Synthesis and properties of novel sulfonated polyimides containing binaphthyl groups as proton-exchange membranes for fuel cells

A novel sulfonated diamine monomer, 2,2'-bis(p-aminophenoxy)-1,1'-binaphthyl-6,6'-disulfonic acid (BNDADS), was synthesized. A series of sulfonated polyimide copolymers containing 30-80 mol % BNDADS as a hydrophilic component were prepared. The copolymers showed excellent solubility and good film-forming capability. Atomic force microscopy phase images clearly showed hydrophilic/hydrophobic microphase separation. The relationship between the proton conductivity and degree of sulfonation was examined. The sulfonated polyimide copolymer with 60 mol % BNDADS showed higher proton conductivity (0.0945-0.161 S/cm) at 20-80 degrees C in liquid water. The membranes exhibited methanol permeability from 9 x 10(-8) to 5 X 10(-7) cm(2)/s at 20 degrees C, which was much lower than that of Nafion (2 x 10(-6) cm(2)/s). The copolymers were thermally stable up to 300 degrees C. The sulfonated polyimide copolymers with 30-60 mol % BNDADS showed reasonable mechanical strength; for example, the maximum tensile strength at break of the sulfonated polyimide copolymer with 40 mol % BNDADS was 80.6 MPa under high moisture conditions. The optimum concentration of BNDADS was found to be 60 mol % from the viewpoint of proton conductivity, methanol permeability, and membrane stability.

Isomeric polyimides

This review deals with polyimides based on isomeric dianhydrides and diamines, and with chiral polyimides. First, however, a summary is presented of recent work on the synthesis of isomeric dianhydrides, the reaction of mellophanic dianhydride with diamines, and the tendency toward cyclization in reactions of some dianhydrides and diamines. Then turning to polymers, the discussion covers solubility, thermal and dielectric properties, permeability and permselectivity for gas separation, and rheology of isomeric polyimides. Several useful general rules have been found: i.e. the glass transition temperature of polyimides based on isomeric dianhydrides with a given diamine decreases in the order 3,3'- > 3,4'- > 4,4-dianhydride if the polymers are of comparable molecular weight, whereas the thermal stability and the T-beta/T-g ratio (in absolute temperatures) increase in the order of 3,3'- < 3,4'- < 4,4'-dianhydride. Polyimides from 3,3'- or 3,4'-dianhydride have higher solubility than those from 4,4'-dianhydride. Polyimides from 3,4'-dianhydrides exhibit much lower melt viscosity than those from the other isomeric anhydrides. The dielectric constants of polyimides derived from m,m'-diamines are lower than those from p,p'-diamines. Polyimides based on 3,3'- or 3,4'-dianhydrides have higher permeability and slightly lower permselectivity than polyimides based on 4,4'-dianhydrides.

Water resistant sulfonated polyimides based on 4,4'-binaphthyl-1,1',8,8'-tetracarboxylic dianhydride (BNTDA) for proton exchange membranes

A series of sulfonated polyimides (SPIs) were synthesized in in-cresol from 4,4'-binaphthyl- 1,11,8,8'-tetracarboxylic dianhydride (BNTDA), 4.4'-diaminodiphenylether-2,2-disulfonicacid (ODADS), and 4.4'-diamino-diphenyl ether (ODA) in the presence of triethylamine and benzoic acid. The resulted polyimides showed much better water resistance than the corresponding sulfonated polyimides from 1,4,5,8-naphthatenetetracarboxylic dianhydride (NTDA) and ODADS, which is contributed to the higher electron density in the carbonyl carbon atoms of BNTDA. Copolyimides S-75 and S-50 maintained their mechanical properties and proton conductivities after aging in water at 100 degrees C for 800 h. The proton conductivity of these SPIs was 0.0250-0.3565 S/cm at 20 degrees C and 100% relative humidity (RH), and increased to 0.11490.9470 S/cm at 80 degrees C and 100% RH. The methanol permeability values of these SPIs were in the range of 0.99-2.36 x 10(-7) cm(2)/S, which are much lower than that of Nafion 117 (2 x 10(-6) cm(2)/s).

Morphology evolutions of organically modified montmorillonite/polyamide 12 nanocomposites

Organically modified montmorillonites (OMMTs) by octadecylammonium chloride with two adsorption levels were dispersed in polyamide 12 (PA12) matrices with two molecular weights for different melt mixing times in order to investigate morphology evolutions and factors influencing fabrication of PA12 nanocomposites. Different adsorption levels of the modifier in the OMMTs provide different environments for diffusion of polymer chains and different attractions between MMT layers. Wide-angle X-ray diffraction (WAXD), transmission electron microscope (TEM) and gas permeability were used to characterize morphologies of the nanocomposites. Both OMMTs can be exfoliated in the PA12 matrix with higher molecular weight, but only OMMT with lower adsorption level can be exfoliated in the PA12 matrix with lower molecular weight. It was attributed to the differences in the levels of shear stress and molecular diffusion in the nanocomposites. The exfoliation of OMMT platelets results from a combination of molecular diffusion and shear. After intercalation of PA12 into interlayer of OMMT in the initial period of mixing, further dispersion of OMMTs in PA12 matrices is controlled by a slippage process of MMT layers during fabricating PA12 nanocomposites with exfoliated structure.

Fabrication and characterization of DNA/QPVP-Os redox-active multilayer film

Calf thymus DNA was immobilized on functionalized glassy carbon, gold and quartz substrates, respectively, by the layer-by-layer (LBL) assembly method with a polycation QPVP-Os, a quaternized poly(4-vinylpyridine) partially complexed with osmium bis(2,2'-bipyridine) as counterions. UV-visible absorption and surface plasmon resonance spectroscopy (SPR) showed that the resulting film was uniform with the average thickness 3.4 nm for one bilayer. Cyclic voltammetry (CV) showed that the total surface coverage of the polycations increases as each QPVP-Os/DNA bilayer added to the electrode surface, but the surface formal potential of Os-centered redox reaction shifts negatively, which is mainly attributed to the intercalation of redox-active complex to DNA chain. The electron transfer kinetics of electroactive QPVP-Os in the multilayer film was investigated by electrochemical impedance experiment for the first time. The permeability of Fe(CN)(6)(3-) in the solution into the multilayer film depends on the number of bilayers in the film. It is worth noting that when the multilayer film is up to 4 bilayers, the CV curves of the multilayer films display the typical characteristic of a microelectrode array.

Synthesis and properties of novel polyimides derived from 2,2 ',3,3 '-benzophenonetetracarboxylic dianhydride

A new synthetic route to 2,2',3,3'-BTDA (where BTDA is benzophenonetetracarboxylic dianhydride), an isomer of 2,3',3',4'-BTDA and 3,3',4,4'-BTDA, is described. Single-crystal X-ray diffraction analysis of 2,2',3,3'-BTDA has shown that this dianhydride has a bent and noncoplanar structure. The polymerizations of 2,2',3,3'-BTDA with 4,4'-oxydianiline (ODA) and 4,4'-bis(4-aminophenoxy)benzene (TPEQ) have been investigated with a conventional two-step process. A trend of cyclic oligomers forming in the reaction of 2,2',3,3'-BTDA and ODA has been found and characterized with IR, NMR, matrix-assisted laser desorption/ionization time-of-flight mass spectrometry, and elemental analyses. Films based on 2,2',3,3'-BTDA/TPEQ can only be obtained from corresponding polyimide (PI) solutions prepared by chemical imidization because those from their polyamic acids by thermal imidization are brittle. PIS from 2,2',3,3'-BTDA have lower inherent viscosities and worse thermal and mechanical properties than the corresponding 2,3',3',4'-BTDA- and 3,3',4,4'-BTDA-based PIs. PIs from 2,2',3,3'-BTDA and 2,3',3',4'-BTDA are amorphous, whereas those from 3,3',4,4'-BTDA have some crystallinity, according to wide-angle X-ray diffraction.

New proton exchange membranes based on poly (vinyl alcohol) for DMFCs

A series of new composite proton exchange membranes for direct methanol fuel cells (DMFCs) based on poly (vinyl alcohol) (PVA), phosphotungstic acid (PWA) and silica were prepared. The highest proton conductivity (a) of these membranes is 0.017 S/cm at ambient temperature. The methanol permeability (D) of these composite membranes ranges from 10(-7) to 10(-8) cm(2)/S. From the ratios of sigma/D, it was found that the optimal weight composition of the PVA/PWA/SiO2 membrane is PVA/PWA/SiO2=0.40:0.40:0.20 wt. Infrared (IR) spectrographic measurements indicate that the Keggin structure characteristics of the PW12O403- anion is present in the composite membranes. Cyclic voltammetry shows that the electrochemical stability window of the complex membrane is from -0.5 to 1.5 V vs. Ag/AgCl electrode. The results of differential scanning calorimetry (DSC) show that silica can improve the thermal stability of the complexes and the single Tg of the membrane indicates that the membrane is homogeneous. The complexes behave as X-ray amorphous.

Polyimides from isomeric diphenylthioether dianhydrides

3,3',4,4'-Diphenylthioether dianhydride (4,4'-TDPA), 2,3,3',4'-diphenylthioether dianhydride (3,4'-TDPA), and 2,2',3,3-diphenylthioether dianhydride (3,3'TDPA) were synthesized from 3-chlorophthalic anhydride and 4-chlorophthalic anhydride. A series of polyimides derived from the isomeric diphenylthioether dianhydrides with several diamines were prepared. The properties, such as the solubility, thermal and mechanical behavior, dynamic mechanical behavior, wide-angle X-ray diffraction, and permeability to some gases, were compared among the isomeric polyimides. Both 3,3'-TDPA- and 3,4-TDPA-based polyimides had good solubility in polar aprotic solvents and phenols. The 5% weight loss temperatures of all the obtained polyimides was near 500 degrees C in nitrogen. The glass-transition temperatures decreased according to the order of the polyimides based on 3,3'-TDPA, 3,4'-TDPA, and 4,4'-TDPA. The 3,4'-TDPA-based polyimides had the best permeability and lowest permselectivity, whereas the 4,4'-TDPA-based polyimides had the highest permselectivity and the lowest permeability of the three isomers. Furthermore, the rheological properties of thermoplastic polyimide resins based on the isomeric dipbenylthioether dianhydrides were investigated, and they showed that polyimide 3,4'-TDPA/4,4-oxydianiline had the lowest melt viscosity among the isomers; this indicated that the melt processibility had been greatly improved.

Synthesis and properties of soluble polyimides based on isomeric ditrifluoromethyl substituted 1,4-bis(4-aminophenoxy)benzene

A new fluorinated diamine monomer, [1,4-bis(4-amino-3-trifluoromethylphenoxy)benzene (2)], and a known isomeric analog 1,4-bis(4-amino-2-trifluoromethylphenoxy)benzene (3) were synthesized. A series of organosoluble polyimides Ia-d and IIa were prepared from the diamines (2, 3) and dianhydrides (a-d) by a high-temperature one-step method. The effects of the trifluoromethyl substituents on the properties of polyimides were evaluated through the study of their soluble, thermal, optical, and gas permeability properties. Polyimides (Ia-d) had glass transition temperatures between 229 and 279 degrees C, and the temperatures at 5% weight loss ranged from 510 to 533 degrees C under nitrogen. These polyimides could be cast into flexible and tough membranes from DMAc solutions. The membranes had tensile strengths in the range of 137-169 MPa, tensile modulus in the range of 1.6-2.2 GPa and elongations at break from 11% to 14%. The polyimide la with trifluoromethyl groups ortho to the imide nitrogen exhibited enhanced gas permeability, solubility, transparency, and thermal stability compared with the isomeric polyimide IIa with the CF3 group meta to the imide nitrogen.

A study on the interaction between ibuprofen and bilayer lipid membrane

Ibuprofen is a well-known nonsteroidal anti-inflammatory drug, which can interact with lipid membranes. In this paper, the interaction of ibuprofen with bilayer lipid membrane was studied by UV-vis spectroscopy, cyclic voltammetry and AC impedance spectroscopy. UV-vis spectroscopy data indicated directly that ibuprofen could interact with lipid vesicles. In electrochemical experiments, ibuprofen displayed a biphasic behavior on bilayer lipid membrane supported on a glassy carbon electrode. It could stabilize the lipid membrane in low concentration, while it induced defects formation, even removed off bilayer lipid membrane from the surface of the electrode with increasing concentration. The mechanism about the interaction between ibuprofen and supported bilayer lipid membrane was discussed.

The interaction of recombinant Pseudomonas aeruginosa exotoxin A with DNA and mimic biomembrane investigated by surface plasmon resonance and electrochemical methods

Based on the multidomain structure of Pseudomonas aeruginosa exotoxin A, a fusion protein termed rPEA has been constructed, which is expected to serve as a gene carrier in vitro. The expression and purification of rPEA are described. The basal properties of rPEA as a gene carrier are evaluated by investigating its interaction with plasmid DNA and mimic biomembrane by surface plasmon resonance (SPR) and electrochemical methods. rPEA is proved to be able to bind with plasmid DNA with high affinity. It can also interact with lipid membrane and increase permeability of the membrane, so the probe molecules can easily reach the gold surface and exhibit the electrochemical response.

Synthesis of nanocrystalline Ba(CoxZn1-x)(2)Fe16O27 by sol-gel auto-combustion method

The synthesis of nanocrystalline W-type hexaferrites Ba(CoxZn1-x)(2)Fe16O27 powders by sol-gel auto-combustion method has been investigated. The thermal decomposition process of dried gel was studied by thermogravimetry (TG), differential thermal analysis (DTA) and infrared spectra (IR). The structural and magnetic properties of resultant particles were investigated by X-ray diffraction (XRD), transmission electron microscope (TEM), and vibrating sample magnetometer (VSM). The results reveal that the dried gel exhibits auto-combustion behavior. After combustion, pure nanocrystalline W-type hexaferrite phase starts to appear at the calcination temperature of 800 degrees C. The crystallinity and the grain size increase at higher temperature. The saturation magnetization and coercivity clearly depend on calcination temperature and Co content X.

Mesoscopic simulation of the impregnating process of unidirectional fibrous preform in resin transfer molding

The resin transfer molding has gained popularity in the preparation of fiber-reinforced polymer-matrix composites because of its high efficiency and low pollution. The non-uniform inter-tow and intra-tow flows are regarded as the reason of void formation in RTM. According to the process characteristics, the axisymmetric model was developed to study the interaction between the flow in the inter-tow space and that in the intra-tow space. The flow behavior inside the fiber tows was formulated using Brinkman's equation, while that in the open space around the fiber tows was formulated by Stokes' equation. The volume of fluid (VOF) method was applied to track the flow front, and the effects of filling velocity, resin viscosity, inter-tow dimension and intra-tow permeability on fluid pressure and flow front were analyzed. The results show that the flow front difference between the inter-tow and intra-tow becomes larger with the decrease of intra-tow permeability, as well as the increase of filling velocity and inter-tow dimension.

Synthesis and characterization of hyperbranched aromatic poly(ether imide)s

The four AB(2) monomers, N-[3- or 4-bis(4-hydroxyphenyl)toluoyl]-4-chlorophthalimide and N-{3- or 4-[1,1-bis(4-hydroxyphenyl)]ethylphenyl}-4-chlorophthalimides, were prepared and used for synthesis of hyperbranched poly(ether imide)s bearing hydroxyl end groups. These hyperbranched poly(ether imide)s had moderate molecular weights with broad distributions and showed glass-transition temperatures (Tgs) between 177 and 230 degreesC. The thermogravimetric analytic measurement revealed the decomposition temperature at 5% weight-loss temperatures (T-d(5%)) ranging from 240 to 281 degreesC. Analysis using H-1 NMR spectroscopy revealed the four types of hyperbranched poly(ether imide)s to have similar degrees of branching (ca. 60%). These polymers were modified by acylation or nucleophilic substitution reaction at the hydroxyl end groups. The conversion effectiveness depended on the type of modification reaction, modifier, and reaction conditions. The thermal stability and solubility of hyperbranched poly(ether imide)s were improved by the modification of the end groups.

Synthesis and characterization of hyperbranched aromatic poly(ester-imide)s

The synthesis and characterization of hyperbranched aromatic poly(ester-imide)s are described. A variety of AB(2) monomers, N-[3- or 4-bis(4-acetoxyphenyl)toluoyl]-4-carboxyl-phthalimide and N-{3- or 4-[1,1-bis(4-acetooxyphenyl)]ethylphenyl}-4-carboxy phthalimides were prepared starting from condensation of nitrobenzaldehydes or nitroacetophenones with phenol and used for synthesis of hyperbranched poly(ester-imide)s containing terminal acetyl groups by transesterification reaction. These hyperbranched poly(ester-imide)s were produced with weight-average molecular weight of up to 6.87 g/mol. Analysis of H-1 NMR and C-13 NMR spectroscopy revealed the structure of the four hyperbranched poly(ester-imide)s. These hyperbranched poly(ester-imide)s exhibited excellent solubility in a variety of solvents such as N,N-dimethylacetamide, dimethyl sulfoxide, and tetrahydrofuran and showed glass-transition temperatures between 217 and 255 degreesC. The thermogravimetric analytic measurement revealed the decomposition temperature at 10% weight-loss temperature (T-d(10)) ranging from 365 to 416 degreesC in nitrogen.