MECHANICAL-PROPERTIES OF PHENOLPHTHALEIN POLYETHER KETONE - YIELD STRESS, YOUNGS MODULUS, AND FRACTURE-TOUGHNESS

A series of tensile and three-point bending studies was conducted at various temperatures and loading rates using phenolphthalein polyether ketone (PEK-C). Yield stress, Young's modulus, fracture toughness, and crack opening displacement data were obtained for various conditions. In general, both yield stress and Young's modulus increase with decreasing temperature. However, the relationships between fracture toughness, loading rate, and temperature are very complex. This behavior is due to the simultaneous intersection of viscoelasticity and localized plastic deformation. The increased yield stress is the main factor contributing to the reduction in fracture toughness and crack opening displacement. The relationship between fracture toughness and yield stress are discussed. (C) 1995 John Wiley and Sons, Inc.

TEMPERATURE EFFECT ON IMPACT FRACTURE-TOUGHNESS AND FRACTURE MECHANISM OF PHENOLPHTHALEIN POLY(ETHER KETONE)

Phenolphthalein poly(ether ketone) (PEK-C) was tested using an instrumented impact tester to determine the temperature effect on the fracture toughness K-c and critical strain energy release rate G(c). Two different mechanisms, namely the relaxation processes and thermal blunting of the crack tip were used to explain the temperature effect on the fracture toughness. Examination of the fracture surfaces revealed the presence of crack growth bands. It is suggested that these bands are the consequence of variations in crack growth along crazes that are formed in the crack tip stress field. As the crack propagates, the stress is relaxed locally, decreasing the growth rate allowing a new bundle of crazes to nucleate along which the crack advances.

COMPARISON OF THE CRACK-GROWTH METHOD AND THE CRACK STRESS WHITENING ZONE METHOD FOR THE FRACTURE-TOUGHNESS DETERMINATION OF PHENOLPHTHALEIN POLY(ETHER KETONE)

Fracture toughness values of phenolphthalein poly(ether ketone) (PEK-C) at 190 degrees C were determined by two different methods, i. e. the conventional crack growth method and the crack stress whitening zone method, which show consistent results. This indicates that the crack stress whitening zone method can be used to determine the crack initiation of some polymers for which the blunting line concept is unsuitable.

THE FRACTURE-BEHAVIOR OF PHENOLPHTHALEIN POLYETHER ETHER KETONE AT ELEVATED-TEMPERATURE FOR LONG TERMS

The fracture behavior of phenolphthalein polyether-ether ketone (PEK-C) affected by physical aging at 200 degrees C was studied by tensile experiments, scanning electron microscopy, and differential scanning calorimetry observations. The ductile-brittle fracture transition (DBT) caused by physical aging can be considered as a competition between fracture mechanisms of crazing and shear yielding. The aging time required for the DBT is found to be around 400 h, based on the morphological studies and tensile experiments. The shear yielding component of the mechanical deformation could erase the aging effect, thus a deaging phenomenon occurs. We found that the deaging phenomenon has an intrinsic relationship with the extent of aging in the specimen and as a result of the fracture behavior. (C) 1995 John Wiley and Sons, Inc.

YIELD BEHAVIOR AND VISCOELASTIC INTERPRETATION BY ACTIVATION VOLUMEN OF PHENOLPHTHALEIN POLYETHER KETONE

Phenolphthalein polyether ketone (PEK-C) exhibits a marked tensile yield behaviour. The yield stress depends on strain rate and the activation volume V could be evaluated from the data of the yield stress. From the creep and stress relaxation behaviour,

TENSILE YIELD IN PHENOLPHTHALEIN POLYETHER KETONE

Uniaxial tension tests to the yield point were performed on phenolphthalein polyether ketone (PEK-C) from room temperature to near the glass transition temperature (T-g) at a constant rate of 0.02 min(-1). At room temperature, some measurements were also

J-INTEGRAL STUDIES OF CRACK INITIATION AND CRACK TIP-BLUNTING OF PHENOLPHTHALEIN POLYETHER KETONE

The J-integral is applied to characterize the fracture initiation of phenolphthalein polyether ketone (PEK-C) for which the concepts of linear elastic fracture mechanics (LEFM) are inapplicable at high temperatures for reasonably-sized specimens due to ex

TEMPERATURE RATE DEPENDENCE OF YIELD AND FRACTURE-BEHAVIOR OF PHENOLPHTHALEIN POLY(ETHER KETONE)

The rate/temperature dependence of yield stress, tensile modulus and crack opening displacement of phenolphthalein poly(ether ketone) (PEK-C) has been investigated. The rate/temperature dependence of crack opening displacement and the correlation establis

DUCTILE TEARING INSTABILITY IN PHENOLPHTHALEIN POLY(ETHER KETONE)

Phenolphthalein poly (ether ketone) (PEK-C) [GRAPHICS] can fail by tearing instability when the elastic contraction is greater than the plastic extension due to crack growth. Tearing instability (TIS) theory developed by Paris and c

TENSILE PROPERTIES OF BLENDS OF PHENOLPHTHALEIN POLY(ETHER ETHER KETONE) WITH A POLY(ETHER IMIDE)

Blends of phenolphthalein poly(ether ether ketone) (PEK-C) with a poly(ether imide) (PEI) in various proportions were prepared by the coprecipitation method. Mechanical properties and morphology of the blends were studied using tensile tests and scanning electron microscopy (SEM). It was found that the tensile moduli exhibit positive deviations from simple additivity. Marked positive deviations were also observed for ultimate strength. These results suggest that the PEI/PEK-C blends are mechanically compatible. SEM study shows no evidence of phase separation, supporting the idea that the blends are compatible.

PHASE-SEPARATION IN ANHYDRIDE-CURED EPOXY-RESIN CONTAINING PHENOLPHTHALEIN POLY(ETHER ETHER KETONE)

Dynamic mechanical analysis and scanning electron microscopy were used to study phase separation of three blends of anhydride-cure bisphenol-A-type epoxy resin with phenolphthalein poly(ether ether ketone). Phase separation was observed for all the blends. The overall compatibility and the resulting morphology of the cured blends are dependent on the choice of cure agent. The phenomena have been discussed from the points of view of both thermodynamics and kinetics. The effects of the choice of hardener on phase separation are considered to be primarily due to differences between the chemical natures of the hardeners.

CRYSTALLIZATION OF POLY(ARYL-ETHER-ETHER-KETONE)S BLENDS

The crystallization and melting behaviour of poly(aryl-ether-ether-ketone) (PEEK) in blends with another polymer of the same family containing a bulky pendant phenolphthalein group (PEK-C) have been investigated by thermal methods. The small interaction energy density of the polymer pair (B = -8.99 J/cm3), evaluated from equilibrium melting point depression, is consistent with the T(g) data that indicate partial miscibility in the melt. Two conjugated phases are in equilibrium at 430-degrees-C: one is crystallizable and contains about 35 wt% of PEK-C; the other, containing only 15 wt% of PEEK, does not form crystals upon cooling and it interferes with the development of spherulites in the sample. The analysis of kinetic data according to nucleation theories shows that crystallization of PEEK in the explored temperature range takes place in Regime III and that a transition to Regime II might be a consequence of an increase in the amount of non-crystallizable molecules in the PEEK-rich phase. A composition independent value of the end surface free energy of PEEK lamellae has been derived from kinetic data (sigma-e = 40 +/- 4 erg/cm2) in excellent agreement with previous thermodynamic estimates. A new value for the equilibrium melting temperature of PEEK (T(m)-degrees = 639 K) has been obtained; it is about 30-degrees-C lower than the commonly accepted value and it explains better the "memory effect" in the crystallization from the melt of this high performance polymer.

BLENDS OF PHENOLPHTHALEIN POLY(ETHER ETHER KETONE) WITH PHENOXY AND EPOXY-RESIN

The properties of miscible phenolphthalein poly(ether ether ketone)/phenoxy (PEK-C/phenoxy) blends have been measured by dynamic mechanical analysis and tensile testing. The blends were found to have single glass transition temperatures (T(g)) that vary continuously with composition. The tensile moduli exhibit positive deviations from simple additivity. Marked positive deviations were also observed for tensile strength. The tensile strengths of the 90/10 and 75/25 PEK-C/phenoxy blends are higher than those of both the pure components. Embrittlement, or transition from the brittle to the ductile mode of failure, occurs in the composition range of 50-25 wt% PEK-C. These observations suggest that mixing on the segmental level has occurred and that there is enough interaction between the components to decrease its internal mobility significantly. PEK-C was also found to be miscible with the epoxy monomer, diglycidyl ether of bisphenol A (DGEBA), as shown by the existence of a single glass transition temperature (T(g)) within the whole composition range. Miscibility between PEK-C and DGEBA could be considered to be due mainly to entropy. However, PEK-C was judged to be immiscible with the diaminodiphenylmethane-curved epoxy resin (DDM-cured ER). It was observed that the PEK-C/ER blends have two T(g), which remain invariant with composition and are almost the same as those of the pure components, respectively. Scanning electron microscopy showed that the PEK-C/ER blends have a two-phase structure. The different miscibility with PEK-C between DGEBA and the DDM-cured ER is considered to be due to the dramatic change in the chemical and physical nature of ER after curing.