Partial oxidation of methane to syngas in tubular oxygen-permeable reactor

A dense Ba0.5Sr0.5Co0.8Fe0.2O3-delta membrane tube was prepared by the extruding method. Furthermore, a membrane reactor with this tubular membrane was successfully applied to partial oxidation of methane (POM) reaction, in which the separation of oxygen from air and the partial oxidation of methane are integrated in one process. At 875degreesC, 94% of methane conversion, 98% of CO selectivity, 95% of H-2 selectivity, and as high as 8.8 mL/(min (.) cm(2)) of oxygen flux were obtained. In POM reaction condition. the membrane tube shows a very good stability.

An in-situ modified sol-gel process for monolith catalyst preparation used in the partial oxidation of methane

An in-situ modified sol-gel method for the preparation of a Ni-based monolith-supported catalyst is reported. With the presence of a proper amount of plasticizer and binder, and at an optimized pH value, the stable boehmite sol was modified with metal ions (Ni, Li, La) successfully without distinct growth of the particle size. Monolith-supported Ni-based/gamma-Al2O3 catalysts were obtained using the modified sol as the coating medium with several cycles of dip-coating and calcination. Combined BET, SEM-EDS, XRD and H-2-TPR investigations demonstrated that the derived monolith catalysts had a high specific surface area, a relatively homogeneous surface composition, and a high extent of interaction between the active component and the support. These catalysts showed relatively stable catalytic activities for partial oxidation of methane (POM) to syngas under atmospheric pressure. The monolith catalysts prepared by this sol-gel method also demonstrated an improved resistance to sintering and loss of the active component during the reaction process.

Novel and ideal zirconium-based dense membrane reactors for partial oxidation of methane to syngas

A novel and ideal dense catalytic membrane reactor for the reaction of partial oxidation of methane to syngas (POM) was constructed from the stable mixed conducting perovskite material of BaCo0.4Fe0.4Zr0.2O3-delta and the catalyst of LiLaNiO/gamma-Al2O3. The POM reaction was performed successfully. Not only was a short induction period of 2 h obtained, but also a high catalytic performance of 96-98% CH4 conversion, 98-99% CO selectivity and an oxygen permeation flux of 5.4-5.8 ml cm(-2) min(-1) (1.9-2.) mumol m(-2) S-1 Pa-1) at 850 degreesC were achieved. Moreover, the reaction has been steadily carried out for more than 2200 h, and no interaction between the membrane material and the catalyst took place.

Partial oxidation of ethane to syngas over nickel-based catalysts modified by alkali metal oxide and rare earth metal oxide

The catalytic activity, thermal stability and carbon deposition of various modified NiO/gamma-Al2O3 and unmodified NiO/gamma-Al2O3 catalysts were investigated with a flow reactor, XRD, TG and UVRRS analysis. The activity and selectivity of the NiO/gamma-Al2O3 catalyst showed little difference from those of the modified nickel-based catalysts. However, modification with alkali metal oxide (Li, Na, K) and rare earth metal oxide (La, Ce, Y, Sm) can improve the thermal stability of the NiO/gamma-Al2O3 and enhance its ability to suppress carbon deposition during the partial oxidation of ethane (POE). The carbon deposition contains graphite-like species that were detected by UVRRS. The nickel-based catalysts modified by alkali metal oxide and rare earth metal oxide have excellent catalytic activities (C2H6 conversion of similar to 100%, CO selectivity of similar to 94%, 7x 10(4) l/(kg h), 1123 K), good thermal stability and carbon-deposition resistance.

Mechanistic studies of methane partial oxidation to syngas over LiNiLaOx/Al2O3 catalyst

Temperature-programmed reduction (TPR) characterization of the LiNiLaOx/Al2O3 catalyst before or after partial oxidation of methane (POM) reaction and a series of O-2, CH4 and CH4/O-2 pulse reaction experiments over the catalyst under different pretreatments were performed. It was found that CH4 dissociatively adsorbs on active center nickel producing H-2 and surface carbon, C(a). The surface carbon reacts with surface lattice oxygen or surface adsorbed oxygen to produce CO. Because the activation barrier for the reaction C(a)+ O(a) =CO(a) is the highest among all the elementary reactions, the rate-determining step of the POM may be the reaction C(a) + O(a) =CO(a).