Difference of ZSM-5 zeolites synthesized with various templates

ZSM-5 zeolites with similar SUM ratio were synthesized successfully using various templates (n-butylamine (BTA), ethylamine (ETA), isopropylamine (IPA), ethylenediamine (EDA), ethanol (ETL), ethanol-ammonium (ETL-AM) and no template (NT)) under hydrothermal conditions. The samples were characterized by XRD, SEM, XRF, NH3-TPD and BET surface area measurements in order to understand the template effects and the differences of the ZSM-5 samples. The synthesis of ZSM-5 with organic templates was relatively easier than those with inorganic templates and without template. SEM results revealed that ZSM-5 synthesized with different templates had different morphology and particle size. The Si/Al ratio and BET specific surface area of the sample with ethanol as template was the lowest. NH3-TPD results showed that the sample synthesized without template had fewer strong acid sites than others. n-Hexane cracking reaction was carried out over the samples to evaluate the catalytic properties. All ZSM-5 zeolites were effective in n-hexane cracking reaction, especially for the sample synthesized without template. (C) 2004 Elsevier B.V. All rights reserved.

Novel synthesis of highly active Pt/C cathode electrocatalyst for direct methanol fuel cell

A 40 wt% Pt/C cathode electrocatalyst with controlled Pt particle size of similar to 2.9 nm showing better performance than commercial catalyst for direct methanol fuel cell was prepared by a polyol process with water but without using stabilizing agent.

Studies on state and structure of noble metals in electrocatalyst made by coprecipitation method

The electrocatalysts of Pt/C, PtRu/C and Ru/C were prepared by the impregnation method. The facet characterization, the dispersion and the particle size for the catalysts were determined by means of X-ray diffraction and transmission electron microscopy. X-ray photoelectron spectroscopy was also used to analyze the state and the valency of the noble metals. The results show that the particle size was in nanometer range and the binary metals have come into being an alloy. The platinum in the catalysts existed in zero valency. The valency of the ruthenium on the surface is different from that in the body, while the ruthenium on the surface existed in oxide-form. PtRu/C and Pt/C are of good activity to the electrooxidation of hydrogen except Ru/C. PtRu/C is more tolerant of CO than Pt/C, and CO is only adsorbed on Pt.

Preparation and characterization of multiwalled carbon nanotube-supported platinum for cathode catalysts of direct methanol fuel cells

Multiwalled carbon nanotube-supported Pt (Pt/MWNT) nanocomposites were prepared by both the aqueous solution reduction of a Pt salt (HCHO reduction) and the reduction of a Pt ion salt in ethylene glycol solution. For comparison, a Pt/XC-72 nanocomposite was also prepared by the EG method. The Pt/MWNT catalyst prepared by the EG method has a high and homogeneous dispersion of spherical Pt metal particles with a narrow particle-size distribution. TEM images show that the Pt particle size is in the range of 2-5 nm with a peak at 2.6 nm, which is consistent with 2.5 nm obtained from the XRD broadening calculation. Surface chemical modifications of MWNTs and water content in EG solvent are found to be the key factors in depositing Pt particles on MWNTs. In the case of the direct methanol fuel cell (DMFC) test, the Pt/MWNT catalyst prepared by EG reduction is slightly superior to the catalyst prepared by aqueous reduction and displays significantly higher performance than the Pt/XC-72 catalyst. These differences in catalytic performance between the MWNT-supported or the carbon black XC-72-supported catalysts are attributed to a greater dispersion of the supported Pt particles when the EG method is used, in contrast to aqueous HCHO reduction and to possible unique structural and higher electrical properties when contrasting MWNTs to carbon black XC-72 as a support.

Natural 13C abundance as a tracer for studies of soil organic matter dynamics

A method for measuring the long- and medium-term turnover of soil organic matter is described. Its principle is based on the variations of 13C natural isotope abundance induced by the repeated cultivations of a plant with a high 13C/12C ratio (C4 photosynthetic pathway) on a soil which has never carried any such plant. The 13C/12C ratio in soil organic matter being about equal to the 13C/12C ratio of plant materials from which it is derived, changing the 13C content of the organic inputs to the soil (by altering vegetation from C3 type into C4 type) is equivalent to a true labelling in situ of the organic matter. Two cases of continuous corn cultivation (Zea mays: δ13C = −12%.) on soils whose initial organic matter average δ13C is −26%. were studied. The quantity of organic carbon originating from corn (that is the quantity which had turned-over since the beginning of continuous cultivation) was estimated using the 13C natural abundance data. After 13 yr, 22% of total organic carbon had turned-over, in the system studied. Particle size fractions coarser than 50μm on the one hand, and finer than 2μm on the other. contained the youngest organic matters. The turnover rate of silt-sized fractions was slower

Microstructure and NO2 sensing properties of Fe2O3 thin films

W-doped Fe2O3 films have been fabricated on polycrystalline alumina substrates by the RF magnetron sputtering method, and effects of annealing temperature on the NO2 sensing properties have been examined. The crystal structure of the obtained film changed from Fe3O4 to α-Fe2O3 after annealing at temperatures of 500 to 500°C in air. An increase in the annealing temperature increased the particle size, resulting in a decrease in the NO2-gas sensitivity. These results suggest that the NO2 sensitivity of W-doped Fe2O3 film depends on the particle size.

Methods for physical separation and characterization of soil organic matter fractions

Turnover of soil organic matter (SOM) is coupled to the cycling of nutrients in soil through the activity of soil microorganisms. Biological availability of organic substrate in soil is related to the chemical quality of the organic material and to its degree of physical protection. SOM fractions can provide information on the turnover of organic matter (OM), provided the fractions can be related to functional or structural components in soil. Ultrasonication is commonly used to disrupt the soil structure prior to physical fractionation according to particle size, but may cause redistribution of OM among size fractions. The presence of mineral particles in size fractions can complicate estimations of OM turnover time within the fractions. Densiometric separation allows one to physically separate OM found within a specific size class from the heavier-density mineral particles. Nutrient contents and mineralization potential were determined for discrete size/density OM fractions isolated from within the macroaggregate structure of cultivated grassland soils. Eighteen percent of the total soil C and 25% of the total soil N in no-till soil was associated with fine-silt size particles having a density of 2.07-2.21 g/cm3 isolated from inside macroaggregates (enriched labile fraction or ELF). The amount of C and N sequestered in the ELF fraction decreased as the intensity of tillage increased. The specific rate of mineralization (mug net mineral N/mug total N in the fraction) for macroaggregate-derived ELF was not different for the three tillage treatments but was greater than for intact macroaggregates. The methods described here have improved our ability to quantitatively estimate SOM fractions, which in turn has increased our understanding of SOM dynamics in cultivated grassland systems.

黑龙江省安达市草地碱化后土壤物理性状变化

调查了安达市盐碱地生物资源环境研究中心试验区羊草Leymus chinensis地土壤物理性状,包括土壤硬度、含水量、饱和导水率、粒径分布、剖面特征和土壤温度等。阐明土地碱化对土壤物理性质的影响,为安达市以及松嫩平原生态环境的修复和土地资源的永续利用提供科学依据。同时,讨论了地下水化学成分和土壤冻融变化对碱化的可能影响,认为在没有植被覆盖的条件下,冻融变化会加剧土壤的碱化程度。

Vulcanization of polybutadiene latex induced by Co-60 gamma radiation

Polybutadiene latex (PBL) vulcanization induced by Co-60 radiation and the influence of dose on crosslinking were investigated. Morphology and particle size distribution were examined by AFM and a particle size analyzer. The casting films were characterized for their swelling and mechanical properties as a function of dose.

Fabrication and spectroscopic broadening properties for 1.5 mu m amplification of Er3+-doped BaF2 nanoparticles

We show the potential application of Er3+-doped BaF2 nanoparticles prepared from microemulsion technology for 1.5 mu m amplification in telecommunication. Nanoparticles with different sizes of about 8, 10, and 20.5 nm were prepared. The XRD patterns showed the excursion of diffraction peaks. When the particle size is smaller or the diffraction angle is larger, this kind of excursion will be more serious.

Phase Behavior and self-assembly of poly[N-vinylformamide-co-(acrylic acid)] copolymers under highly acidic conditions

Copolymers of N-vinylformamide and acrylic acid were synthesized by conventional aqueous free-radical polymerization. The phase behavior of the copolymer solutions was investigated through the addition of hydrochloric acid and the variation of the temperature. With a moderate content of N-vinylformamide, the copolymers showed complex phase behaviors. Under low-acidity conditions, a suspending liquid was formed, whereas under high-acidity conditions, the random copolymers could assemble into round nanoparticles with a broad particle size distribution.

Critical behavior of brittle-ductile transition of polymers

We report that the brittle-ductile transition of polymers induced by temperature exhibits critical behavior. When t close to 0, the critical surface to surface interparticle distance (IDc) follows the scaling law: IDc proportional to t(-v) where t = 1 - T/T-BD(m) (T and T-BD(m) are the test temperature and brittle-ductile transition temperature of matrix polymer, respectively) and v = 2/D. It is clear that the scaling exponent v only depends on dimension (D). For 2, 3, and 4 dimension, v = 1, 2/3, and 1/2 respectively. The result indicates that the ID, follows the same scaling law as that of the correlation length (xi), when t approach to zero.

Highly Uniform and Monodisperse Ba2CIF3 Microrods: Solvothermal Synthesis and Characterization

One-dimensional hexagonal Ba2CIF3 microrods with highly uniform morphology and size have been successfully synthesized via a facile solvothermal method at a low temperature (160 degrees C). X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM) were used to characterize the samples. The synthesis process, based on a phase-transfer and separation mechanism, allows the control of properties such as particle size and shape in low dispersity by bonding the surfactant oleic acid to the crystal surface.

Surface modification of bioactive glass nanoparticles and the mechanical and biological properties of poly(L-lactide) composites

Novel bioactive glass (13G) nanoparticles/poly(L-lactide) (PLLA) composites were prepared as promising bone-repairing materials. The BG nanoparticles (Si:P:Ca = 29:13:58 weight ratio) of about 40 run diameter were prepared via the sol-gel method. In order to improve the phase compatibility between the polymer and the inorganic phase, PLLA (M-n = 9700 Da) was linked to the surface of the BG particles by diisocyanate. The grafting ratio of PLLA was in the vicinity of 20 wt.%. The grafting modification could improve the tensile strength, tensile modulus and impact energy of the composites by increasing the phase compatibility.

Preparation, structure and dielectric properties of (Ba1-xSrx)(2)NaNb5O15 ceramics

In this study the tungsten-bronze type tetragonal (Ba1-xSrx)(2)NaNb5O15 system as a kind of lead-free ferroelectric ceramics has been synthesized by low-temperature combustion method. Microstructure and dielectric properties of (Ba1-xSrx)(2)NaNb5O15 system were also investigated. X-ray diffraction (XRD) study confirms the formation of single-phase tetragonal compounds in the crystal system at room temperature. The TEM photograph shows that the particles synthesized by low-temperature combustion method are uniform with an average particle size of 30nm in diameter.