.14 manifests that in beta-Ga2O3 crystals Cr3+ ions are influenced by low energy crystal field. After high temperature annealing in air, the Cr3+ intrinsic emission was enhanced and the green luminescence disappeared. The strong and broad 691 nm emission was obtained at 420 nm excitation due to the electron transition occurred from T-4(2) to (4)A(2). The studies manifest that the beta-Ga2O3 crystals have the potential application for tunable laser.

液相外延法制备β-BBO薄膜

采用液相外延法在掺Sr^2＋的Q—BBO（001）衬底上制备了β-BBO薄膜，研究了制备条件对薄膜质量的影响．结果表明：当生长温度为810℃时，转速为300r／min生长的外延膜具有较高的结晶质量，且随着生长时间的延长，外延膜的结晶质量有所提高．β—BBO薄膜呈C轴高度择优取向，薄膜的双晶摇摆曲线半峰宽值FWHM仅为676．6”，表明β-BBO薄膜较好的结晶质量；在不具备相位匹配的条件下，β—BBO外延膜也能够实现二次谐波输出．

导模法和温度梯度法生长r面蓝宝石(英文)

r面(0112)蓝宝石晶体可用作制备非极性GaN薄膜的衬底。采用温度梯度法(temperature gradient technique,TGT)和导模法(edge-defined film-fed crystal growth,EFG)生长了质量良好的r面蓝宝石晶体。利用双晶衍射、光学显微镜、光谱仪观察和分析了晶体的结构和缺陷。结果表明:TGT法生长的r蓝宝石晶体的双晶摇摆曲线对称性好,半高宽值仅为18 rad.s,位错密度为4×103 cm-2,透过率达83%,晶体质量好。与TGT法相比,EFG法生长的r面蓝宝石晶体的结构完整性较差,位错密度为5×105 cm-2,透过率仅为75%。但是EFG法具有晶体生长速度快,后期加工成本低的优点。

Edge-defined, film-fed growth (EFG) technique for the preparation of alpha-Al2O3 : C crystal with highly sensitive thermoluminescence response

In this work, alpha-Al2O3:C, a highly sensitive thermoluminescence dosimetry crystal, was grown by the EFG method in which a graphite heating unit and shield acted as the carbon source during the growth process. The optical, luminescent properties and dosimetric characteristics of the crystal were investigated. The as-grown crystal shows a single glow peak at 536 K, which is associated with Cr3+ ions. After annealing in H-2 at 1673 K for 80 h, the crystal shows a single glow peak at 460 K and a blue emission band at 415 nm. The thermoluminescent response of the annealed crystal shows linear-sublinear-saturation characteristics in the dose range from 5 x 10(-6) to 100 Gy.

Growth of highly sensitive thermoluminescent crystal alpha-Al2O3 : C by the temperature gradient technique

In this work, an alpha-Al2O3:C crystal with highly sensitive thermoluminescence was directly grown by the temperature gradient technique (TGT) using Al2O3 and graphite powders as raw materials. The optical and luminescent properties and the dosimetric characteristics of the crystal were investigated. An as-grown alpha-Al2O3:C crystal shows a single glow peak at 462 K and a blue emission peak at 415 nm. The thermoluminescence (TL) response of the crystal shows a linear-sublinear-saturation characteristic. In the dose range from 5 x 10(-6) to 10Gy, the alpha-Al2O3:C crystal shows excellent linearity, and saturation was observed at about 30Gy. The sensitivity of the crystal decreases as the heating rate increases. (c) 2008 Elsevier B.V. All rights reserved.