Crystallization of mechanically alloyed amorphous W-Mg alloy under high pressure

Pure metal powder mixtures of W and Mg at the desired composition were milled in conventional high-energy ball mill, and amorphous alloy W50Mg50 was obtained after milling for 20 h. The structure evolution of elemental powder mixtures was studied following milling and subsequent high pressure and high temperature treatment. The amorphous alloy transform into a nanocrystalline material below 1050 degreesC at 4.0 GPa. On increasing the temperature, it transforms into a mixture of several new crystal phases under high-pressure condition. It also found that both mechanical alloying and high pressure treatment are the two necessary processes to form the nanocrystalline and the new phases.

Microstructures and tensile properties of Mg-8Gd-0.6Zr-xNd-yY (x+y=3, mass%) alloys

Mg-8Gd-0.6Zr-xNd-yY (mass%) alloys which containing different Nd:Y mass ratio of 3:0, 2:1, 1:2 and 0:3 with a constant x + y = 3 were prepared by metal mould casting method, and the microstructure, aging behaviour and tensile properties have been investigated. The fibrous eutectic areas along the boundaries enlarge clearly in the as-cast alloys containing Y element, and the fine grain boundaries and dispersed precipitation are observed in the aged alloys. The Mg-8Gd-0.6Zr-2Nd-Y alloy exhibits notably age-hardening behaviour and the highest mechanical property. The ultimate tensile strength and yield strength of Mg-8Gd-0.6Zr-2Nd-Y alloy in the peak aged hardness are 293 and 221 MPa at room temperature, 248 and 191 MPa at 230 degrees C. The improvement of age-hardening response and tensile properties is mainly attributed to the quadrate-like stable Mg5RE precipitate, which forms readily and orderly in aged Mg-8Gd-0.6Zr-2Nd-Y alloy.

Microstructures and properties of melt-spun and as-cast Mg-20Gd binary alloy

Mg-20Gd(%, mass fraction) samples were prepared using melt-spinning and copper mold casting techniques. Microstructures and properties of the Mg-20Gd were investigated. Results show that the melt-spun ribbon is mainly composed of supersaturated alpha-Mg solid solution phase and the as-east ingot mainly contains alpha-Mg solid solution and Mg5Gd phase. The differential scanning calorimeter (DSC) curve of the ribbon exhibits a small exothermic peak in the temperature range from 630 to 680 K, which indicates that the ribbon contains a metastable phase (amorphous). Tensile strength at room temperature of the melt-spun ribbon and as-cast specimen are 308 and 254 MPa, respectively. The elongations of the two samples are less than 2%. The fracture surfaces demonstrate that the fracture mode of the as-cast Mg-20Gd is a typical cleavage fracture and that of the melt-spun sample is a combination of brittle fracture and ductile fracture.

Carbon ceramic electrodes bulk-modified with nanoparticles of ferrocenebutyrate-intercalated Mg-Al layered double hydroxide

Ferrocenebutyrate-intercalated layered double hydroxide (FcLDH) was prepared by the coprecipitation method and characterized by PXRD, FTIR, TEM and elemental analysis. FcLDH nanoparticles in deionized water were deposited onto the surface of graphite powder to yield graphite powder-supported FcLDH, which was subsequently dispersed into methyltrimethoxysilane-derived gels to fabricate surface-renewable, stable, rigid carbon ceramic electrodes containing the electroactive ferrocenyl group. Cyclic voltammetric study revealed that peak currents of the FcLDH-modified electrode were diffusion-con trolled in 0.1 mol l(-1) KCl aqueous solution. In addition, the formal potential of the modified electrode is related to the activity of chloride ion with a Nernst slope of 56 mV per decade.

Preparation, structure and luminescence of BaMAl10O17 : Eu2+ (M = Be, Mg, Ca, Zn, Cd, Mn, Co, Li) system

The BaMA(10)O(17) (M = Be, Mg, Ca, Zn, Cd, Mn, Co, Li) system has been synthesized by solid state method and characterized by XRD. The results show that when M is Mg, Zn, Mn, Co, Li, there exists the structure of beta-Al2O3 for BaMAl10O17 system, and when M indicates Cd, beta-Al2O3 structure is formed accompanying alpha-Al2O3 phase, and when M represents Be and Ca, beta-Al2O3 structure cannot be formed. This demonstrates that the condition forming beta-Al2O3 structure compounds for the system BaMAl10O17 is 0.05nm < R-M < 0.09nm (R-M represents the radius of M). The thought that if a M ion can form a stable spinel structure there exsits a corresponding magnetoplumbite and beta-alumina structure is proposed for BaMAl10O17 system according to the experimental results. When M is Li, Be, Zn, Eu2+ activator produces an emission of nearly 450 nm with half height width about 50 nm, when M is Mn, there are simultaneously the emissions of Eu2+ and Mn2+ and the excitation energy of Eu2+ can transfer to Mn2+ in the host, when M is Cd, Eu2+ displays a double-emission band, which can be explained by the Jahn-Teller's effect. It is possible for the system BaMAl10O17 with M being Li, Be, Zn to become blue-emitting component in three colour lamp through further study.

BaMAl_(10)O_(17)(M=Be,Mg,Ca,Zn,Cd,Mn,Co,Li)体系的合成、结构和Eu~(2+)在其中的发光

在BaMAl10O17 体系中 ,将M扩大到除镁以外的其它离子 ,研究和讨论了离子半径与基质结构的形成关系 ,提出能稳定(形成)尖晶石结构的M离子有相应的磁铅矿或β Al2O3 结构的化合物存在的思想 ,并研究了Eu2 +在体系中的发光性能。结果表明 ,M=Zn,Cd,Mn,Co,Li时可形成 β Al2O3 结构化合物 ,M=Ca,Be时不能形成这类结构 ,Ca形成多相共存 ,Be形成一未知相 ;Eu2 +在M=Li,Be,Zn体系中具有良好的发光性能 ,发射波长450nm ,半高宽在50nm附近 ,将是一类很有前途的新的蓝色发光材料 ,Eu2 +在M=Mn的体系中存在Eu2 +和Mn2 +的同时发射 ,在M=Cd体系中 ,Eu2 +产生一双重宽带发射。对实验结果进行了合理的解释

ABF_3:Eu,Gd(A:K,Li;B:Ba,Mg)中Gd~(3+)→Eu~(2+)的能量传递

通过高温固相反应法,在高纯N_2气氛中合成了BaLiF_3,KMgF_3中单掺和双掺Eu,Gd的ABF_3型复合氟化物。研究了各类掺杂体系的光谱特性,观察到了Gd~(3+)→Eu~(2+)的能量传递,分析了能量传递过程,探讨了能量传递机理,并讨论了Gd~(3+)和Eu~(2+)的取代格位。

LaMAl_(11)O_(19)(M=Mg,Fe)的化学键性质和穆斯堡尔谱研究

利用复杂晶体化学键的平均能带模型研究了LaMAl11O19(M =Mg ,Fe)晶体的化学键性质。结果表明 ,La O键只有 3%的共价性 ,4f1格位却具有很强的共价特征。晶体中各格位共价次序为 :La O

A mechanistic study of electrochemical oxidation processes of (OEP)Mg(II) in the presence of anions

In the presence of F-, OH-, Cl-, electrochemical redox of (OEP)Mg(II) [2,3, 7,8,12,13,17,18 octaethyl-21H, 23H-porphine magnesium (II)] are investigated in DCE/0.1 mol/L solution by cyclic voltammetry and spectroelectrochemistry, In the presence of anions, anions are axially coordinated to (OEP)Mg(II) generate (OEP)Mg(II)Y, the E-1/2 of (OEP)MS(II)Y oxidation are negatively shifted. A chemical reaction following the second oxidation step is observed, the E-1/2 of the reaction product is obtained. Mechanism of (OEP)Mg(II) in the halogen and OH- anions titration process has been proposed.

以水滑石为前体的Mg-Al-M复合氧化物对催化消除NOx的活性

通过H2-TPR，XRD，TG-DTA及比表面积测定等对ＭｇＡｌ水滑石化合物进行了表征，研究了焙烧温度对水滑石物理性质的影响．在此基础上，研究了ＭｇＡｌ水滑石中加入过渡金属（Ｍ）离子后对ＮＯ＋ＣＯ反应的催化活性．结果发现，含有Ｃｕ离子的样品对ＮＯ＋ＣＯ反应有较高的催化活性，并与ＣｏＡｌＭ的催化性能进行了比较

阴离子存在下(OEP)MG(Ⅱ)的电化学氧化机理研究

用电化学滴定和现场光谱电化学方法研究考察了DCE中OH~－，F~-和Cl-等阴离子存在下的（OEP）Mg（Ⅱ）的电极氧化过程．发现阴离子能与（OEP）Mg（目）轴向配位，形成五配位化合物，从而引起（OEP）Mg（Ⅱ）的氧化峰电位的负移；在生成二价环阳离子的过程中伴随后行化学反应．获得了反应产物的氧化还原峰电位.

稀土对Al-Mg-Si系合金结构和性能的影响

本文用ＸＲＤ和ＳＥＭ方法研究了稀土对Ａｌ－Ｍｇ－Ｓｉ系合金微观结构的影响，同时还测定了这些合金的耐腐蚀及力学性能。结果表明，该体系的稀土铝合金中大约含０．１０％稀土就可以细化组织，提高使用性能。具有很好的应用前景。

Luminescence properties of Ce3+ in KMF3(M=Mg, Ca, Sr, Ba) hosts with perovskite structure

KMF3(M = Mg, Ca, Sr, Ba) compounds were synthesized by solid state reaction under argon atmosphere. Their structures were determined by X-ray diffraction. It belongs to cubic system with perovskite structure. The excitation and emission spectra of KMF3:Ce3+ were measured. According to the characteristics of spectral structures, the occupation site of Ce3+ is discussed.

离子型晶体的点电荷电量的确定和晶体的化学键性质MX(M=Mg,Ca,Sr,Ba,X=O,S,Se,Te;不含MgTe)

离子型晶体的点电荷电量的确定和晶体的化学键性质ＭＸ（Ｍ＝Ｍｇ，Ｃａ，Ｓｒ，Ｂａ，Ｘ＝Ｏ，Ｓ，Ｓｅ，Ｔｅ；不含ＭｇＴｅ）孟庆波武志坚张思远（中国科学院长春应用化学研究所稀土无机材料实验室，长春１３００２２）ＮｅｔＣｈａｒｇｅａｎｄＣｈｅｍｉｃａｌＢｏｎ...