Growth mode and strain evolution during InN growth on GaN(0001) by molecular-beam epitaxy

Epitaxial growth of InN on GaN(0001) by plasma-assisted molecular-beam epitaxy is investigated over a range of growth parameters including source flux and substrate temperature. Combining reflection high-energy electron diffraction (RHEED) and scanning tunneling microscopy (STM), we establish a relationship between film growth mode and the deposition condition. Both two-dimensional (2D) and three-dimensional (3D) growth modes of the film are observed. For 2D growth, sustained RHEED intensity oscillations are recorded while STM reveals 2D nucleation islands. For 3D growth, less than three oscillation periods are observed indicating the Stranski-Krastanov (SK) growth mode of the film. Simultaneous measurements of (reciprocal) lattice constant by RHEED suggest a gradual relaxation of the strain in film, which commences during the first bilayer (BL) deposition and almost completes after 2-4 BLs. For SK growth, 3D islanding initiates after the strain has mostly been relieved, presumably by dislocations, so the islands are likely strain free. (C) 2002 American Institute of Physics.

Relaxation of carriers in terbium-doped ZnO nanoparticles

Terbium ions were successfully incorporated in nano-sized zinc oxide particles with a doping concentration up to 3% by using a wet chemical route. Four narrow emission peaks of Tb3+ ions and a broad emission band of the surface states on ZnO nano-hosts were observed for all Tb-doped nanoparticles. Relaxation of carriers from excited states of ZnO hosts to rare earth (RE) dopants is disclosed by the fact that the emission intensity of Tb3+ centers increases with increased Tb content at the expense of the emission from surface defect states in ZnO matrix. (C) 2001 Elsevier Science B.V. All rights reserved.

Study of rapid carrier capture and relaxation in InAs/GaAs heterostructures

The rapid carrier capture and relaxation processes in InAs/GaAs quantum dots were studied at 77K by using a simple degenerate pump-probe technique. A rising process was observed in the transient reflectivity, following the initial fast relaxation associated with GaAs bulk matrix, and this rising process was assigned to be related to the carrier capture from the GaAs barriers to InAs layers. The assignment was modeled using Kramers-Kronig relation. By analyzing the rising process observed in the transient reflectivity, the carrier capture time constants were obtained. The measured capture times decrease with the increase of carrier concentration.

Anisotropic strain in (100) ZnSe epilayers grown on lattice mismatched substrates

We show that part of the reflectance difference resonance near the E-0 energy of ZnSe is due to the anisotropic in-plane strain in the ZnSe thin films, as films grown on three distinctly different substrates, GaAs, GaP, and ZnS, all show the resonance at the same energy. Such anisotropic strain induced resonance is predicted and also observed near the E-1/E-1+Delta(1) energies in ZnSe grown on GaAs. The theory also predicts that there should be no resonance due to strain at, the E-0+Delta(0) energy, which is consistent with experiments. The strain anisotropy is rather independent of the ZnSe layer thickness, or whether the film is strain relaxed. For ZnSe films with large lattice mismatch with substrates, the resonance at the E-1/E-1+Delta(1) energies is absent, very likely due to the poor crystalline quality of the 20 nm or so surface layer. (C) 2000 American Vacuum Society. [S0734-211X(00)05604-3].

X-ray double-crystal characterization of the strain relaxation in GaAs/GaNxAs1-x/GaAs(001) sandwiched structures

An X-ray diffraction method, estimating the strain relaxation in an ultrathin layer, has been discussed by using kinematic and dynamical X-ray diffraction (XRD) theory. The characteristic parameter Delta Omega, used as the criterion of the strain relaxation in ultrathin layers, is deduced theoretically. It reveals that Delta Omega should be independent of the layer thickness in a coherently strained layer. By this method, we characterized our ultrathin GaNxAs1-x samples with N contents up to 5%. XRD measurements show that our GaNxAs1-x layers are coherently strained on GaAs even for such a large amount of N. Furthermore, a series of GaNxAs1-x samples with same N contents but different layer thicknesses were also characterized. It was found that the critical thickness (L-c) of GaNAs in the GaAs/GaNAs/GaAs structures determined by XRD measurement was 10 times smaller than the theoretical predictions based on the Matthews and Blakeslee model. This result was also confirmed by in situ observation of reflection high-energy electron diffraction (RHEED) and photoluminescence (PL) measurements. RHEED observation showed that the growth mode of GaNAs layer changed from 2D- to 3D-mode as the layer thickness exceeded L-c. PL measurements showed that the optical properties of GaNAs layers deteriorated rapidly as the layer thickness exceeded L-c. (C) 2000 Elsevier Science B.V. All rights reserved.

Dielectric relaxation of poled polymer DCNP/PMMA

We have prepared the polymer thin films of a 3-(1,1-dicyanothenyl)-1-phenyl-4,5-dihydro-1H-pyrazole (DChTP)/poly (methyl methacrylate) (PMMA) guest-host system by spin coating. In order to investigate their temporal and temperature stability, we have measured their dielectric relaxation spectra including the frequency dependence of the real and imaginary parts of dielectric constants. The investigated frequency ranged from 50 Hz to 10 MHz. The measured temperature range above the glass transition temperature T-g (95 degrees C) of the DCNP/PMMA system was from 95 degrees C to 1250C. By using the Adam-Gibbs model, the temperature dependence of the characteristic time tau above T-g was fitted, and the values of the characteristic times tau below T-g were estimated. The lifetimes of the polymer were evaluated by the Kohlrausch-Williams Watts (KWW) empirical decay model. (C) 2000 Elsevier Science B.V. All rights reserved.

New modulation structures observed in Bi2.13Sr1.87CuO6+delta superconductors

A new two-dimensional structure modulation along c- and b-axes has been discovered in superconducting single crystals of Bi2.13Sr1.87CuO6+delta (Bi2201) by x-ray scattering. Such modulation structure does not exist in non-superconducting Bi2201 single crystals, but instead lattice distortions are observed in the a-b-plane. This phenomenon may indicate that both strain relaxation and charge modulation in the a-b-plane are important to the occurrence of superconductivity in the copper oxides.

Strain relaxation of GeSi alloy with low dislocation density grown on low-temperature Si buffers

We have developed a low-temperature (LT) growth technique. Even with Ge fraction x upto 90%, the total thickness of fully relaxed GexSi1-x buffers can he reduced to 1.7 mu m with dislocation density lower than 5 x 10(6) cm(-2). The surface roughness is no more than 6 nm. The strain relaxation is quite inhomogeneous From the beginning. Stacking faults generate and form the mismatch dislocations in the interface of GeSi/LT-Si. (C) 1999 Elsevier Science B.V. All rights reserved.

A new interface anisotropic potential of zinc-blende semiconductor interface induced by lattice mismatch

A new interface anisotropic potential, which is proportional to the lattice mismatch of interfaces and has no fitting parameter, has been deduced for (001) zinc-blende semiconductor interfaces. The comparison with other interface models is given for GaAs/AlAs and GaAs/InAs interfaces. The strong influence of the interface anisotropic potential on the inplane optical anisotropy of GaAs/AlGaAs low dimensional structures is demonstrated theoretically within the envelope function approximation.

Growth mode and strain relaxation of InAs on InP (111)A grown by molecular beam epitaxy

Growth mode and strain relaxation of molecular-beam-epitaxy grown InAs/InAlAs/InP (111)A system have been investigated using reflection high-energy electron diffraction, transmission electron microscopy, atomic force microscopy, and photoluminescence measurements. In direct contrast to the well-studied InAs/GaAs system, our experimental results show that the InAs grown on InAlAs/InP (111)A follows the Stranski-Krastanov mode. Both self-organized InAs quantum dots and relaxed InAs islands are formed depending on the InAs coverage. Intense luminescence signals from both the InAs quantum dots and wetting layer are observed. The luminescence efficiency of (111)A samples is comparable to that of (001) samples, suggesting the feasibility of fabricating quantum dot optoelectronic devices on InP (111)A surfaces. (C) 1999 American Institute of Physics. [S0003-6951(99)01010-4].

Electronic structures of cubic lattice quantum dots

In this article, we give the electronic structure and optical transition matrix elements of coupled quantum dots (QDs) arranged as different cubic lattices: simple cubic (sc), body-centered cubic (bcc), and face-centered cubic (fcc) superlattices. The results indicate that electron and hole energies of bcc, sc, and fcc superlattices are the lowest, the highest, and the middle, respectively, for the same subband under the same QD density or under the same superlattice constant. For a fixed QD density, the confinement effects in sc, fcc, and bcc superlattices are the strongest, the middle, and the weakest, respectively. There are only one, two, and four confined energy bands, with energies lower than the potential barrier for sc, bcc, and fcc QD superlattices, respectively. The results have great significance for researching and making semiconductor quantum dot devices. (C) 1998 American Institute of Physics. [S0021-8979(98)02119-7]

Characterization of strain relaxation in As ion implanted Si1-xGex epilayers grown by gas source molecular beam epitaxy

Strain relaxation in the As ion implanted Si0.57Ge0.43 epilayers was studied by double-crystal x-ray diffractometry and transmission electron microscopy, and was compared to that in the nonimplanted Si0.57Ge0.43 epilayers. Experimental results show that after rapid thermal annealing (RTA) the x-ray linewidth of the As+-implanted Si0.57Ge0.43 epilayers is narrower than that of the nonimplanted epilayers, and than that of the partially relaxed as-grown samples, which is due primarily to low density of misfit dislocations in the As+-implanted SiGe epilayers. RTA at higher than 950 degrees C results in the formation of misfit dislocations for the nonimplanted structures, and of combinations of dislocations and precipitates (tentatively identified as GeAs) for the As+-implanted epilayers. The results mean that the strain relaxation mechanism of the As+-implanted Si1-xGex epilayers may be different from that of the nonimplanted Si1-xGex epilayers. (C) 1998 American Institute of Physics.

Influence of rapid thermal annealing on the optical properties of gallium nitride grown by gas-source molecular-beam epitaxy

Raman scattering, photoluminescence (PL), and nuclear reaction analysis (MA) have been employed to investigate the effects of rapid thermal annealing (RTA) on GaN films grown on sapphire (0001) substrates by gas-source molecular-beam epitaxy, The Raman spectra showed the presence of the E-2 (high) mode of GaN and shift of this mode from 572 to 568 cm(-1) caused by annealing. The results showed that RTA has a significant effect on the strain relaxation caused by the lattice and thermal expansion misfit between the GaN epilayer and the substrate. The PL peak exhibited a blueshift in its energy position and a decrease in the full width at half maximum after annealing, indicating an improvement in the optical quality of the film. Furthermore, a green luminescence appeared after annealing and increased in intensity with increasing annealing time. This effect was attributed to H concentration variation in the GaN film, which was measured by NRA. A high H concentration exists in as-grown GaN, which can neutralize the deep level, and the H-bonded complex dissociates during RTA, This leads to the appearance of a luminescent peak in the PL spectrum. (C) 1998 American Institute of Physics.

Hydrogen-decorated lattice defects in proton implanted GaN

Several vibrational bands were observed near 3100 cm(-1) in GaN that had been implanted with hydrogen at room temperature and subsequently annealed, Our results indicate that these bands are due to nitrogen-dangling-bond defects created by the implantation that an decorated by hydrogen, The frequencies are close to those predicted recently for V-Ga-H-n complexes, leading us to tentatively assign the new lines to V-Ga defects decorated with different numbers of H atoms. (C) 1998 American Institute of Physics. [S0003-6951(98)03614-6].