Novel and ideal zirconium-based dense membrane reactors for partial oxidation of methane to syngas

A novel and ideal dense catalytic membrane reactor for the reaction of partial oxidation of methane to syngas (POM) was constructed from the stable mixed conducting perovskite material of BaCo0.4Fe0.4Zr0.2O3-delta and the catalyst of LiLaNiO/gamma-Al2O3. The POM reaction was performed successfully. Not only was a short induction period of 2 h obtained, but also a high catalytic performance of 96-98% CH4 conversion, 98-99% CO selectivity and an oxygen permeation flux of 5.4-5.8 ml cm(-2) min(-1) (1.9-2.) mumol m(-2) S-1 Pa-1) at 850 degreesC were achieved. Moreover, the reaction has been steadily carried out for more than 2200 h, and no interaction between the membrane material and the catalyst took place.

A novel zirconium-based perovskite-type membrane material for oxygen permeation

A novel zirconium-based membrane material of BaCo0.4Fe0.4Zr0.2O3-6 with cubic perovskite structure was synthesized for the first time through a method of citric and EDTA acid combined complexes. The structural stability was characterized by XRD, O-2-TPD and H-2-TPR techniques respectively. The high oxygen permeation flux of 0.873 mL/cm(2) min at 950 degreesC was obtained under He/Air gradient. Meanwhile, the single activation energy for oxygen permeation and the long-term steady operation of 200 h at 800 degreesC were achieved.

Post-grafting preparation of large-pore mesoporous materials with localized high content titanium doping

A new post-grafting process, consisting of two steps of substrate preparation and sol - gel post-grafting, has been developed to prepare titanium-doped mesoporous SBA-15 material with a double-layered structure and locally concentrated titanium content at the inner pore surface. With this novel technique, the single phased and originally ordered mesostructures can be well conserved; in the conventional direct synthesis they can be partially damaged when the frameworks are doped with high content heteroatoms. Titanium species exist in an isolated, tetrahedral structure and are localized at the pore surface; this is beneficial to both reactant access and product release. Characterization with XRD, N-2 adsorption/desorption isotherms, HREM/ EDS, ICP, UV - Vis, and the newly developed UV - Raman spectroscopy confirm these results. Preliminary catalytic tests with the selective epoxidation of cyclohexene show good catalytic activity. Among them, sample TiSBA-15-10 with a Si : Ti molar ratio of 10 shows a TON value of 75 and a highest product ( epoxide) yield of 55%.

表面纳米化Zr的拉伸性能

利用表面机械研磨处理(SMAT)技术在Zr片状拉伸样品表面施加剧烈变形,获得超细/纳米晶粒组织的变形细化表层,其中Zr板厚度1 mm,两侧变形层厚度均为100μm.拉伸实验结果表明,表层细化组织提高了屈服强度和抗拉强度,使加工硬化能力及伸长率下降.应变速率在10~(-4)～10~(-3)s~(-1)范围时,拉伸强度随应变速率的提高而提高;应变速率增大至10~(-2)s~(-1)量级时,抗拉强度下降.扫描电镜观察显示出韧性韧窝状断裂特征.

Microstructure of Zr-alloyed coating using pulsed laser

Coatings were synthesized by laser alloying of zirconium (Zr) particles using a pulsed Nd:YAG laser on an austenite stainless steel. The distribution of Zr is uneven, in a depth of 18 mum just below the surface of the pool. The coating consisted of duplex microstructures, i.e. metallic glass (MG) and austenite. The MG formed in Zr-contained regions, with the Zr composition ranging from 7.6 to 16.8 at.%. The formation of the MG was attributed to an increase in glass-forming ability by Zr addition.

Essential and Non-Essential Work of Fracture of PI/SiO2 Hybrid Thin Films

Essential work of fracture (EWF) analysis is used to study the effect of the silica doping level on fracture toughness of polyimide/silica (PI/SiO2) hybrid films. By using double-edge-notched-tension (DENT) specimens with different ligament lengths, it seems that the introduction of silica additive can improve the specific essential work of fracture (w (e) ) of PI thin films, but the specific non-essential work of fracture (beta w (p) ) will decease significantly as the silica doping level increasing from 1 to 5 wt.%, and even lower than that of neat PI. The failure process of the fracture is investigated with online scanning electron microscope (SEM) observation and the parameters of non-essential work of fracture, beta and w (p) , are calculated based on finite element (FE) method.

Low Temperature Properties of PI/SiO_2 Nanocomposite Films

In this paper, the mechanical properties of PI/Si_O, nanocomposite hybrid films with different silica doping levels are experimentally studied at low temperature. Experimental results show that the coefficient of thermal expansion (CTE) of the PI/Si_O, nanocomposite hybrid films gradually reduces when the ambiance temperature is decreased. At the liquid nitrogen temperature (77 K), the CTE value is about five times less than that at room temperature (287 K). The measured CTEs of hybrid films greatly decrease when doped with inorganic silica, especially when the silica doping level is more than 1 wt.%. However, too high silica contents (more than 10 wt.%) can cause problem to disperse effectively and the specimens become quite opaque. Experimental results also show that the effects of the pre-applied stress levels can be neglected on the CTE testing. When the ambient temperature changes from 287 to 77 K, the measured average values of the films' ultimate tensile strength (UTS) and Young's modulus increase about 60 and 90%, respectively, while the breaking elongation decreases about 42%.

Mechanisms of thermal shock failure for ultra-high temperature ceramic

The materials considered in our analysis were ZrB2 ceramic matrix composites. Effect of two different additives (graphite and AlN) on thermal shock stability for the materials was measured by water quench test. It showed that it may provide more stable thermal shock properties with additives of graphite. It was explained by different thermal properties and crack resistance of the two materials in detail. Surface oxidation was one of main reasons for strength degradation of ceramic with additives of graphite after quenched in water, and surface crack was one of main reasons for strength degradation of ceramic with additives of AlN after quenched in water. It was presented that it was a potential method for improving thermal shock stability of ZrB2 ceramic matrix composites by introducing proper quantities of graphite.

Nonvolatile holograms in LiNbO3 : Fe : Cu by use of the bleaching effect

We report our observation of a bleaching effect under an ultraviolet exposure in LiNbO3:Fe:Cu crystals. Two three-step recording-transferring-fixing schemes are proposed to record nonvolatile photorefractive holograms in such crystals. In the schemes two red laser beams and an ultraviolet illumination are used selectively to write the charge grating in the shallow-level Fe centers, to develop the charge grating in the deep-level Cu centers by transferring the charge grating in the Fe centers, and to fix only the charge grating in the Cu centers for unerasable read-out. Experimental results, verifications, and an optimal recording scheme are given. A comparison of the lithium niobate crystals of the same double-doping system of Fe:Mn, Ce:Mn, Ce:Cu, and Fe:Cu is outlined. (C) 2002 Optical Society of America.

Prescription for optimizing holograms in LiNbO3 : Fe : Mn

The photorefractive holographic dynamics of grating formation in photochromic doubly doped LiNbO3:Fe:Mn crystal is studied numerically and analytically in terms of the two-center model of Kukhtarev Et al. [Ferroelectrics 22, 949 (1979)]. The relations among the recorded and fixed space-charge fields and the doping densities, the oxidation-reduction states of the fields, and the intensities of UV-sensitizing and red recording beams are studied. Important conditions and effects are feued, and an optimal prescription for material doping and oxidation-reduction processing is suggested in which the crystal can be strongly oxidized and the Mn-doping density is smaller than the Fe-doping density. (C) 2000 Optical Society of America. OCIS codes: 050.7330, 190.5330, 090.2900.

Nonvolatile photorefractive holograms in LiNbO3 : Cu : Ce crystals

We report experimental and theoretical studies of nonvolatile photorefractive holographic recording in LiNbO3:Cu:Ce crystals with two illumination schemes: (1) UV light for sensitization and a red interfering pattern for recording and (2) blue light for sensitization and a red pattern for recording. The results show that the oxidized LiNbO3:Cu:Ce crystals can provide high, persistent refractive-index modulation with weak lightinduced scattering. The optimal working conditions and the prescription for doping and oxidation-reduction processing that yields the maximum refractive-index modulation are discussed. (C) 2000 Optical Society of America OCIS codes: 050.7330, 190.5330, 090.2900.