Preparation of Y1.84La0.16O3 nanopowders by oxalate co-precipitation method

Nanopowder of Y(1.84)mLa(0.16)O(3) was prepared by oxalate co-precipitation method. The powder was characterized by TG-DTA, XRD and TEM. The results show that the precursor is Re-2 (NO3)(2) (C2O4)(2)center dot 2H(2)O (Re=Y, La), and the Y1.84La0.16O3 nanopowders produced by calcining the precursor at 1000 degrees C for 4 h are 20 similar to 40 nm spherical particles and well dispersed. The powders were with high sintering activity and could be fabricated to transparent ceramic without additive at 1450 similar to 1550 degrees C in H-2 atmosphere for 3 hours. The total transmission of the transparent ceramic could reach 80%.

Effect of La2O3 on microstructure and transmittance of transparent alumina ceramics

Optically transparent alumina ceramics were fabricated by conventional process and sintered without pressure in H-2 atmosphere. The results indicate that relative densities of alumina specimens increase to theoretical densities (T. D.) with increasing content of La2O3. With increasing holding time during sintering, much less pores and larger grains were found in the sintered alumina samples. Higher transmittance was achieved in alumina codoped with MgO and La2O3 as compared with that doped with MgO only. The total-transmittance of alumina sample is up to 86% at a wavelength range of 300 - 800 nm.

Nd：YAG透明陶瓷的烧成及其显微结构

由溶胶一凝胶／燃烧合成结合法合成了Nd：YAG(掺钕钇铝石榴石，neodymium—doped yttrium aluminium garnet)粉体，用真空烧结法制备了Nd：YAG透明陶瓷。研究了显微结构随烧结温度和保温时间的变化，并对透明陶瓷的晶界结构和成分分布进行了表征。随着烧结温度的提高和保温时间的延长，Nd：YAG陶瓷的密度增大，晶形发育完整，透过率提高。晶粒内部和晶界的化学组成基本相同。所制备的Nd：YAG透明陶瓷在激光工作波长1064nm的透过率达到75％。

氧化铝透明陶瓷中Cr3+的发光性能

采用传统无压烧结工艺制备出透明性良好的掺Cr3+氧化铝陶瓷;测定了陶瓷的吸收光谱、发射光谱和激发光谱。结果表明,氧化铝陶瓷吸收峰与红宝石单晶一致,吸收截面大小与单晶相近;陶瓷中Cr3+离子所处格位的晶体场强较单晶弱,但其发射谱仍有较好的锐线发射;陶瓷中微量添加剂以及晶界的存在使得Al2O3晶胞发生畸变,造成其发射峰宽化。

Yb:Y2-2xLa2xO3激光透明陶瓷的光谱性能

It was first reported the spectral properties of a low-temperature sintered transparent Yb: Y2-2x La-2x O-3 laser ceramics. Yb: Y2-2x La-2x O-3 laser ceramics have broad absorption band and large absorption cross- section of 4.0 x 10(-20) cm(2) at wavelengths 977nm of the highest absorption peak. Its fluorescence lifetime is 1.1 ms, and the emission cross-sections are 1.0 x 10(-20) cm(2) and 0.7 x 10(-20) cm(2) at wavelengths 1033nm and 1077nm, respectively. All the optical properties are similar to those of single crystals.

Diode-pumped passively q-switched Nd : YAG ceramic laser with a Cr4+: YAG crystal-satiable absorber

Transparent polycrystalline Nd:YAG ceramics were fabricated by solid-state reactive sintering a mixture of commercial Al2O3,Y2O3, and Nd2O3 powders. The powders were mixed in ethanol and doped with 0.5 wt% tetraethoxysilane, dried, and pressed. Pressed samples were sintered at 1750 degrees C in vacuum. Transparent fully dense samples with average grain sizes of 10 mu m were obtained. The 1 at.% Nd:YAG ceramic was used to research passively Q-switched laser output with a Cr4+:YAG crystal as a saturable absorber. An average output power of 94 mW with a pulse width of 50 ns was obtained when the incident pump power was 750 mW. The slope efficiency was 13%. The pulse energy is 5 mu J, and the peak power is about 100 W.

In situ synthesis of ZrO2/ZrW2O8 composites with near-zero thermal expansion

In this paper, ZrO2 and WO3 were used as the raw materials to prepare ZrO2/ZrW2O8 composites by in situ reaction method and the thermal expansion property of the composites was studied. This novel method included a heating step up to 1473 K for 24 h, which combines the synthesizing and sintering of ZrW2O8. The result indicates that ZrO2/ZrW2O8 composite shows near-zero thermal expansion when the weight ratio of ZrO2 and WO3 is 2.5:1. Compared with composites prepared previously by non-reactive sintering of ZrO2 and ZrW2O8, the composites show higher relative density and lower porosity.

Diode-pumped Yb : YAG ceramic laser

Transparent polycrystalline Yb:YAG ceramics were fabricated by solid-state reactive sintering a mixture of commercial Al2O3, Y2O3, and Yb2O3 powders. The powders were mixed in ethanol and doped with 0.5 wt% tetraethoxysilane, dried, and pressed. Pressed samples were sintered at 1730 degrees C in vacuum. Transparent fully dense samples with grain sizes of several micrometers were obtained. The phase from 1500 degrees to 1700 degrees C was important for the grain growth, in which the grains grew quickly and a mass of pores were eliminated from the body of the sample. Annealing was an important step to remove the vacancies of oxygen and transform Yb2+ to Yb3+. The 1 at.% Yb:YAG ceramic sample was pumped by a diode laser to study the laser properties. The maximum output power of 1.02 W was obtained with a slope efficiency of 25% at 1030 nm. The size of the lasering sample was 4 mm x 4 mm x 3 mm.

用纳米粉制备Nd：Y1.84La0.16O3透明陶瓷Nd：Y1

用碳酸盐共沉淀法制备一种新的掺钕氧化镧钇（Nd：Y1.84La0.16O3）纳米粉体,得到颗粒细小、均匀、分散性好、粒径为50～60nm的Nd：Y1.84La0.16O3纳米粉体.分别采用Nd：Y1.84La0.16O3纳米粉料和商业粉料,用传统陶瓷无压烧结工艺制备Nd：Y1.84La0.16O3透明陶瓷.Nd：Y1.8vLa0.16O3纳米粉制备的陶瓷样品的组分均匀、几乎不存在第二相,具有较高的透过率.商业粉制备的陶瓷样品因混料不均匀而在晶界处存在部分第二相,降低了陶瓷的透过率.此外,还运用体视学法预测

晶格匹配氮化镓和氧化锌基外延薄膜衬底材料ScAlMgO4晶体生长研究

采用提拉法成功生长了氮化镓和氧化锌基外延薄膜晶格匹配的ScAlMgO4单晶衬底材料,晶体呈透明白色,尺寸为Ф30mm×59mm,表面部分沿解理面有裂纹.粉末X射线衍射（XRD）分析表明经1400℃固相反应烧结的原料基本合成了ScAlMgO4多晶相.初步的偏光显微镜观察、晶体的粉末XRD表征、透过光谱和双晶摇摆测试表明晶体具有较好的光学性质和结晶质量.研究表明晶体本身的层状结构、较大的温度梯度和热应力的不均匀性是生长过程中引起晶体开裂的几个主要原因.

Enhancement of ferromagnetic properties in In1.99Co0.01O3 by additional Cu doping

This paper reports room-temperature ferromagnetism in Co- and Cu-doped In2O3 samples synthesized by a solid-state reaction method. Structure and composition analyses revealed that Co and Cu were incorporated into the In2O3 lattices. Photoluminescence measurement revealed an additional emission at 520 urn from these doped samples. The magnetic measurement showed that additional Cu doping greatly enhanced the ferromagnetism of In1.99Co0.01O3 bulk samples. The implication of the effects of additional Cu doping is also discussed. (c) 2007 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Luminescence behavior of Yb(3+)heavy-doped yttrium lanthanum oxide transparent ceramics

Yb3+ heavy-doped yttrium lanthanum oxide transparent ceramics were fabricated and their spectroscopic properties were investigated. The absorption bands of (YbxY0.9-xLa0.1)(2)O-3 (x = 0.05-0.15) ceramics are broad at wavelength of 900-1000 nm. The absorption cross-sections centered at 974 nm and the emission cross-sections at 1031 nm of Yb3+ ion are 0.89-1.12 x 10(-20) cm(2) and 1.05 x 10(-20) cm(2) respectively. The up-conversion luminescence intensity of Yb3+-doped yttrium lanthanum oxide ceramics increased firstly, then decreased with the increase of Yb3+ ion content. (C) 2008 Elsevier B.V. All rights reserved.

薄膜材料对TiO2基薄膜激光损伤阈值的影响

abstract {The optical property, structure, surface properties (roughness and defect density) and laser-induced damage threshold (LIDT) of TiO₂ films deposited by electronic beam (EB) evaporation of TiO₂ (rutile), TiO₂ (anatase) and TiO₂ + Ta₂O₅ composite materials are comparatively studied. All films show the polycrystalline anatase TiO₂ structure. The loose sintering state and phase transformation during evaporating TiO₂ anatase slice lead to the high surface defect density, roughness and extinction coefficient, and low LIDT of films. The TiO₂ + Ta₂O₅ composite films have the lowest extinction coefficient and the highest LIDT among all samples investigated. Guidance of selecting materials for high LIDT laser mirrors is given.}

Effects of process on microstructure and properties of translucent Dy-alpha-SiAlON sintered at lower temperatures

Hot pressing (HP) at higher sintering temperature has been a traditional and prevalent technique for the fabrication of alpha-SiAlON. In order to prepare translucent SiAlON more easily, LiF was used as a non-oxide sintering additive to lower the sintering temperature to <= 1650 degrees C. As a result, all of the samples possessed a good hardness and fracture toughness. At the same time, the lower temperature sintered samples showed a higher optical transmittance in the range of 2.5-5.5 mu m wavelength (0.5 mm in thickness). The maximum infrared transmission reached 68% at a wavelength of 3.3 mu m. The present work shows that the sintering process has a strong effect on microstructure and property of alpha-SiAlON. To be exact, a lower sintering temperature and longer holding time can produce some fully-developed microstrcture, which is beneficial for the optical transmittance. (C) 2008 The Ceramic Society of Japan. All rights reserved.

Hot-pressed translucent aluminum oxynitride (AlON) ceramics

AlON with a composition of Al23O27N5 was prepared by hot pressing at temperatures lower than 1900°C. The microstructures and final properties, including both mechanical properties and optical properties, of the sintered specimens were studied. The results showed that sintering temperature had a great influence on the densification of specimens and could lead to very different properties, especially the optical transmittance and the maximum infrared transmission.