Adsorption and reaction of thiophene and H2S on Mo2C/Al2O3 catalyst studied by in situ FT-IR spectroscopy

The reactions of both thiophene and H2S onMo(2)C/Al2O3 catalyst have been studied by in situ FT-IR spectroscopy. CO adsorption was used to probe the surface sites of Mo2C/Al2O3 catalyst under the interaction and reaction of thiophene and H2S. When the fresh Mo2C/Al2O3 catalyst is treated with a thiophene/H-2 mixture above 473 K, hydrogenated species exhibiting IR bands in the regions 2800-3000 cm(-1) are produced on the surface, indicating that thiophene reacts with the fresh carbide catalyst at relatively low temperatures. IR spectra of adsorbed CO on fresh Mo2C/Al2O3 pretreated by thiophene/H-2 at different temperatures clearly reveal the gradual sulfidation of the carbide catalyst at temperatures higher than 473 K, while H2S/H-2 can sulfide the Mo2C/Al2O3 catalyst surface readily at room temperature (RT). The sulfidation of the carbide surface by the reaction with thiophene or H2S maybe the major cause of the deactivation of carbide catalysts in hydrotreating reactions. The surface of the sulfided carbide catalyst can be only partially regenerated by a recarburization using CH4/H-2 at 1033 K. When the catalyst is first oxidized and then recarburized, the carbide surface can be completely reproduced.

Catalytic alcohols synthesis from CO and H2O on TiO2 catalysts calcined at various temperatures

The reaction performance for CO hydration on a TiO2 catalyst under different calcination temperatures was investigated. Under reaction conditions of T = 573 K, P = 0.5 MPa, CO flow rate of 30 ml min(-1), TOS = 12 h, and CO/H2O (g) = 3/2 (mol), the TiO2 catalyst with a futile content of 18% shows a maximum alcohols STY of 1.81 Mg m(-2) h(-1). In addition, the catalyst deactivation and regeneration were discussed.

Analysis of specific gene by integration of isothermal amplification and electrophoresis on poly(methyl methacrylate) microchips

We have successfully achieved the integration of isothermal amplification and the subsequent analysis of specific gene fragments on poly(methyl methacrylate) microchips. In our experiments, loop-mediated isothermal amplification, which can offer higher specificity and efficiency than PCR, has been performed at a constant temperature (65 degreesC). After amplification, products could be either examined by the integrated microchip-based electrophoresis or directly observed by naked eye with SYBR Green I added into the reaction solution. By such an integrated microsystem, the amplification and the subsequent analysis of prostate-specific antigen gene with template concentration at 23 fg/muL could be finished within 15 min, which demonstrates its advantages of high specificity, good reproducibility, and fast speed in gene detection.

Water reduction and oxidation on Pt-Ru/Y2Ta2O5N2 catalyst under visible light irradiation

Y2Ta2O5N2 is presented as a novel photocatalyst with high activity for water splitting under visible-light irradiation in the presence of appropriate sacrificial reagents; the activity for reduction to H-2 is increased by the incorporation of Pt or Ru as a co-catalyst, with a significant increase in production efficiency when both Pt and Ru are present.

Molecular imprinting of nitrophenol and hydroxybenzoic acid isomers: effect of molecular structure and acidity on imprinting

Three nitrophenol isomer-imprinted polymers were prepared under the same conditions using 4-vinylpyridine as a functional monomer. Different recognition capacities for template molecules were observed for the three polymers. Another imprinting system with stronger acidity than nitrophenol isomers, 2-hydroxybenzoic acid (salicylic acid) and 4-hydroxybenzoic acid, was imprinted using 4-vinylpyridine or acrylamide as functional monomer respectively. Both 4-hydroxybenzoic acid-imprinted polymers using the two monomers showed recognition ability for the template molecule. However, when acrylamide was chosen as functional monomer, the salicylic acid-imprinted polymer showed very weak recognition for the template molecule, whereas strong recognition ability of the resultant polymer for salicylic acid was observed with 4-vinylpyridine as functional monomer. It seems that the structure and acidity of template molecules is responsible for the difference in recognition, by influencing the formation and strength of interaction between template molecule and functional monomer during the imprinting process. An understanding of the mechanism of molecular imprinting and molecular recognition of MIPs will help to predict the selectivity of MIPs on the basis of template molecule properties. Copyright (C) 2003 John Wiley Sons, Ltd.

Adsorption of arsenite and arsenate on amorphous iron hydroxide

Adsorption isotherms in solutions with ionic strengths of 0.01 at 25°C were measured over the arsenite and arsenate concentration range 10−7−10−3 M and the pH range 4–10. At low concentrations, these isotherms obeyed equations of the Langmuir type. At higher concentrations the adsorption isotherms were linear, indicating the existence of more than one type of surface site on the amorphous iron hydroxide adsorbent. Removal of arsenite and arsenate by amorphous iron hydroxide throughout the concentration range were determined as a function of pH. By careful selection of the relative concentration of arsenic and amorphous iron hydroxide and pH, removals on the order of 92% can be achieved.

Rare-earth-metal mixed hydride/aryloxide complexes bearing mono(cyclopentadienyl) ligands. Synthesis, CO2 fixation, and catalysis on copolymerization of CO2 with cyclohexene oxide

Hydrogenolysis of mono(cyclopentadienyl)-ligated rare-earth-metal bis(alkyl) complexes Cp'Ln-(CH2SiMe3)2(THF) (Ln = Y (1a), Dy (1b), Lu (1c); Cp' = C5Me4SiMe3) with PhSiH3 afforded the mixed hydride/alkyl complexes [Cp'Ln(mu-H)(CH2SiMe3)(THF)](2) (Ln = Y (2a), Dy (2b), Lu (2c)). The overall structure of complexes 2a-c is a C-2-symmetric dimer containing a planar symmetric Ln(2)H(2) core at the center of the molecule. Deprotonation of ArOH (Ar = C6H2-Bu-t(2)-2,6-Me-4) by the metal alkyl group of 2a-c led to formation of the mixed hydride/aryloxide derivatives [Cp'Ln(mu-H)(OAr)](2) (Ln = Y (3a), Dy (3b), Lu (3c)), which adopt the dimeric structure through hydride bridges with trans-accommodated terminal aryloxide groups.

The influence of mischmetal and tin on the microstructure and mechanical properties of Mg-6Zn-5Al-based alloys

The influence of the addition of mischmetal (MM) and tin (Sn) (total content of mischmetal and tin = 4 wt.%) on the microstructure, aging behavior and mechanical properties of Mg-6Zn-5Al-based alloys has been investigated. The microstructure of the as-cast alloys consists of alpha-Mg. Mg-32(Al,Zn)(49), Al2Mg5Zn2, Mg2Sn and Al2MMZn2 phases, and the morphology of these intermetallic phases varies with different MM and Sri additions.

Rare-Earth Metal Bis(alkyl)s Supported by a Quinolinyl Anilido-Imine Ligand: Synthesis and Catalysis on Living Polymerization of epsilon-Caprolactone

The tridentate ligand N-(2-((2,6-diisopropylphenylimino)methyl)phenyl)quinolin-8-amine (HL) was prepared. Treatment of HL with 1 equiv of Ln(CH2SiMe3)(3)(THF)(2) afforded the corresponding rare-earth metal bis(alkyl) complexes LLn(CH2SiMe3)(2)(THF)(n) (Ln = Sc, n = 0 (1); Y, n = 1 (2); Lu, n = 0 (3)) in high yields. Variable-temperature H-1 NMR spectral analysis showed that these complexes were fluxional at room temperature. Complexes 1 and 3 were THF-free, where the metal center adopted a square-pyramidal geometry, while in 2 the metal center generated a distorted octahedral geometry owing to the coordination of a THF molecule.

Determination of Cd2+ and Pb2+ on glassy carbon electrode modified by electrochemical reduction of aromatic diazonium salts

Carbon modified by the reduction of aromatic diazonium derivatives was first used as electrode for the electrochemical stripping analysis of heavy metals. As a model, the glassy carbon electrode was modified with benzoic acid by electrochemical reduction of diazobenzoic acid, and the resulting modified electrodes were used for determination of Cd2+ and Pb2+. The anodic peak currents of cadmium and lead at the benzoic acid-modified glassy carbon electrode are 7.2 and 6 times of that at the bare glassy carbon electrode. A linear response was observed for Pb2+ and Cd2+ in the range of 0.5-50 mu g/l.

Synthesis of Aromatic Oxide-Oxadiazoles Containing Pyridine Ring and Study on Their Spectral Properties

In order to explore new highly organic electroluminescent materials, six symmetrical aromatic oxide-oxadiazoles containing pyridine ring 4a similar to 4f were synthesized through cyclization of substituted benzoic acid (2) with 2,6-dihydrazide pyridine (3) by "one-pot" method in POCl3. Their structures were confirmed by MS, IR, H-1 NMR techniques and elemental analysis. The fluorescence spectra of the target compounds showed that the A,m ranged from 347 to 507 nm, and the maximum A,m were close to 384 nm, which showed that these compounds have good fluorescence with strong fluorescence intensity. When the 5-Br group was introduced into the aromatic ring (4e and 4f), the fluorescent emission wavelength took place Einstein shift, and the fluorescent intensity decreased a little. Using quinine bisulphate as a reference, the fluorescence quantum yields were all tested, and the introduction of 5-Br group had no visible effect on fluorescence quantum yield.

Nucleation and growth of glycine crystals with controllable sizes and polymorphs on Langmuir-Blodgett films

Control of crystal polymorph and size is very important in many application fields. Herein we demonstrate that Langmuir-Blodgett (LB) films of stearic acid (SA) and octadecylamine (ODA) can serve as templates and generate different polymorphs of glycine crystals. In the neutral aqueous solutions, gamma-glycine crystallizes on LB films of ODA while the polymorphic outcome becomes the (x-form on LB films of SA. These observed results could be explained by the electrostatic interactions and geometric lattice matching at the LB film/crystal interfaces, respectively. By keeping the appropriate supersaturation, we have successfully controlled the number of crystals grown on LB films; for example, in some certain cases, only one piece of crystal was grown on LB films in solution. Therefore, large crystals of centimeter size could be prepared. These experimental results suggest a new approach to produce an organic crystal with bulk scale.