(PE-g-PB-g-PA6)接枝共聚物中PA6链段结晶行为研究

采用选择性溶剂交替抽提的方法提纯在PE-g-PB-g-MA/PA6共混物中原位生成的接枝共聚物PE-g-PB-g-PA6,通过TEM﹑XPS﹑XRD﹑DSC等方法研究了该接枝共聚物的形貌与结晶行为。结果表明,PA6链段的结晶受到相形貌和分子结构的限制,扩散速度降低,导致在通常的结晶速率条件下(10℃/min)结晶不完善。

Study of the mechanism of nanocrystalline Pb(Zr0.52Ti0.48)O-3 prepared by accelerated sol-gel process

Nanocrystalline Pb(Zr0.52Ti0.48)O-3 was prepared from lead acetate, zirconium oxynitrate and titanium tetra-n-butoxide by a sol-gel method. It is found that both the crystallization temperature of precursor PZT and PZT product size were increased with increase of V(C3H8O2)/V(H2O) ratio in solution used. At V(C3H8O2)/V(H2O) = 4.47 the gel was formed moderately quick, and the nanocrystalline PZT with uniform granularity and low crystallizing temperature could be obtained. The diameter of the final nanocrystalline was ranged 60similar to70 nm as measured by atomic force microscopy (AFM). The crystallizing temperature of the precursor PZT was 443degreesC and the crystallization reaction was completed at 500degreesC by DTA and TG. The sol-gel reaction process was monitored by FT-IR and XRD.

PB-g-PMMA核壳粒子的合成及其在PVC中的分散

聚丁二烯(PB)橡胶粒子与聚氯乙烯(PVC)不相容。采用乳液聚合手段,在聚丁二烯乳胶粒表层接枝与聚氯乙烯相容的聚甲基丙烯酸甲酯(PMMA)充当增容剂制备了聚丁二烯接枝聚甲基丙烯酸甲酯(PB g PMMA ,MB)核壳粒子。用熔融共混法制备了PVC/MB共混物。SEM照片表明,这种核壳结构的粒子在聚氯乙烯中的分散情况随着核壳比的不同而改变,当核壳质量比小于93/7时能够完全均匀地分散在PVC基体中,核壳质量比大于94/6时根本不能分散在PVC基体中,核壳质量比为93/7是粒子能否分散开的转折点。共混物的力学性能数据表明,当MB加入量改变时,共混物也存在脆韧转变点,但受MB粒子的核壳比影响。

ABS树脂合成中影响PB-g-SAN接枝共聚物接枝率的因素

采用种子乳液聚合方式 ,以 K2 S2 O8为引发剂引发聚合 ,合成了一系列 PB- g- SAN接枝共聚物。考察了引发剂用量、分子量调节剂 (TDDM)用量和橡胶 (PB)含量对 PB- g- SAN接枝共聚物接枝率的影响。并将 K2 S2 O8引发剂与氧化 -还原引发体系做了比较。结果表明 ,随着引发剂 K2 S2 O8用量逐渐增加 ,PB- g- SAN接枝共聚物的接枝率逐渐降低。引发剂用量太少时 ,不能满足聚合要求 ,PB- g- SAN接枝共聚物的接枝率也会降低。随着分子量调节剂 (TDDM)用量的增加 ,PB- g- SAN接枝共聚物的接枝率逐渐降低。随胶含量的增加 ,PB- g- SAN接枝共聚物的接枝率逐渐降低。采用氧化 -还原引发体系引发聚合有利于接枝反应的进行 ,在 PB含量相同时 ,采用氧化 -还原引发体系合成的 PB- g- SAN接枝共聚物的接枝率比采用 K2 S2 O8合成的接枝共聚物接枝率高。

Bonding and Mossbauer isomer shifts in (Tl, Pb)-1223 cuprate

By using the clinical bond theory of dielectric description, the chemical bond parameters of (Tl.Pb) - 1223 was calculated. The results show that the Sr-O, Tl-O, and Ca-O types of bond have higher ionic character and the Cu-O types of bond have more covalent, character. Mossbauer isomer shifts of Fe-57 and Sn-119 doped in (Tl, Pb) -1223 were calculated by using the chemical environmental factor, h, defined by covalency and electronic polarizability. Four valence state tin and three valence iron sites were identified ill Fe-57, and Sn-119 doped (Tl, Pb) -1223 superconductor. We conclude that all of' the Fe atoms substitute the Cu at square planar Cu (H site, whereas Sn prefers to Substitute the square pyramidal Cu (2) site.

溶胶-凝胶法制备纳米Pb(Zr_(0.52)Ti_(0.48))O_3

以醋酸铅 ,硝酸氧锆 ,钛酸四丁酯为原料用溶胶 -凝胶法制备了纳米 Pb( Zr0 .52 Ti0 .48) O3 ( PZT)。结果表明 ,随溶剂中乙二醇单甲醚与水的比例的增大 ,PZT粉体的晶化温度增高 ,晶粒的粒径尺寸也增大 ,当V( C3 H8O2 ) / V( H2 O) =4 .4 7时 ,不仅凝胶完成时间短 ,且可得到粒度分布集中、晶化温度低的 PZT粉体。用原子力显微镜测定 PZT的粒径为 6 0～ 70 nm,用 TG-DTA分析确定在 4 43℃即可发生晶化反应 ,在 5 0 0℃下结晶完善。通过对不同温度下热处理的粉体的红外光谱和 X射线衍射的分析 ,对溶胶 -凝胶法制备 PZT粉体形成钙钛矿结构的过程进行了研究。

盐酸介质中 P_(507) 萃取 Pb(Ⅱ)的平衡

通过实验，研究了２－乙基已基膦酸单（２－乙基已基）酯，在盐酸介质中萃取铅的规律和机理，为荧光级稀土生产提供了理论依据。

Preparation of Pb-Ca-Na master alloy using molten chloride salt electrolysis

An electrolysis technique for co-deposition of Ca2+ and Na+ at the liquid lead cathode was put forward. The experiment was carried out at an electrolysis temperature below 650 degrees C and had a current efficiency of 98%, which are respectively 100 similar to 300 degrees C lower and 15% similar to 30% higher than those reported both at home and abroad.

Comparative study on the doping effect of 3d elements in Bi(1.5)Pb(0.2)Sr(2)Ca(2)Cu(2.8)M(0.2)O(y) (M=Sc,Ti,V,Cr,Mn,Fe,Co,Ni, or Zn)

With XRD, R-T, and ac chi measurements a comparative study on the doping effects of 3d elements in Bi(1.5)Pb(0.2)Sr(2)Ca(2)Cu(2.8)M(0.2)O(y) (M = Sc, Ti, V, Cr, Mn, Fe, Co, Ni, or Zn) has been carried out. The effects of the former five members are significantly different, both on phase formed and on T-c, from the latter four. It seems that the effect on phase stabilization correlates with the valency of the doped cation. In connection with the instability of the 2223 phase, the correlation has been discussed.