Sol-gel synthesis and photoluminescence properties of spherical SiO2@LaPO4 : Ce3+/Tb3+ particles with a core-shell structure

LaPO4: Ce3+ and LaPO4: Ce3+, Tb3+ phosphor layers have been deposited successfully on monodispersed and spherical SiO2 particles of different sizes ( 300, 500, 900 and 1200 nm) through a sol - gel process, resulting in the formation of core - shell structured SiO2@ LaPO4: Ce3+/ Tb3+ particles. X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), scanning electron microcopy (SEM), transmission electron microscopy (TEM), and general and time-resolved photoluminescence (PL) spectra as well as lifetimes were used to characterize the resulting SiO2@ LaPO4: Ce3+/ Tb3+ samples. The XRD results demonstrate that the LaPO4: Ce3+, Tb3+ layers begin to crystallize on the SiO2 templates after annealing at 700 degrees C, and the crystallinity increases on raising the annealing temperature. The obtained core - shell phosphors have perfectly spherical shape with a narrow size distribution, non-agglomeration, and a smooth surface. The doped rare-earth ions show their characteristic emission in the core - shell phosphors, i.e. Ce3+ 5d - 4f and Tb3+5D4 - F-7(J) (J = 6 - 3) transitions, respectively. The PL intensity of the Tb3+ increased on increasing the annealing temperature and the SiO2 core particle size.

An effective layer-by-layer adsorption and polymerization method to the fabrication of polyoxometalate-polypyrrole nanoparticle ultrathin films

A layer-by-layer (LbL) adsorption and polymerization method was developed for the controllable preparation of polypyrrole (PPy) nanoparticles within ultrathin films. By repetitive adsorption of pyrrole and subsequent polymerization with 12-molybdophosphoric acid, the polyelectrolyte multilayer films containing PPy nanoparticles were fabricated. UV-visible absorption spectrocopy, Fourier transform infrared (FTIR) spectroscopy, atomic force microscopy (AFM), transmission electron microscopy (TEM) and cyclic voltammograras (CVs) were used to characterize the PPy nanoparticles and their multilayer thin films. UV-visible spectra indicate that the growth of PPy nanoparticles was regular and occurred within the polyelectrolyte films. The size of prepared PPy nanoparticles was found by TEM to increase with the increasing of polymerization cycles. The electrochemistry behavior of the multilayer thin films was studied in detail on ITO. The results suggest that the LbL adsorption and polymerization method developed herein provides an effective way to prepare PPy nanoparticles in the polymer matrix.

Synthesis and photoluminescence of Y2O3 : RE3+ (RE = Eu, Tb, Dy) porous nanotubes templated by carbon nanotubes

Y2O3:RE3+ (RE = Eu, Tb, Dy) porous nanotubes were first synthesized using carbon nanotubes as template. The morphology of the coated precursors and porous Y2O3:Eu3+ nanotubes was determined by scanning electron Microscopy (SEM) and transmission electron microscopy (TEM). It was found that the coating of precursors on carbon nanotubes (CNTs) is continuous and the thickness is about 15 nm, after calcinated, the Y2O3:Eu3+ nanotubes are porous with the diameter size in the range of 50-80 nm and the length in micrometer scale. X-ray diffraction (XRD) patterns confirmed that the samples are cubic phase Y2O3 and the photoluminescence studies showed that the porous rare earth ions doped nanotubes possess characteristic emission of Eu3+, Tb3+, and Dy3+. This method may also provide a novel approach to produce other inorganic porous nanotubes used in catalyst and sensors.

Preparation, patterning and luminescent properties of nanocrystalline Gd2O3 : A (A = Eu3+, Dy3+, Sm3+, Er3+) phosphor films via Pechini sol-gel soft lithography

Nanocrystalline Gd2O3:A (A = Eu3+, Dy3+, Sm3+, Er3+) phosphor films and their patterning were fabricated by a Pechini sol-gel process combined with a soft lithography. X-ray diffraction (XRD), atomic force microscopy (AFM), scanning electron microscopy (SEM) and optical microscopy, UV/vis transmission and photoluminescence (PL) spectra as well as lifetimes were used to characterize the resulting films. The results of XRD indicated that the films began to crystallize at 500 degreesC and that the crystallinity increased with the elevation of annealing temperatures. Uniform and crack free non-patterned phosphor films were obtained by optimizing the composition of the coating sol, which mainly consisted of grains with an average size of 70 nm and a thickness of 550 nm. Using micro-molding in capillaries technique, we obtained homogeneous and defects-free patterned gel and crystalline phosphor films with different stripe widths (5, 10, 20 and 50 mum). Significant shrinkage (50%) was observed in the patterned films during the heat treatment process. The doped rare earth ions (A) showed their characteristic emission in crystalline Gd2O3 phosphor films due to an efficient energy transfer from Gd2O3 host to them. Both the lifetimes and PL intensity of the rare earth ions increased with increasing the annealing temperature from 500 to 900 degreesC, and the optimum concentrations for Eu3+, Dy3+, sm(3+), Er3+ were determined to be 5, 0.25, 1 and 1.5 mol% of Gd3+ in Gd2O3 films, respectively.

One-step synthesis and size control of dendrimer-protected gold nanoparticles: A heat-treatment-based strategy

Dendrimer-protected gold nanoparticles have been facilely obtained by heating an aqueous solution containing third generation poly(propyleneimine) dendrimers and HAuCl4 without the additional step of introducing other reducing agents. Transmission electron microscopy (TEM) and UV vis data indicate the size the nucleation and growth kinetics of gold nanoparticles thus formed which can be tuned by changing the initial molar ratio of dendrimer to gold.

Effect of LB monolayers on the mixed crystals of Lead and barium sulfate

The effect of LB monolayers on the mixed crystal was investigated by using X-ray photoelectron spectroscopy (XPS), Transmission electron microscopy (TEM), and Inductively coupled plasma-atomic emission spectroscopy (ICP-AES). The results show that LB monolayer has selectivity for the different nucleation ions with equal charge numbers and about the same ion radius. The selectivity is dependent on the head groups of monolayer. The monolayer and the doped ions have also an effect on the crystal morphology. (C) 2000 Published by Elsevier Science B.V. All rights reserved.

Chlorohydrin water swellable rubber compatibilized by an amphiphilic craft copolymer. I. Synthesis and characterization of compatibilizer PVA-g-PBA

The graft copolymerization of butyl acrylate onto poly(vinyl alcohol) with eerie ammonium nitrate as redox initiator in a aqueous medium has been investigated. The formation of graft copolymer was confirmed by means of IR, scanning electron microscopy (SEM), and wide-angle X-ray diffraction (WAXD). The percentage of mononer conversion and percentage of grafting varied with concentrations of initiator, nitric acid, monomer, macromolecular backbone (X-n = 1750, M = 80 000), reaction temperature and reaction time. Some inorganic salts and organic solvents have a great influence upon grafting. The reaction mechanism has been explored, and rate equations for the reaction are established. (C) 2000 John Wiley & Sons, Inc.

Isothermal and nonisothermal crystallization of poly(aryl ether ketone ketone) with all-para phenylene linkage

Isothermal and nonisothermal crystallization behavior for PEKK(T) was studied using differential scanning calorimetry (DSC), transmission electron microscopy (TEM), and electron diffraction (ED). In the isothermal crystallization process, the Avrami parameters obtained were n = 2.33-2.69, which shows crystal growth of two-dimensional extensions consistent with our observations by TEM. The lamellar thickness increases with the crystallization temperature of PEKK(T) crystallized isothermally from the melt. However, for the nonisothermal crystallization of PEKK(T), the results from the modified Avrami analysis show two different crystallization processes. Avrami exponents n(1) = 3.61-5.30, obtained from the primary crystallization process, are much bigger than are the secondary n(2) = 2.26-3.04 and confirmed by the observation of the spherulite morphology. PEKK(T) crystallized isothermally from the melt possesses the same crystal structure (Form I) as that from nonisothermal melt crystallization. The results from TEM observation show that the spherulite radius decreases with an increasing cooling rate. (C) 2001 John Wiley & Sons, Inc.

Electrocatalytic mechanism for formaldehyde oxidation on the highly dispersed gold microparticles and the surface characteristics of the electrode

Electrocatalytic mechanism for the electrochemical oxidation of formaldehyde (HCHO) on the highly dispersed Au microparticles electrodeposited on the surface of the glass carbon (GC) electrode in the alkaline Na2CO3/NaHCO3 solution and the surface characteristics of the Au microparticle-modified glass carbon (Au/GC) electrode were studied with in situ FTIR spectroscopy, scanning electron microscopy (SEM) and X-ray diffraction (XRD). It was found that the final products of HCHO oxidation is HCOO- at the Au/GC electrode and CO2 at the bulk Au electrode. The difference may be ascribed to the different surface characteristics between the Au/GC electrode and the bulk Au electrode. (C) 1999 Elsevier Science B.V. All rights reserved.

Miscibility of linear low density polyethylene (LLDPE)-graft-poly(methyl methacrylate) with poly(vinylidene fluoride) (PVF2) and its application as compatibilizer LLDPE/PVF2 blends

Differential scanning calorimetry (DSC), Fourier-transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy (XPS) were used to study the miscibility of blends of a graft copolymer of poly(methyl methacrylate) on linear low density polyethylene (LLDPE-g-PMMA, G-3) with poly(vinylidene fluoride)(b) (PVF2) and the compatibilization of blends of LLDPE/PVF2. The specific interaction between PMMA side chains and PVF2 in G-3/PVF2 binary blends is weaker than that between the homopolymers PMMA and PVF2. There are two states of PVF2 in the melt of a G-3/PVF2 (60/40, w/w) blend, one as pure PVF2 and the other interacting with PMMA side chains. The miscibility between PMMA side chains and PVF2 affects the crystallization of PVF2. LLDPE-g-PMMA was demonstrated to be a good compatibilizer in LLDPE/PVF2 blends, improving the interfacial adhesion and dispersion in the latter. Diffusion of PMMA side chains into PVF2 in the interfacial region reduces the crystallization rate and lowers the melting point (T-m) and the crystallization temperature (T-c) of PVF2 in the blends.

Studies on morphology and crystallization of polypropylene/polyamide 12 blends

Scanning electron microscopy (SEM) and an image analyser are used to study morphologies of the fractured surface, etched by hot phenol, of polypropylene/maleated polypropylene/polyamide 12 PP/PP-MA/PA12) = 65/10/25 blend and PP-MA/PA12 = 75/25 blend. The particle dimension and its distribution of PA12 dispersed phase in these blends are much lower and narrower than that of the PP/PA12. blends. Especially, most of the particles in the PP-MA/PA12 = 75/25 blend are smaller than 0.1 mu m. The effect of the morphology of PP/PA12 blends on their crystallization behaviour is studied using differential scanning calorimetry and SEM. PA12 dispersed phase coarsens during annealing in the PP/PP-MA/PA12 = 65/10/25 blend. The mechanism of coarsening of the PA12 dispersed phase is a coalescence process. The intense mixing between the PP component and the PA12 component through reaction of PP-MA and PA12 leads to a change of dynamic mechanical behaviour of the components. A separation method is used to separate the polyolefin parts (precipitated from hot phenol), from PA12 parts (hot phenol filtrate). Of PP/PP-MA/PA12 = 65/10/25 blend, infra-red measurements and elementary analysis show that the precipitate has a lower PA12 content than the feed, whereas the filtrate has a higher PA12 content. From PP-MA/PA12 = 75/25 blend, PA12 contents in the precipitate and the filtrate are the same as in the feed. This implies that all PA12 has reacted with all PP-MA in the latter case while not in the former case. Using the method of interface exposure, interfacial reaction of PP-MA with PA12 is studied by X-ray photoelectron spectrometry (X.p.s.). Copyright (C) 1996 Elsevier Science Ltd.

Miscibility and crystallization behavior of thermosetting polyimide thermoplastic polyimide blends

Compatibility, morphology, crystalline structure and mechanical properties of the blends of a thermosetting polyimide with thermoplastic polyimides consisting of dianhydrides of different lengths have been studied by the use of dynamic mechanical analysis (DMA), differential scanning calorimetry (DSC), scanning electron microscopy (SEM) and small-angle X-ray scattering (SAXS) techniques. The results of our research show that the blends change from compatible to semi-compatible when the difference between the length of the dianhydrides of the two components increases. Addition of a thermoplastic polyimide inhibits the crystallization of the thermosetting component. However, this effect decreases with increasing length of the dianhydrides and the distribution of the molecules of the thermoplastic polyimide component changes from interlamellar to interfibrillar. Impact strength and morphology of the fractured surfaces indicate that among the semiinterpenetrating polymer networks (semi-IPN) obtained the toughening effect of the partially compatible one is the best. The results are discussed in terms of charge transfer interaction between imide group and p-phenylene group.

SYNTHESIS OF A POLYETHYLENE-GRAFT-POLYSTYRENE COPOLYMER AND ITS COMPATIBILIZATION FOR LINEAR LOW-DENSITY POLYETHYLENE/POLY(PHENYLENE OXIDE) BLENDS

Based on unsteady diffusion kinetics, polyethylene(PE)-graft-polystyrene (PS) copolymers were designed and synthesized with a heterogeneous high yield titanium-based catalyst by copolymerization of ethylene with a PS-macromonomer using 1-hexene as a short chain agent to promote the incorporation of the PS-macromonomer. The presence of 1-hexene facilitated the diffusion of the PS-macromonomer, giving rise to the significantly increased incorporation of the PS-macromonomer. Compatibilization of blends of linear low density polyethylene (LLDPE)/poly(phenylene oxide) (PPO) with the PE-g-PS copolymer were investigated using scanning electron microscopy (SEM) and dynamic mechanical analysis (DMA).

SCANNING-TUNNELING-MICROSCOPY (STM) AND LATERAL FORCE MICROSCOPY (LFM) INVESTIGATION OF THE STRUCTURE AND CHARACTER OF CONDUCTIVE POLYPYRROLE FILM

Polypyrrole doped with p-toluenesulfonate was electropolymerized onto highly oriented pyrolytic graphite (HOPG), glassy carbon (GC) and Pt electrode surfaces under the same experimental conditions. The resulting films were studied by scanning tunneling m