Preparation and properties of microporous membrane from poly(vinylidene fluoride-co-tetrafluoroethylene) (F2.4) for membrane distillation

Flat-sheet microporous membranes from F2.4 for membrane distillation (MD) were prepared by phase inversion process. Dimethylacetamide (DMAC) and LiClO(4)(.)3H(2)O/trimethyl phosphate (TMP) were, respectively, used as solvent and pore-forming additives. The effects of casting solution composition, exposure time prior to coagulation and temperature of precipitation bath on F2.4 membrane structure were investigated. The morphology of resultant porous membrane was observed by scanning electron microcopy. Some natures of F2.4 porous membrane after drying in air, such as mechanical properties and hydrophobicity, were exhibited and compared with poly(vinylidene fluoride) (PVDF) membrane prepared by the same ways. Stress-at-break and strength stress of F2.4 microporous membrane are higher than that of PVDF membrane, and elongation percentage of F2.4 membrane at break is about eight-fold as great as that of PVDF membrane. Contact angle of F2.4 microporous membrane to water (86.6 +/- 0.51degrees) was also larger than that of PVDF mernbrane (80.0 +/- 0.78degrees). MD experiment was carried out using a direct contact membrane distillation (DCMD) configuration as final test to permeate performance of resultant microporous membrane.

Factors affecting pore structure and performance of poly(vinylidene fluoride-co-hexafluoro propylene) asymmetric porous membrane

Preparation of poly(vinylidene fluoride-co-hexafluoro propylene) (F2.6) flat-sheet asymmetric porous membrane has been studied for the first time. Factors affecting F2.6 membrane pore structure and permeate performance, such as macromolecule pore formers (polyethylene glycol-400, 1000, 1540, 2000 and 6000), the small molecule former (glycerol), swelling agent (trimethyl phosphate) in casting solution, precipitating bath component and temperature, exposure time and ambient humidity, were investigated in detail. Average pore radius and porosity were used to characterize F2.6 membrane structure, and respectively, determined by ultrafiltration and gravimetric method for the wet membrane. Morphology of the resultant membranes was observed by scanning electronic microscopy (SEM). Final test on permeate performance of F2.6 porous membrane was carried out by a direct contact membrane distillation (DCMD) setup. The experimental F2.6 membrane exhibits a higher distilled flux than PVDF membrane under the same operational situations. The determination of contact angle to distilled water also reveals higher hydrophobic nature than that of PVDF membrane.

Determination of Nb and Ta in Nb/Ta minerals by inductively coupled plasmas optical emission spectrometry using slurry sample introduction

The determination of Nb and Ta in Nb-Ta minerals was accomplished by slurry nebulization inductively coupled plasma optical emission spectrometry (ICP-OES), using a clog-free V-groove ceramic nebulizer. Samples were first wet-ground to appropriate particle sizes with narrow size distribution and 90% of the particles in the slurry were smaller than 2.32 mu m in diameter. Subsamples were then dispersed in pH 9 aqueous solutions, and agitated in an ultrasonic bath for 15 min prior to analysis. Due to the lack of slurry standards matching well with the samples, calibration was simply carried out using aqueous solution standards. Results were compared with those obtained from a conventional fusion decomposition procedure and acid digestion procedures and a good agreement between the measured and referred values was obtained. The technique provided a good alternative for the rapid determination of Nb and/or Ta in their corresponding minerals.

Rheological properties in blends of poly(aryl ether ether ketone) and liquid crystalline poly(aryl ether ketone)

Rheological properties of the blends of poly(aryl ether ether ketone) (PEEK) with liquid crystalline poly(aryl ether ketone) containing substituted 3-trifluoro-methylbenzene side group (F-PAEK), prepared by solution precipitation, have been investigated by rheometer. Dynamic rheological behaviors of the blends under the oscillatory shear mode are strongly dependent on blend composition. For PEEK-rich blends, the systems show flow curves similar to those of the pure PEEK, i.e., dynamic storage modulus G' is larger than dynamic loss modulus G", showing the feature of elastic fluid. For F-PAEK-rich systems, the rheological behavior of the blends has a resemblance to pure F-PAEK, i.e., G" is greater than G', showing the characteristic of viscous fluid. When the PEEK content is in the range of 50-70%, the blends exhibit an unusual rheological behavior, which is the result of phase inversion between the two components. Moreover, as a whole, the complex viscosity values of the blends are between those of two pure polymers and decrease with increasing F-PAEK content. However, at 50% weight fraction of PEEK, the viscosity-composition curves exhibit a local maximum, which may be mainly attributed to the phase separation of two components at such a composition.

Green electroluminescent device with a terbium beta-diketonate complex as emissive center

In this study, a terbium complex, Tb(acac)(3)bath (acac: acetylacetone, bath: 4,7-diphenyl-1,10-phenanthroline), was synthesized and its luminescent properties were investigated compared with the reported terbium complex, Tb(acac)(3)phen (phen: phenanthroline). When it was used as an emitting material in organic electroluminescent (EL) device, the triple-layer-type device with a structure of glass substrate/ITO (indium-tin oxide)/TPD (N,N'-diphenyl-N,N'-bis(3-methylphenyl)-1,1'-biphenyl-4,4'-diamine)/Tb(acac)(3)bath/Alq(3) (tris (8-hydroxyquinolinato) aluminum)/Al (aluminum) exhibited bright characteristic emission of terbium ion upon applying DC voltage. An apparent difference was observed between the photoluminescence spectrum and the EL spectrum. The EL device exhibited some characteristics of diode and the maximum luminance of 77 cd/m(2) was obtained at 17 V.

Rheology and morphology of reactively compatibilized PP/PA6 blends

This work aims to use the Palierne emulsion type model to describe the relationship between the rheological response to small amplitude oscillatory deformation and morphology of polypropylene/polyamide 6 (PP/PA6) blends compatibilized with maleic anhydride grafted polypropylene (PP-g-MAH). It was found that the Palierne emulsion type model could describe very well the linear viscoelastic responses of binary uncompatibilized PP/PA6 blends and failed to describe the ternary compatibilized PP/PP-g-MAH/PA6 blends. These features could be attributed to the fact that the morphology of the ternary blends was not of the emulsion type with the PA6 particles dispersed in the PP matrix but of an emulsion-in-emulsion type, i.e., PA6 particles dispersed in the PP matrix themselves contained PP or PP-g-MAH inclusions. By consideration of PP-in-PA6 particles as pure PA6 particles, where the volume fraction of the PA6 phase was increased accordingly, the Palierne emulsion type model could work very well for a ternary blending system. Preshear at low frequencies modified the morphology of both binary and ternary blends. The particles of the dispersed phase (PA6) became more uniform. These results suggested that the Palierne emulsion type model could be used to extract information on rheological properties and interfacial tension of polymer blends from known morphology and vice versa.

Determination of sulpiride by capillary electrophoresis with end-column electrogenerated chemiluminescence detection

Background: Capillary electrophoresis (CE) with tris(2,2'-bipyridyl)ruthenium(II) [Ru(bpy)(3)(2+)]-electro-generated chemiluminescence (ECL) detection is a promising method for clinical analysis. In this study, a method combining CE with Ru(bpy)(3)(2+) ECL (CE-ECL) detection that can be applied to amine-containing clinical species was developed, and the performance of CE-ECL as a quantitative method for determination of sulpiride in human plasma or urine was evaluated. Methods: Sulpiride was separated by capillary zone electrophoresis in uncoated fused-silica capillaries [510 cm x 25 mum (i.d.)] filled with phosphate buffer (pH 8.0 and a driving voltage of +15 kV, with end-column Ru(bpy)(3)(2+) ECL detection. A platinum disc electrode was used as working electrode. Sulpiride in human plasma or urine samples (100 muL) was extracted by a double-step liquid-liquid extraction procedure, dried under nitrogen at 35 degreesC in a water bath, and reconstituted with 100 muL of filtered water. The extraction solvent was ethyl acetate-dichloromethane (5:1 by volume). Results: Under optimum conditions (pH 8.0 phosphate buffer, injection for 6 s at 10 kV, and +1.2 V as detection potential), separation of sulpiride was accomplished within 4 min. The calibration curve was linear over a concentration range of 0.05-25.0 mumol/L, and the limit of detection was 2.9 x 10(-8) mol/L for sulpiride. Intra- and interday CVs for ECL intensities were <6%. Extraction recoveries of sulpiride were 95.6-101% with CVs of 2.9-6.0%. The method was,clinically validated for patient plasma and urine samples. Conclusions: CE combined with Ru(bpy)(3)(2+) ECL is reproducible, precise, selective, and enables the analysis of sulpiride in human plasma and urine. It thus is of value for rapid and efficient analysis of amine-containing analytes of clinical interest.

Preparation and properties of conductive polyaniline/poly-omega-aminoundecanoyle fibers

Historically, polyaniline (PANI) had been considered an intractable material, but it can be dissolved in some solvents. Therefore, it could be processed into films or fibers. A process of preparing a blend of conductive fibers of PANI/poly-omega-aminoun-decanoyle (PA11) is described in this paper. PANI in the emeraldine base was blended with PA11 in concentrated sulfuric acid (c-H,SO,) to form a spinning dope solution. This solution was used to spin conductive PANI/PA11 fibers by wet-spinning technology. As-spun fibers were obtained by spinning the dopes into coagulation bath water or diluted acid and drawn fibers were obtained by drawing the as-spun fibers in warm drawing bath water. A scanning electron microscope was employed to study the effect of the acid concentration in the coagulation bath on the microstructure of as-spun fibers. The results showed that the coagulating rate of as-spun fibers was reduced and the size of pore shrank with an increase in the acid concentration in the coagulation bath. The weight fraction of PANI in the dope solution also had an influence on the microstructure of as-spun fibers. The microstructure of as-spun fibers had an influence on the drawing process and on the mechanical properties of the drawn fibers. Meanwhile, the electrically conductive property of the drawn fibers with different percentage of PANI was measured.

Effect of physical aging on the microstructure and the crystallization of amorphous poly(aryl ether ether ketone ketone) (PEEKK)

Physical aging of poly(aryl ether ether ketone ketone) (PEEKK) has been investigated. Heat flow responses were measured after annealing the amorphous samples obtained by quenching the melt into an ice-water bath close to, but below, the glass transition temperature. The extent of aging is related to the supercooling from the glass transition temperature and to the aging time. The activation energy of the aging process, which was estimated by a Williams-Watt expression, is similar in magnitude to that obtained for the cold crystallization for the aged samples. The quenched glass is a metastable glass. The conformation of molecular chains rearranges with physical aging which results in the formation of a denser packing in the amorphous phase. The dense amorphous phase may form an initial nucleus for crystallization. Isothermal cold crystallization of the aged samples was carried out. The Avrami equation was used to determine the kinetic parameters, and the Avrami constant n is about 2. An Arrhenius expression was used to evaluate the activation energy of relaxation upon physical aging and the activation energy of transportation upon isothermal crystallization. The activation energy of relaxation is similar in magnitude to that of crystallization for aged samples. Results obtained are interpreted as kinetic effects associated with the glass formation process.

Physical aging and crystallization of amorphous poly(aryl ether ether ketone ketone)

Physical aging of poly(aryl ether ether ketone ketone) (PEEKK) was investigated. Heat flow responses were measured after annealing the amorphous samples that were obtained by quenching the melt into an ice-water bath at just below the glass transition temperature. Isothermal cold crystallization of the aged samples was carried out. The Avrami equation was used to determine the kinetic parameters, and the Avrami constant it is about 2. An Arrhenius form was used to evaluate the relaxation activation energy of physical aging and the transport activation energy of isothermal crystallization. The activation energy of physical aging was similar in magnitude to that observed for the temperature dependence of crystallization under conditions of transportation control. Results obtained were interpreted as purely kinetic effects associated with the glass formation process. (C) 1998 John Wiley & Sons, Inc.

The fabrication of dipped CdS and sputtered ITO thin films for photovoltaic solar cells

Stable bilayer thin films of indium tin oxide (ITO) on CdS and CdS on ITO were formed for the window material of solar cells by chemical bath and sputtering methods. Scanning electron microscopy and X-ray diffraction studies have shown that both the ITO and CdS films are continuous, homogeneous, with high compactness. Measurement of the CdS film thickness across the 2 x 4 cm(2) reveals the good uniformity of these films. Four-point probe measurements show that the resistivity of a CdS film on an ITO surface is much better than that of the single CdS film The thermal stability of an ITO/CdS bilayer, interfacial reaction and optical transmittance were investigated at different annealing temperatures and environments (air, vacuum and N-2 + H-2). The results showed that the ITO/CdS bilayer film is a good window material for the CuInSe2 and CdTe cells. It is a simple method using a small amount of the cadmium compound.

Relationship between the structure and catalytic activity of La2-xSrxNiO4-lambda(0<=x<=1) mixed oxides for NH3 oxidation

A series of samples having the composition of La2-xSrxNiO4(0 less than or equal to x less than or equal to 1) were prepared and used as catalysts for NH3 oxidation. It was found that the La and oxygen vacancies exist in the La2-xSrxNiO4-lambda(0 less than or equal to x less than or equal to 1). The unit cell volume decreases with the increase of x. For bath c and a parameters there appeared a turning point at x = 0.5. Doping with a lower valence cation Sr2+ in the case of La2NiO4 resulted in an increase of Ni3+, consequently the formation of oxygen vacancies, the increase of reducing ability and the increase of catalytic activity. In the oxygen TPD of La2-xSrxNiO4(0 less than or equal to x less than or equal to 1) appeared three peaks, the alpha' peak at about 400K was attributed to the surplus oxygen desorption, the a peak at 700K which approaches to a maxium at x = 0.6 was attributed to the oxygen adsorbed at oxygen vacancies. The beta peak at about 1000K which depends closely on the x and favors the catalytic activity was attributed to the reduction of Ni3+. The catalytic activity of La-2-x SrxNiO4 mixed oxides in the NH3 oxidation in general could be attributed to the extent of the redox reaction: 2Ni(2+) + O-2 + V-0(..) reversible arrow 2Ni(3+) + 20(-) where V-0(..) representes the oxygen vacancies and O- the oxygen species adsorbed at the vacancies.

ELECTRODEPOSITION OF POLYCRYSTALLINE CD-RICH HG1-XCDXTE AND PHOTOELECTRO-CHEMICAL BEHAVIOR OF HG0.09CD0.91TE THIN-FILM

Electrodeposition process of polycrystalline Cd-rich Hg_(1-z)Cd_xTe (x>0.5) in acidic bath of CdSO_4+HTeO_2~+HgCl_2 was investigated. The simultaneous electrodeposition technique of three kinds of ions at the same potential has been achieved. The XRD, SEM and EDAX analysis of the thin film electrodeposited on titanium substrate showed a typical cubic zinc blende polycrystalline structure and homogeneous dispersion. The photoelectrochemical behavior of (1-x)=0.09 polycrystalline thin film in a polysulfide re...

XPS STUDY OF CORROSION BEHAVIOUR OF TITANIUM IN H2C2O4 SOLUTION

The corrosion behaviour of titanium substance and the XPS characterization of Ti surface in the H2C2O4 solution have been first studied by X-ray photoelectron spectroscopy, The experimental results show that there am mile Ti-2 and Ti2+ on sample surface in 10% H2C2O4 solution for two boars corrosion at 80 degrees C, but if corrosion is extended to 4 hones, the surface composition is mainly TiO2 with a small amount of Ti2+. This result corresponds to the structure of TiH1.642 composion in sample surface found by XRD analysis. Since bath TiO2 and the surface coating RuO2 are of Gald-Redstone structure, therefore electrode materials of Ti-Ru are stable in chemical industry.

Isolation and analysis of the vaccine potential of an attenuated Edwardsiella tarda strain

Edwardsiella tarda is an important aquaculture pathogen that can infect a wide range of marine and freshwater fish worldwide. In this study, a modified E. tarda strain, TX5RM, was selected by multiple passages of the pathogenic E. tarda strain TX5 on growth medium containing the antibiotic rifampicin. Compared to the wild type strain, the rifampicin-resistant mutant TX5RM (i) shows drastically increased median lethal dose and reduced capacity to disseminate in and colonize fish tissues and blood; (ii) exhibits slower growth rates when cultured in rich medium or under conditions of iron depletion; and (iii) differs in the production profile of whole-cell proteins. The immunoprotective potential of TX5RM was examined in a Japanese flounder (Paralichthys olivaceus) model as a vaccine delivered via intraperitoneal injection, oral feeding, bath immersion, and oral feeding plus immersion. All the vaccination trials, except those of injection, were performed with a booster at 3-week after the first vaccination. The results showed that TX5RM administered via all four approaches produced significant protection, with the highest protection levels observed with TX5RM administered via oral feeding plus immersion, which were, in terms of relative percent of survival (RPS), 80.6% and 69.4% at 5- and 8-week post-vaccination, respectively. Comparable levels of specific serum antibody production were induced by TX5RM-vaccinated via different routes. Microbiological analyses showed that TX5RM was recovered from the gut, liver, and spleen of the fish at 1-10 days post-oral vaccination and from the spleen, liver, kidney, and blood of the fish at 1-14 days post-immersion vaccination. Taken together, these results indicate that TX5RM is an attenuated E. tarda strain with good vaccine potential and that a combination of oral and immersion vaccinations may be a good choice for the administration of live attenuated vaccines. (C) 2010 Elsevier Ltd. All rights reserved.