Cr~(2+):ZnSe的激光输出和调谐性能

Cr~(2+):ZnSe具有很宽的吸收带和发射带,是中红外波段优秀的可调谐激光材料。从吸收光谱、发射光谱以及角度调谐输出对Cr~(2+):ZnSe晶体的激光输出性能进行了研究。采用真空高温扩散法制备Cr~(2+):ZnSe晶体.获得了高浓度的Cr~(2+)离子掺杂的厚1.7 mm,直径10 mm的薄片ZnSe晶体。使用中心波长2.05μm,最大输出功率8 W的Tm离子掺杂的光纤激光器抽运,使用平凹腔结构搭建谐振腔,获得了最大平均功率1.034 W,中心波长2.367μm,线宽10 nm的连续激光输出。利用角度调谐的方法,对Cr:ZnSe晶体的调谐性能进行了研究,在100 nm范围内获得了调谐输出。

Cr^4＋：YAG被动调QNd：YAG陶瓷激光器的研究

介绍了近几年迅速发展的一种新型激光介质——透明Nd：YAG多晶陶瓷的发展状况，对比分析了多晶陶瓷与单晶的光谱特性、激光特性和连续实验研究情况。并对钛宝石激光器调谐至808nm，端面抽运Nd：YAG陶瓷被动调Q全固态激光器的脉冲运转进行了较为详细的理论分析和实验研究。采用初始透射率为90％的Cr^4＋：YAG可饱和吸收晶体，被动调Q的阈值功率为119mW，当端面抽运功率为465mW时，获得波长为1064nm，脉宽为16ns，重复频率为18．18kHz，单脉冲能量为3．4μJ，平均输出功率为61mW的稳定调Q

A compact diode-pumped injection seeded Nd : YAG laser with resonance-detection technique

A diode pumped injection seeded single-longitudinal-mode (SLM) Nd:YAG laser is achieved by using the resonance-detection technique in Q-switching operation. The pulsed oscillator laser uses a folded cavity to achieve compact construction. This system operates at 100 Hz and provides over 20 mJ/pulse of single-frequency 1064 nm output. The M-2 values of horizontal and vertical axes are 1.58 and 1.41, respectively. The probability of putting out single-longitudinal-mode pulses is 100%. The 355 nm laser output produced by frequency tripling has a linewidth less than 200 MHz. The laser can run over eight hours continually without mode hopping.

Generation of 1.5-12 ns width-tunable 532 nm pulses by adopting laser-induced plasma shutter technique

The pulse-shaping technique has found widespread applications in nonlinear optics and material processing. Experimental research on laser-induced plasma shutter to control the 532 nm pulse width is conducted. The impacts of the total pulse output energy on pulse compression are investigated, and a useful conclusion can be drawn that there exists an optimal value of pulse energy at which the shortest output pulse of 3.23 ns can be obtained without a device for delay-time. Once the device for delay-time is employed to change the optical differences between two laser paths, the pulse width can be further shortened to 1.51 ns. In short, the 1.5-12 ns width-tunable 532 nm laser pulses have been obtained by adopting the laser-induced plasma shutter technique. (C) 2007 Elsevier GmbH. All rights reserved.

TeO2对氟铝酸盐玻璃性质和结构的影响

以10MgF2—20CaF2—10SrF2—10BaF2—15YF3—35AlF3氟铝酸盐玻璃为基玻璃引入不同含量的TeO2得到了新的氟碲铝酸盐玻璃．用差热分析方法研究了TeO2对氟铝酸盐玻璃性能的影响，通过拉曼光谱和红外吸收谱来研究玻璃的结构变化．差热分析表明TeO2的增加使玻璃开始析晶温度瓦升高，融化温度％降低，成玻璃能力增加．玻璃结构分析表明氟碲铝酸盐玻璃的结构中存在[FnAl-O—AlFn]、[TeO3]、[TeO2F]和[TeOF2]等多面体，这些多面体由F^-和O^2-离子连接．这种新的氟碲铝

Effect of network modifiers on spectroscopic properties of erbium-doped phosphate glasses

The integrated absorption cross section Sigma(abs), I peak emission cross section sigma(cmi), Judd-Ofeld intensity parameters Omega(iota) ( t = 2,4,6), and spontaneous emission probability A(R) of Er3+ ions were determined for Erbium doped alkali and alkaline earth phosphate glasses. It is found the compositional dependence of sigma(emi) 5 almost similar to that of Sigma(abs), which is determined by the sum, of Omega(1) (3 Omega(2) + 10 Omega(4) + 21 Omega(6)). In addition, the compositional dependence of Omega(1) was studied in these glass systems. As a result, compared with. Omega(4) and Omega(6) the Omega(2) has a stronger compositional dependence on the ionic radius and content of modifers. The covalency of Er-O bonds in phosphate glass is weaker than that in silicate glass, germanate glass, aluminate glass, and tellurate glass, since Omega(6) of phosphate glass is relatively large. A(R) is affected by the covalency of the Er3+ ion sites and corresponds to the Omega(6) value.

掺铒碲酸盐玻璃的热力学稳定性和光谱性质的研究

分析了掺Er^3+碲酸盐玻璃的热力学稳定性能，研究了掺Er^3+碲酸盐玻璃的吸收和荧光光谱性质；应用Judd-Ofelt理论计算了碲酸盐玻璃中Er^3+离子的强度参数Ω(Ω2=4．79×10^-20cm^2,Ω4=1．52×10^-20cm^2，Ω6=0．66×10^-20cm^2)，计算了离子的自发跃迁几率，荧光分支比；应用McCumber理论计算了Er^3+的受激发射截面(σe=10．40×10^-21cm^2)、Er^3+离子^4I13／2→^4I15／2发射谱的荧光半高宽(FWHM=65．5nm)

Effect of bismuth oxide on the thermal stability and Judd-Ofelt parameters of Er 3(+)/Yb3(+) co-doped aluminophosphate glasses

The Er3+/Yb3+ co-doped glasses with compositions of xBi(2)O(3)-(65-x)P2O5-4Yb(2)O(3)-11Al(2)O(3)-5BaO-15Na(2)O (where x = 0, 2.5, 5, 7.5 and 10 mol%) were prepared using the normal melt quench technique. The optical absorption spectra of the glasses were recorded in the wavelength range 300-1700 nm. The effect of Bi2O3 content on the thermal stability and absorption spectra of glasses was investigated. In addition, the Judd-Ofelt parameters and oscillator strengths were calculated by employing Judd-Ofelt theory. It was observed that the positions of the fundamental absorption edge and cut-off wavelength shifted towards red as the content of Bi2O3 increased. However, there were no red shifts found both in the peak wavelength and in the center of mass wavelength of all absorption bands with Bi2O3 content increasing. The results of Judd-Ofelt theory analysis showed that Judd-Ofelt parameters Omega(t), (t = 2, 4, 6) changed sharply when Bi2O3 concentration exceeded 5 mol%. The variation trends of experimental oscillator strength were similar with those of Judd-Ofelt parameters as function of Bi2O3 concentrations. Moreover, differential scanning calorimetry experiments showed that the increases of Bi2O3 content weakened the network structure and then lowered the thermal stability of the glasses. The spontaneous emission probability A(rad), branching ratio beta and the radiative lifetime tau(rad) were also calculated and analyzed. The stimulated emission cross-section of Er3+ was calculated according to the McCumber theory. It was found that the stimulated emission cross-section of Er3+ was monotonically increases with Bi2O3 content increasing. (C) 2006 Elsevier B.V. All rights reserved.

不同玻璃组分对掺铒碲酸盐玻璃 光谱性质的影响

Series of tellurite glasses were prepared by traditional melting method, the glass composition were changed and the different effects of glass modifier oxides(alkali metals and alkaline earth metal oxides) and glass intermediate (Y2O3, GeO2, Nb2O5, WO3) on the optical and spectroscopic properties of Er³⁺ doped tellurite glass were researched and compared. The infrared transmitting spectra, absorption spectra and fluorescence spectra were tested, the results showed that Nb2O5 and WO3 in the glass act as part of the body's role in the formation of the network, caused the reduction of transmitting range in infrared wavelength, which decrease the transmitting properties of tellurite glass. The introduction of high valence cationic ions, WO3 especially, can increase the FWHM of Er³⁺ for the increased polarization effect. With the decreasing of cationic field of glass modifier ions, the ion filed of the environment around Er³⁺ increased, subsequently, the role of ligand field polarization effect reduced, which makes the luminescence lifetime increase, and on the contrary the FWHM decrease monotonously.