Anomalous temperature dependence of photoluminescence in GaInNAs/GaAs multiple quantum wells

Photoluminescence (PL) spectra of GaInNAs/GaAs multiple quantum wells grown on a GaAs substrate by molecular beam epitaxy are measured in a range of temperatures and excitation power densities. The energy position of the dominant PL peak shows an anomalous S-shape temperature dependence instead of the Varshni relation. By careful inspection, especially for the PL under lower excitation power density, two near bandedge peaks are well identified. These are assigned to carriers localized in nitrogen-induced bound states and interband excitonic recombinations, respectively. It is suggested that the temperature-induced switch of such two luminescence peaks in relative intensity causes a significant mechanism responsible for the S-shape shift observed in GaInNAs. A quantitative model based on the thermal depopulation of carriers is used to explain the temperature dependence of the PL peak related to N-induced bound states.

The mechanism of blueshift in excitation-intensity-dependent photo luminescence spectrum of nitride multiple quantum wells

(1 1 (2) over bar 0) GaN/InGaN multiple quantum wells (MQWs) were grown on (1 (2) over bar 0 2) sapphire by metal-organic vapor phase epitaxy. The excitation-intensity-dependent photoluminescence (PL) spectrum of these samples was measured, and no peak shift was observed. This phenomenon was attributed to the absence of piezoelectric field (PEF) along the growth orientation of the (1 1 (2) over bar 0) face MQWs. Our experimental results showed that PEF was the main reason causing peak blueshift in excitation-intensity-dependent PL spectrum of (0 0 0 1) InGaN/GaN NIQWs. It was expected that fabricating (1 1 (2) over bar 0) face nitride device should be a method to avoid PEF and get low-threshold, high-quantum-efficiency and stable-emission-wavelength light-emission devices. (C) 2002 Elsevier Science B.V. All rights reserved.

GaInNAs/GaAs multiple-quantum well resonant-cavity-enhanced photodetectors at 1.3 mu m

A GaInNAs/GaAs multiple quantum well (MQW) resonant-cavity enhanced photodetector (RCF-PD) operated at a wavelength of 1.3 mum with the full width at half maximum of 4nm has been demonstrated. The GaInNAs RCE - PD was grown by molecular beam epitaxy using a homemade ion-removed dc plasma cell as a nitrogen source. GaInNAs/GaAs MQW shows a strong exciton peak at room temperature, which is very beneficial for applications in long-wavelength absorption devices. For a 100 mum diameter RCE-PD, the dark current is 20 and 32 pA at biases of 0 and 6 V, respectively, and the breakdown voltage is - 18 V. The measured 3 dB bandwidth is 308 MHz, which is limited by the resistance of p-type distributed Bragg reflector mirror. The tunable wavelength in a range of 18 nm with the angle of incident light was observed.